Method and apparatus for reducing the watt loss of a grain-oriented electromagnetic steel sheet and a grain-oriented electromagnetic steel sheet having a low watt loss
Assignee: Nippon Steel Corp
•
Filing: 1982-07-15
•
Granted: 1985-10-22
•
Expires: 2002-07-15
Abstract
Abstract The watt loss of a grain-oriented electromagnetic steel sheet can be decreased by known methods in which serrations or scratches are locally formed on said steel sheet or a small ball or disc is rolled or rotated over said steel sheet. The known methods are disadvantageous in that the rate of production is low and in that said steel sheet has a marked unevenness. In the present invention, particles, e.g., steel shots, are projected onto substantially linear selected portions of a grain-oriented electromagnetic steel sheet, thereby producing strain on spot-formed regions. Spotlike indentations are formed in the steel sheet by the projection of steel shots onto the steel sheet.
Inventors
- 👤 Tetsuo Kimoto
- 👤 Kiyoshi Orita
- 👤 Katsuro Kuroki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:23
CPC Classifications
C; C21; C21D; C21D7/00; C21D7/02; C21D7/04; C21D7/06; C21D8/00; C21D8/12; C21D8/1294; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/16
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
192 words
A method for reducing the watt loss of a grain-oriented electromagnetic steel sheet, characterized in that: after final annealing of a steel sheet during which grain orientation occurs an insulating film is applied to the surface of said grain-oriented electromagnetic steel sheet, and thereafter, particles consisting of metal are projected onto substantially linear selected portions of the surface of said grain-oriented electromagnetic steel sheet having said applied insulating film thereon to form spot-like indentations in said steel sheet in said linear selected portions, wherein said linear selected portions are parallel to one another and are oriented transverse to the longitudinal direction of the grain-oriented electromagnetic steel sheet, with said projecting taking place at a projection speed of from 12 to 52 m/sec and at a projection amount of from 3 to 30 kg/min/m 2 thereby producing strain in the spot-like indentations of said selected portions of said grain-oriented electromagnetic steel sheet, said spot-like indentations having a diameter of from approximately 60 to 80 microns and a depth of from approximately 3 to 5 microns, and said selected portions are spaced from one another at a distance of from 3 to 10 mm.
Claim 2
Independent Claim
192 words
A method for reducing the watt loss of a grain-oriented electromagnetic steel sheet, characterized in that: after final annealing of a steel sheet during which grain orientation occurs an insulating film is applied to the surface of said grain-oriented electromagnetic steel sheet, and thereafter, particles consisting of metal are projected onto substantially linear selected portions of the surface of said grain-oriented electromagnetic steel sheet having said applied insulating film thereon to form spot-like indentations in said steel sheet in said linear selected portions, wherein said linear selected portions are parallel to one another and are oriented transverse to the longitudinal direction of the grain-oriented electromagnetic steel sheet, with said projecting taking place at a projection speed of from 12 to 52 m/sec and at a projection amount of from 3 to 30 kg/min/m 2 thereby producing strain in the spot-like indentations of said selected portions of said grain-oriented electromagnetic steel sheet, said spot-like indentations having a diameter of from approximately 60 to 80 microns and a depth of from approximately 3 to 5 microns, and said selected portions are spaced from one another at a distance of from 3 to 10 mm.
Claim 3
Dependent Claim
26 words
A method according to claim 1, wherein each of said substantially linear selected portions of the grain-oriented electromagnetic steel sheet is a continuous line or curve.
Claim 4
Dependent Claim
26 words
A method according to claim 1, wherein each of said substantially linear selected portions of the grain-oriented electromagnetic steel sheet is a discontinuous line or curve.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |