Fiber reinforced resin molded articles for electromagnetic waves and method for production thereof
Assignee: Inax Corp
•
Filing: 1983-11-03
•
Granted: 1985-11-19
•
Expires: 2003-11-03
Abstract
Abstract There is provided an FRP molded article having the properties of uniformly reflecting and shielding electromagnetic waves in the range of VHF to EHF. The molded article comprises a compression-molded laminated structure composed of an electroconductive nonwoven fabric-resin composite surface layer, a woven fabric-resin composite intermediate layer, and a fiber material reinforced resin substrate layer. The molded article can be produced by placing, on a mold, an electroconductive nonwoven fabric or a prepreg thereof, a woven fabric or a prepreg thereof, and then a mixture of a reinforcing fiber material and a liquid crosslink-curable resin composition thereon, and subjecting the laminated materials to compression molding. The molded articles can be advantageously used, for example, as reflecting dish antennas as well as shielding sheets or boards for electromagnetic waves.
Inventors
- 👤 Nobuhiro Ono
- 👤 Eiji Miwa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 15:23
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/08; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B29C70/88; B29C70/882; B32B5/02; B32B5/022; B32B5/024; B32B5/028; B32B5/28; H; H01; H01Q; H01Q15/00; H01Q15/14; H01Q15/141; H05; H05K; H05K9/00; H05K9/0073; H05K9/0081; H05K9/009; B29C37/00; B29C37/0025; B29C37/0028; B29C70/28; B29C70/30; B29C70/34; B29K; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/0809; B29K2105/0854; B29K2105/12; B29K2995/00; B29K2995/0003; B29K2995/0005; B29L; B29L2031/00; B29L2031/34; B29L2031/3456; B32B2305/00; B32B2305/08; B32B2305/38; B32B2305/72; B32B2307/00; B32B2307/20; B32B2307/202; B32B2307/212; B32B2307/40; B32B2307/416; Y; Y10; Y10T; Y10T442/00; Y10T442/30; Y10T442/3707; Y10T442/378; Y10T442/3813
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
126 words
A fiber reinforced resin molded article for electromagnetic waves having the properties of uniformly reflecting and shielding electromagnetic waves in the range of VHF to EHF, which comprises a compression-molded crosslink-cured laminated structure, having a plane or curved reflective surface, consisting essentially of a surface layer, an intermediate layer adjacent to said surface layer and a substrate layer; said surface layer being an electroconductive nonwoven fabric-cured resin composite layer having an effective layer thickness of at least about 0.005 mm; said intermediate layer being a woven fabric-cured resin composite layer having an effective layer thickness of at least about 0.005 mm, said woven fabric having a mesh size of not larger than about 5 mesh; and said substrate layer being a fiber material reinforced resin layer.
Claim 2
Dependent Claim
126 words
A fiber reinforced resin molded article for electromagnetic waves having the properties of uniformly reflecting and shielding electromagnetic waves in the range of VHF to EHF, which comprises a compression-molded crosslink-cured laminated structure, having a plane or curved reflective surface, consisting essentially of a surface layer, an intermediate layer adjacent to said surface layer and a substrate layer; said surface layer being an electroconductive nonwoven fabric-cured resin composite layer having an effective layer thickness of at least about 0.005 mm; said intermediate layer being a woven fabric-cured resin composite layer having an effective layer thickness of at least about 0.005 mm, said woven fabric having a mesh size of not larger than about 5 mesh; and said substrate layer being a fiber material reinforced resin layer.
Claim 3
Dependent Claim
38 words
The molded article according to claim 1, in which the fiber of the nonwoven fabric is selected from the group consisting of a metal fiber, a carbon fiber, a metal-coated fiber, an electroconductive synthetic fiber, and mixtures thereof.
Claim 4
Dependent Claim
29 words
The molded article according to claim 1, in which the cured resin of the molded article contains a crosslink-cured resin and a thermoplastic resin used as an anti-shrinkage agent.
Claim 5
Dependent Claim
30 words
The molded article according to claim 1, which is a parabola antenna for electromagnetic waves, the surface of the electroconductive nonwoven fabric layer being substantially a concave paraboloid of revolution.
Claim 6
Dependent Claim
25 words
The molded article according to claim 1, which is an electromagnetic wave-shielding sheet or board preventing penetration of the waves therethrough without substantially irregular reflection.
Claim 7
Dependent Claim
22 words
The molded article according to claim 1, in which the article has a thin top resin layer on the surface electroconductive layer.
Claim 8
Dependent Claim
68 words
The molded article according to claim 1, which is produced by the steps consisting essentially of placing, on a mold, an effective amount of an electroconductive nonwoven fabric or a prepreg thereof and then an effective amount of a woven fabric or a prepreg thereof; placing thereon a mixture of a reinforcing fiber material and a liquid crosslink-curable resin composition; and subjecting the laminated materials to compression molding.
Claim 9
Dependent Claim
32 words
The molded article according to claim 1, in which the fiber material reinforced resin substrate layer is a short fiber reinforced resin layer having thickness of about 1 to about 10 mm.
Claim 10
Dependent Claim
160 words
A process for producing a molded article, having a reflective surface for electromagnetic waves, comprising a electroconductive nonwoven fabric-resin surface layer, a woven fabric-resin intermediate layer adjacent said surface layer and a fiber material reinforced resin substrate layer, and having the properties of uniformly reflecting and shielding electromagnetic waves in the range of VHF to EHF; which process comprises placing, on a mold having a desired molding surface, an effective amount of an electroconductive nonwoven fabric and then an effective amount of a woven fabric for the intermediate layer, placing thereon a mixture of a reinforcing fiber material and a liquid crosslink-curable resin composition for the substrate layer, the compound viscosity of the liquid resin composition being not more than about 5×10 8 cps; and then compressing the laminated materials under a molding pressure of about 25 to about 100 kgf/cm 2 and at a mold closing speed of not more than about 240 mm/minute and curing the resin composition.
Claim 11
Dependent Claim
160 words
A process for producing a molded article, having a reflective surface for electromagnetic waves, comprising a electroconductive nonwoven fabric-resin surface layer, a woven fabric-resin intermediate layer adjacent said surface layer and a fiber material reinforced resin substrate layer, and having the properties of uniformly reflecting and shielding electromagnetic waves in the range of VHF to EHF; which process comprises placing, on a mold having a desired molding surface, an effective amount of an electroconductive nonwoven fabric and then an effective amount of a woven fabric for the intermediate layer, placing thereon a mixture of a reinforcing fiber material and a liquid crosslink-curable resin composition for the substrate layer, the compound viscosity of the liquid resin composition being not more than about 5×10 8 cps; and then compressing the laminated materials under a molding pressure of about 25 to about 100 kgf/cm 2 and at a mold closing speed of not more than about 240 mm/minute and curing the resin composition.
Claim 12
Dependent Claim
58 words
The process according to claim 9, in which the resulting electroconductive nonwoven fabric-cured resin layer has molded thickness of at least about 0.005 mm, the woven fabric of the intermediate layer has a mesh size of not larger than about 5 mesh, and the resulting woven fabric-cured resin layer has molded thickness of at least about 0.005 mm.
Claim 13
Dependent Claim
37 words
The process according to claim 9, in which the fiber of the nonwoven fabric is selected from the group consisting of a metal fiber, a carbon fiber, a metal-coated fiber, an electroconductive synthetic fiber, and mixtures thereof.
Claim 14
Dependent Claim
22 words
The process according to claim 9, in which the liquid crosslink-curable resin composition contains a thermoplastic resin used as an antishrinkage agent.
Claim 15
Dependent Claim
18 words
The process according to claim 9, in which a sheet molding compound is used for the substrate layer.
Claim 16
Dependent Claim
31 words
The process according to claim 9, in which a resin surfacing agent for a thin top layer is applied onto the mold prior to placing the laminated materials on the mold.
Claim 17
Dependent Claim
29 words
The molded article according to claim 1, in which the thickness of the nonwoven fabric composite layer is in the range of about 0.005 mm to about 1 mm.
Claim 18
Dependent Claim
28 words
The process according to claim 10, in which the thickness of the nonwoven fabric-cured resin layer is in the range of about 0.005 mm to about 1 mm.
Claim 19
Dependent Claim
129 words
A fiber reinforced resin molded article for electromagnetic waves having the properties of uniformly reflecting and shielding electromagnetic waves in the range of VHF to EHF, which comprises a compression-molded crosslink-cured laminated structure, having a plane or curved reflective surface, consisting essentially of a surface layer, an intermediate layer and a substrate layer; said surface layer being an electroconductive non-woven fabric-cured resin composite layer having an effective layer thickness of at least about 0.005 mm; said intermediate layer being a woven fabric-cured resin composite layer having an effective layer thickness of at least about 0.005 mm, said woven fabric having a mesh size of not larger than about 5 mesh; and said substrate layer being a fiber material reinforced resin layer, made according to the process of claim 10.
Claim 20
Dependent Claim
19 words
The process according to claim 9, in which the electroconductive nonwoven fabric is impregnated with a liquid crosslink-curable composition.
Claim 21
Dependent Claim
18 words
The process according to claim 9, in which a bulk molding compound is used for the substrate layer.
Claim 22
Dependent Claim
20 words
The process according to claim 9, in which the mold has a molding surface of a convex paraboloid of revolution.
Claim 23
Dependent Claim
23 words
The molded article according to claim 1, which is an article of uniformly reflecting electromagnetic waves in the range of VHF to EHF.
Claim 24
Dependent Claim
25 words
The molded article according to claim 1, in which the electroconductive nonwoven fabric-resin layer has a distinct layer structure on the woven fabric-resin intermediate layer.
References Cited (Backward Citations)
US3112221A
Cited
US3445320A
Cited
US3591400A
Cited
US4269800A
Cited
US4243460A
Cited
US4402779A
Cited
US4373001A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-18 | 1989-05-20 | 1989-11-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-18 | 1993-05-20 | 1993-11-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-18 | 1997-05-20 | 1997-11-19 | $7700.00 | Window Closed / Lapsed |