Magnetic recording material using plate-shaped ferromagnetic particles
Assignee: Fujifilm Holdings Corp
•
Filing: 1983-11-23
•
Granted: 1985-11-12
•
Expires: 2003-11-23
Abstract
Abstract A magnetic recording material is disclosed which is comprised of a single magnetic layer comprised of plate-shaped ferromagnetic particles wherein the plate-shaped ferromagnetic particles are present in greater number in the surface part of the magnetic layer than in the inner part and/or the plate-shaped ferromagnetic particles are aligned such that an average horizontal axis component of the particles with respect to the surface of magnetic layer is larger in the surface part than in the inner part. The location and alignment of the particles make is possible to increase output with short-wave recording.
Inventors
- 👤 Masaaki Fujiyama
- 👤 Takamitsu Asai
- 👤 Toshihiko Miura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:34
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70678; G11B5/714; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/25; Y10T428/256; Y10T428/257; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
126 words
A magnetic recording material, comprising: a non-magnetic support base having provided thereon; a single magnetic recording layer comprised of plate-shaped ferromagnetic particles dispersed in a binder, wherein the ferromagnetic particles have a mean size of 0.01 μm to 10 μm, and wherein the thickness of the ferromagnetic particles is equal to or less than their diameter, wherein the plate-shaped ferromagnetic particles are present in greater numbers per unit volume in surface part of the single magnetic layer than in an inner part of the single magnetic layer and/or the plate-shaped ferromagnetic particles are aligned such that an average horizontal axis component of the particles which respect to the surface of the single magnetic layer is larger in the surface part than in the inner part thereof.
Claim 2
Dependent Claim
126 words
A magnetic recording material, comprising: a non-magnetic support base having provided thereon; a single magnetic recording layer comprised of plate-shaped ferromagnetic particles dispersed in a binder, wherein the ferromagnetic particles have a mean size of 0.01 μm to 10 μm, and wherein the thickness of the ferromagnetic particles is equal to or less than their diameter, wherein the plate-shaped ferromagnetic particles are present in greater numbers per unit volume in surface part of the single magnetic layer than in an inner part of the single magnetic layer and/or the plate-shaped ferromagnetic particles are aligned such that an average horizontal axis component of the particles which respect to the surface of the single magnetic layer is larger in the surface part than in the inner part thereof.
Claim 3
Dependent Claim
18 words
A magnetic recording material as claimed in claim 1, wherein the ferromagnetic particles have a circular plate-like shape.
Claim 4
Dependent Claim
18 words
A magnetic recording material as claimed in claim 1, wherein the ferromagnetic particles have a hexagonal plate-like shape.
Claim 5
Dependent Claim
27 words
A magnetic recording material as claimed in claim 1, wherein the ferromagnetic particles have a mean size in the range of from 0.01 μm to 0.3 μm.
Claim 6
Dependent Claim
27 words
A magnetic recording material as claimed in claim 1, wherein the thickness of the ferromagnetic particles is in the range of 1/2 to 1/15 of the diameter.
Claim 7
Dependent Claim
32 words
A magnetic recording material as claimed in claim 1, wherein the number of the plate-shaped ferromagnetic particles in the surface part is 10 to 20% greater than that in the inner part.
Claim 8
Dependent Claim
31 words
A magnetic recording material as claimed in claim 6, wherein the number of the plate-shaped ferromagnetic particles in the surface part is from 10 10 to 10 20 /cm 3 .
Claim 9
Dependent Claim
31 words
A magnetic recording material as claimed in claim 6, wherein the number of the plate-shaped ferromagnetic particles in the surface part is from 10 12 to 10 18 /cm 3 .
Claim 10
Dependent Claim
31 words
A magnetic recording material as claimed in claim 6, wherein the number of the plate-shaped ferromagnetic particles in the surface part is from 10 14 to 10 16 /cm 3 .
Claim 11
Dependent Claim
32 words
A magnetic recording material as claimed in claim 1, wherein the ratio of the average horizontal axis component in the surface part to that in the inner part is more than 1.2/1.
Claim 12
Dependent Claim
32 words
A magnetic recording material as claimed in claim 1, wherein the ratio of the average horizontal axis component in the surface part to that in the inner part is more than 1.5/1.
Claim 13
Dependent Claim
32 words
A magnetic recording material as claimed in claim 1, wherein the ferromagnetic particles are present in an amount of 1 to 20 parts by weight per part by weight of the binder.
Claim 14
Dependent Claim
22 words
A magnetic recording material as claimed in claim 12, wherein the magnetic layer has a thickness of from 0.5 to 20 μm.
Claim 15
Dependent Claim
168 words
A magnetic recording material as claimed in claim 1, wherein said magnetic recording material is formed by subjecting the same to at least one surface particle alignment method selected from the group consisting of: forcing the surface of the magnetic layer to come into contact with a heated roll; forcing the magnetic recording material to pass between a compressive rubbing roll and a tape driving roll, which differ in rotating speed, in such a manner that the magnetic layer has contact with the compressive rubbing roll; forcing the magnetic recording material to pass between a hard compressive rubbing roll and a soft roll, which differ in rotating speed, in such a manner that the magnetic layer has contact with the hard compressive rubbing roll; and forcing the magnetic recording material to pass between a heated hard roll having a small diameter and a cooled hard roll having a large diameter in such a manner that the magnetic layer has contact with the hard roll having a small diameter.
Claim 16
Dependent Claim
41 words
A magnetic recording material as claimed in claim 14, wherein the particle alignment method is method (1) and wherein the surface temperature of the heated roll is 60° C. or higher and the diameter of the heated roll is 1-30 cm.
Claim 17
Dependent Claim
41 words
A magnetic recording material as claimed in claim 14, wherein the surface particle alignment method is method (2) and wherein the difference in speed is 0.2 to 20% and the temperature of the compressive rubbing roll is 60° C. or higher.
Claim 18
Dependent Claim
31 words
A magnetic recording material as claimed in claim 16, wherein the difference in speed is 2 to 10% and the temperature of the compressive rubbing roll is 80° C. or higher.
Claim 19
Dependent Claim
42 words
A magnetic recording material as claimed in claim 15, wherein the surface particle alignment method is method (3) and wherein the difference of speed is 0.1% or more and the temperature of the hard compressive rubbing roll is 60° C. or higher.
Claim 20
Dependent Claim
32 words
A magnetic recording material as claimed in claim 18, wherein the difference in speed is 0.2 to 20% and the temperature of the hard compressive rubbing roll is 80° C. or higher.
Claim 21
Dependent Claim
77 words
A magnetic recording material as claimed in claim 14, wherein the surface particle alignment method is method (4) and wherein the ratio of the diameter of the hard roll which comes into contact with the magnetic layer to the diameter of the hard roll which comes into contact with the non-magnetic base is not more than 1/1.3 and the temperature of the hard roll which comes into contact with the magnetic layer is more than 40° C.
Claim 22
Dependent Claim
37 words
A magnetic recording material as claimed in claim 14, wherein the surface particle alignment method is carried out at a processing rate of 1 m/min or more and at a roll pressure of 200 kg/cm or more.
Claim 23
Dependent Claim
92 words
A magnetic recording material as claimed in claim 1, wherein the magnetic recording material is formed by coating a magnetic coating solution on a SUS drum, and then carrying out magnetic orientation as a drying air flow is supplied to the magnetic coating solution, wherein an N-pole is arranged inside the SUS drum and an S-pole is disposed farther from the magnetic layer than the N-pole, the magnetic layer thus formed being peeled off the SUS drum and, at the same time, applied to an adhesive layer provided on a non-magnetic support.
Claim 24
Dependent Claim
29 words
A magnetic recording material as claimed in claim 22, wherein the SUS drum has a mere surface having a center line surface roughness of not more than 0.30 mm.
Claim 25
Dependent Claim
29 words
A magnetic recording material as claimed in claim 14, wherein the at least one surface particle alignment method is carried out before or after supercalendering the magnetic recording layer.
Claim 26
Dependent Claim
20 words
A magnetic recording material as claimed in claim 24, wherein the surface particle alignment method is carried out after supercalendering.
Claim 27
Dependent Claim
39 words
A magnetic recording material as claimed in claim 25, wherein supercalendering is carried out at a linear pressure of 50 kg/cm or more, a temperature of 50° C. or more and at a rate of 5 m/min or more.
Claim 28
Dependent Claim
35 words
A magnetic recording material as claimed in claim 26, wherein said linear pressure is 150 kg/cm or more, said temperature is from 50° C. to 100° C. and the rate is 15 to 100 m/min.
References Cited (Backward Citations)
US3023166A
Cited
US3185775A
Cited
US3144520A
Cited
US3117065A
Cited
US4135016A
Cited
US4341648A
Cited
US4442159A
Cited
US4486496A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-11 | 1989-05-13 | 1989-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-11 | 1993-05-13 | 1993-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-11 | 1997-05-13 | 1997-11-12 | $7700.00 | Window Closed / Lapsed |