US4543166A — Zinc-alloy electrolyte and process

Claim 1

Independent Claim 263 words

An aqueous acidic electrolyte for electrodepositing a zinc alloy on a substrate comprising: (a) zinc ions present in an amount sufficient to electrodeposit zinc, (b) at least one additional metal ion selected from the group consisting of nickel, cobalt and mixtures thereof present in an amount sufficient to electrodeposit an alloy of zinc-nickel, zinc-cobalt and zinc-nickel-cobalt, (c) a brightening amount of a primary brightener, (d) a carrier brightener present in an amount effective to refine the grain of the zinc alloy electrodeposit, (e) an auxiliary brightener present in an amount effective to impart supplemental brightness to the zinc alloy electrodeposit, (f) a ductilizer present in an amount effective to impart ductility to the zinc alloy electrodeposit comprising a compound as well as the bath soluble and compatible salts thereof corresponding to the structural formula: ##STR2## wherein: R is H or C 6 -C 10 aryl, or C 6 -C 20 alkyl aryl in which the alkyl group is C 1 -C 4 ; or C 1 -C 22 alkyl, or C 2 -C 10 heterocyclic nitrogen compounds having at least one tertiary or quaternary ring containing nitrogen; as well as the mono, di or tri substituted derivatives thereof including --OH, --SO 3 H or --COOH; the Group I and II metals and NH 4 salts thereof; and the aldehyde, ketone and ether derivatives thereof; X is R or --OR' or --NR 2 ' in which R' is H or a C 1 -C 4 aliphatic radical; and Y is H or SO 3 H; as well as the compatible water soluble salts thereof.

Claim 2

Dependent Claim 263 words

An aqueous acidic electrolyte for electrodepositing a zinc alloy on a substrate comprising: (a) zinc ions present in an amount sufficient to electrodeposit zinc, (b) at least one additional metal ion selected from the group consisting of nickel, cobalt and mixtures thereof present in an amount sufficient to electrodeposit an alloy of zinc-nickel, zinc-cobalt and zinc-nickel-cobalt, (c) a brightening amount of a primary brightener, (d) a carrier brightener present in an amount effective to refine the grain of the zinc alloy electrodeposit, (e) an auxiliary brightener present in an amount effective to impart supplemental brightness to the zinc alloy electrodeposit, (f) a ductilizer present in an amount effective to impart ductility to the zinc alloy electrodeposit comprising a compound as well as the bath soluble and compatible salts thereof corresponding to the structural formula: ##STR2## wherein: R is H or C 6 -C 10 aryl, or C 6 -C 20 alkyl aryl in which the alkyl group is C 1 -C 4 ; or C 1 -C 22 alkyl, or C 2 -C 10 heterocyclic nitrogen compounds having at least one tertiary or quaternary ring containing nitrogen; as well as the mono, di or tri substituted derivatives thereof including --OH, --SO 3 H or --COOH; the Group I and II metals and NH 4 salts thereof; and the aldehyde, ketone and ether derivatives thereof; X is R or --OR' or --NR 2 ' in which R' is H or a C 1 -C 4 aliphatic radical; and Y is H or SO 3 H; as well as the compatible water soluble salts thereof.

Claim 3

Dependent Claim 23 words

The electrolyte as defined in claim 1 in which said ductilizer is present in an amount of about 0.001 to about 10 g/l.

Claim 4

Dependent Claim 23 words

The electrolyte as defined in claim 1 in which said ductilizer is present in an amount of about 0.01 to about 5 g/l.

Claim 5

Dependent Claim 25 words

The electrolyte as defined in claim 1 further including hydrogen ions present in an amount to provide a pH of about 3 to about 6.9.

Claim 6

Dependent Claim 25 words

The electrolyte as defined in claim 1 further including hydrogen ions present in an amount to provide a pH of about 4 to about 6.

Claim 7

Dependent Claim 46 words

The electrolyte as defined in claim 1 in which said zinc ions are present in an amount of at least about 10 g/l up to solubility and said at least one additional metal ion is present in an amount of about 0.5 to about 60 g/l.

Claim 8

Dependent Claim 28 words

The electrolyte as defined in claim 1 in which said at least one additional metal ion is present in an amount of about 5 to about 25 g/l.

Claim 9

Dependent Claim 55 words

The electrolyte as defined in claim 1 in which said primary brightener is present in an amount of about 0.001 to about 10 g/l, said carrier brightener is present in an amount of about 0.5 to about 10 g/l and said auxiliary brightener is present in an amount of about 0.6 to about 10 g/l.

Claim 10

Dependent Claim 55 words

The electrolyte as defined in claim 1 in which said primary brightener is present in an amount of about 0.1 to about 5 g/l, said carrier brightener is present in an amount of about 2 to about 6 g/l and said auxiliary brightener is present in an amount of about 0.2 to about 5 g/l.

Claim 11

Dependent Claim 24 words

The electrolyte as defined in claim 1 further including a buffering agent present in an amount sufficient to stabilize the pH of said electrolyte.

Claim 12

Dependent Claim 12 words

The electrolyte as defined in claim 1 further including a dispersing agent.

Claim 13

Dependent Claim 28 words

The electrolyte as defined in claim 1 further including bath soluble and compatible conductivity salts present in an amount sufficient to enhance the electrical conductivity of the electrolyte.

Claim 14

Dependent Claim 45 words

The electrolyte as defined in claim 1 in which said at least one additional metal ion is present in an amount to produce a zinc alloy electrodeposit containing from about 0.01 to about 15 percent by weight of nickel and/or cobalt in the alloy electrodeposit.

Claim 15

Dependent Claim 39 words

The electrolyte as defined in claim 1 in which said one additional metal ion comprises cobalt present in said electrolyte in an amount to provide a zinc-cobalt alloy electrodeposit containing about 0.1 to about 5 percent by weight cobalt.

Claim 16

Dependent Claim 42 words

The electrolyte as defined in claim 1 in which said at least one additional metal ion comprises nickel present in the electrolyte in an amount to produce a zinc-nickel alloy electrodeposit containing about 0.25 to about 9 percent nickel in the alloy.

Claim 17

Dependent Claim 27 words

The electrolyte as defined in claim 1 in which said primary brightener comprises an alkyl nicotinate quaternary compound and said carrier brightener comprises an alkoxylated acetylenic compound.

Claim 18

Dependent Claim 41 words

A process for electrodepositing a zinc alloy on a conductive substrate which comprises the steps of contacting a substrate with the aqueous acidic electrolyte as defined in claim 1 and electrodepositing a zinc alloy on the substrate to a desired thickness.

Claim 19

Dependent Claim 28 words

The process as defined in claim 17 including the further step of controlling the temperature of the electrolyte within a range of about 60° to about 120° F.

Claim 20

Dependent Claim 27 words

The process as defined in claim 17 including the further step of controlling the pH of said electrolyte within a range of about 3 to about 6.9.

Claim 21

Dependent Claim 39 words

The process as defined in claim 17 including the further step of controlling the average cathode current density during the step of electrodepositing the zinc alloy on the substrate within a range of about 0.5 to about 80 ASF.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1988-09-23	1989-03-25	1989-09-24	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1992-09-23	1993-03-25	1993-09-24	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1996-09-23	1997-03-25	1997-09-24	$7700.00	Window Closed / Lapsed

Zinc-alloy electrolyte and process

Abstract