Process for eliminating surface melt fracture during extrusion of thermoplastic polymers

Claim 2

A process for substantially eliminating surface melt fracture during extrusion of a thermoplastic polymer under conditions of flow rate and melt temperature which would otherwise produce such surface melt fracture which comprises extruding said polymer through a die having a die land region defining opposing surfaces, and wherein at least one of said opposing surface is fabricated from an alloy containing 5 to 95 parts by weight zinc and 95 to 5 parts by weight of copper whereby surface melt fracture is substantially eliminated on the surface of the polymer adjacent to said zinc/copper containing alloy surface.

Claim 3

A process according to claim 1 wherein said thermoplastic polymer is a molten narrow molecular weight distribution, linear, ethylene polymer or copolymer.

Claim 4

A process according to claim 2 wherein a stabilizing additive is added to said ethylene copolymer.

Claim 5

A process according to claim 3 wherein said stabilizing additive is a fatty diethoxylated tertiary amine.

Claim 6

A process according to claim 4 wherein said fatty diethoxylated tertiary amine is added to said ethylene copolymer in an amount of about 50 to 1500 parts per million.

Claim 7

A process according to claim 2 wherein said alloy includes tin, or aluminum or lead or mixtures thereof.

Claim 8

A process according to claim 2 wherein said alloy contains about 30 to 40 parts by weight zinc and about 70 to 60 parts by weight copper.

Claim 9

A process according to claim 2 wherein said alloy surface in said die land region is provided by inserts secured to the pin and collar of said die.

Claim 10

A process according to claim 8 wherein said inserts extend the length of said die land region.

Claim 11

A process according to claim 8 wherein said inserts extend for a portion of the length of said die land region.

Claim 12

A process according to claim 2 wherein said alloy surface is provided by fabricating the die pin and die collar of said die from said alloy.

Claim 13

A process according to claim 2 wherein the distance between said die lips is up to about 0.050 inch.

Claim 14

A process according to claim 2 wherein said copolymer is a copolymer of greater than or equal to 80 mol percent of ethylene and less than or equal to 20 mol percent of at least one C 3 to C 8 alpha olefin.

Claim 15

A process according to claim 13 in which said copolymer has a melt index of greater than or equal to 0.1 to less than or equal to 5.0.

Claim 16

A process for substantially eliminating surface melt fracture during extrusion of a molten narrow molecular weight distribution, linear, ethylene copolymer, under conditions of flow rate and melt temperature which would otherwise produce such surface melt fracture which comprises extruding said polymer through a die having a die land region defining opposing surfaces and wherein at least one of said opposing surface is fabricated from an alloy containing about 30 to 40 parts by weight zinc and about 70 to 60 parts by weight copper said ethylene copolymer containing from about 50 to 1500 ppm of a fatty diethoxylated tertiary amine, whereby melt fracture is substantially eliminated on the surface of the polymer adjacent to said zinc/copper containing alloy surface.

Claim 17

A process for substantially eliminating surface melt fracture during extrusion of a molten narrow molecular weight distribution, linear, ethylene copolymer, under conditions of flow rate and melt temperature which would otherwise produce such surface melt fracture which comprises extruding said polymer through a die having a die land region defining opposing surfaces and wherein at least one of said opposing surface is fabricated from an alloy containing about 30 to 40 parts by weight zinc and about 70 to 60 parts by weight copper said ethylene copolymer containing from about 50 to 1500 ppm of a fatty diethoxylated tertiary amine, whereby melt fracture is substantially eliminated on the surface of the polymer adjacent to said zinc/copper containing alloy surface.

Claim 18

A process according to claim 15 wherein said alloy surface in said die land region is provided by inserts secured to the pin and collar of said die.

Claim 19

A process according to claim 11 wherein said inserts extend the length of said die land region.

Claim 20

A process according to claim 16 wherein said inserts extend for a portion of the length of said die land region.

Claim 21

A process according to claim 15 wherein said alloy surface is provided by fabricating the die pin and die collar of said die from said alloy.

Claim 22

A process according to claim 1 wherein said thermoplastic polymer is a propylene polymer.

Claim 23

A process according to claim 20 wherein said propylene is a copolymer of greater than or equal to 85 mol percent propylene and less than or equal to 15 percent of ethylene and/or one or more of C 3 to C 8 alpha olefins.

Claim 24

A process according to claim 20 wherein said propylene polymer is a block or impact copolymer with a total weight percent of from about 70 to about 95% of propylene and a minor weight percent of from about 5 to about 30% of ethylene and/or one or more C 3 to C 8 alpha olefins.

Claim 25

A process according to claim 1 wherein said resin is subjected to an inert gas to remove moisture content prior to extrusion.

Claim 26

A process according to claim 23 wherein said inert gas is nitrogen.

Claim 27

A die for extruding thermoplastic polymers prone to melt fracture which comprises a die block having inlet means for introducing an extruder melt into said die block and outlet means for discharging molten polymer from said die block, conduit means for passing molten material from said inlet means to said outlet means, said outlet means including a land entry section and a die land, said die land having surfaces in contact with said molten polymer, at least one of said surfaces being fabricated from an alloy containing 5 to 95 parts by weight zinc and 95 to 5 parts by weight of copper whereby melt fracture is substantially eliminated on the surface of the polymer adjacent to said zinc/copper containing alloy surface.

Claim 28

A die for extruding thermoplastic polymers prone to melt fracture which comprises a die block having inlet means for introducing an extruder melt into said die block and outlet means for discharging molten polymer from said die block, conduit means for passing molten material from said inlet means to said outlet means, said outlet means including a land entry section and a die land, said die land having surfaces in contact with said molten polymer, at least one of said surfaces being fabricated from an alloy containing 5 to 95 parts by weight zinc and 95 to 5 parts by weight of copper whereby melt fracture is substantially eliminated on the surface of the polymer adjacent to said zinc/copper containing alloy surface.

Claim 29

A die according to claim 25 wherein said alloy includes tin, or aluminum or lead or mixtures thereof.

Claim 30

A die according to claim 25 wherein said alloy contains about 30 to 40 parts by weight zinc and about 70 to 60 parts by weight copper.

Claim 31

A die according to claim 25 wherein said alloy surface in said die land region is provided by inserts secured to the pin and collar of said die.

Claim 32

A die according to claim 28 wherein said inserts extend the length of said die land region.

Claim 33

A die according to claim 28 wherein said inserts extend for a portion of the length of said die land region.

Claim 34

A die according to claim 25 wherein said alloy surface is provided by fabricating the die pin and die collar of said die from said alloy.

Claim 35

A die according to claim 25 wherein the distance between said die lips is between about 0.005 inch to about 0.040 inch.