Epoxy bonded rare earth-iron magnets
Assignee: Motors Liquidation Co
•
Filing: 1984-03-08
•
Granted: 1985-12-10
•
Expires: 2004-03-08
Abstract
Abstract Novel epoxy compositions and a method of using them to make bonded rare earth-iron alloy magnets have been developed. The epoxy resins are polyglycidyl ethers of polyphenol alkanes that have high glass transition temperatures. The epoxy resin is provided in the form of a powder containing a suitable amount of a latent imidazole curing agent. The powder is mixed with rare earth-iron alloy particles, the mixture is compacted, and the resultant compact is heated to melt the powder and activate the curing agent. The alloy particles in the resultant magnet body are exceptionally resistant to flux loss upon aging.
Inventors
- 👤 Richard K. Gray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:56
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/10; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/057; H01F1/0571; H01F1/0575; H01F1/0578
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
128 words
A compact for making a bonded rare earth-transition metal permanent magnet, said compact comprising particles of magnetizable rare earth-transition metal alloy blended with a dry epoxy powder comprised of a polyglycidyl ether of a polyphenol alkane having a glass transition temperature greater than about 150° and a latent imidazole catalyst for said epoxy which is substituted in the two position with an alkyl group, which dry epoxy powder melts at an elevated temperature to flow around the alloy particles and thereby protect them from oxidation and at which temperature the imidazole catalyst is first activated to cure the epoxy resin and bind the alloy particles together into a durable magnet body which is resistant to flux loss at temperatures below the glass transition temperature of the cured epoxy.
Claim 2
Dependent Claim
128 words
A compact for making a bonded rare earth-transition metal permanent magnet, said compact comprising particles of magnetizable rare earth-transition metal alloy blended with a dry epoxy powder comprised of a polyglycidyl ether of a polyphenol alkane having a glass transition temperature greater than about 150° and a latent imidazole catalyst for said epoxy which is substituted in the two position with an alkyl group, which dry epoxy powder melts at an elevated temperature to flow around the alloy particles and thereby protect them from oxidation and at which temperature the imidazole catalyst is first activated to cure the epoxy resin and bind the alloy particles together into a durable magnet body which is resistant to flux loss at temperatures below the glass transition temperature of the cured epoxy.
Claim 3
Dependent Claim
145 words
A compact for making a bonded rare earth-transition metal permanent magnet, said compact comprising particles of magnetizable rare earth element-iron-boron alloy where the rare earth element is neodymium and/or praseodymium thoroughly mixed with a dry epoxy powder consisting essentially of an epoxy resin having the idealized structure ##STR4## and one or more latent imidazole catalysts for said resin taken from the group consisting of 2-ethyl-4-methyl imidazole and 1-(2-hydroxypropyl)-2-methyl imidazole, said compact having a density of at least about seventy percent of the alloy density and which compact can be heated to a temperature above about 100° C. to melt the epoxy powder so that it fills the spaces between the alloy particles and first activates the catalyst to cure the epoxy and form a magnet body that is durable and resistant to flux loss at temperatures below the glass transition temperature of the cured epoxy.
Claim 4
Dependent Claim
145 words
A compact for making a bonded rare earth-transition metal permanent magnet, said compact comprising particles of magnetizable rare earth element-iron-boron alloy where the rare earth element is neodymium and/or praseodymium thoroughly mixed with a dry epoxy powder consisting essentially of an epoxy resin having the idealized structure ##STR4## and one or more latent imidazole catalysts for said resin taken from the group consisting of 2-ethyl-4-methyl imidazole and 1-(2-hydroxypropyl)-2-methyl imidazole, said compact having a density of at least about seventy percent of the alloy density and which compact can be heated to a temperature above about 100° C. to melt the epoxy powder so that it fills the spaces between the alloy particles and first activates the catalyst to cure the epoxy and form a magnet body that is durable and resistant to flux loss at temperatures below the glass transition temperature of the cured epoxy.
Claim 5
Independent Claim
165 words
A method of making a bonded permanent magnet comprising the steps of mixing particles of rapidly quenched rare earth-iron-boron alloy with about 2-5 weight percent of a dry, free-flowing powder consisting essentially of an uncured epoxy resin which is a polyglycidyl ether of a polyphenol alkane having a glass transition temperature of at least about 150° C. and an imidazole catalyst for said resin which is inactive at the mixing temperature to cure the resin; pressing the mixture into a compact having a density of at least about 70 percent of the alloy density; heating said compact for a time and to a temperature at which the epoxy powder melts to coat and fill the voids between the alloy particles and the catalyst is activated to fully cure the epoxy resin; and magnetizing the compacted alloy particles in an applied magnetic field, said method providing a magnet that is durable and resistant to flux loss at temperatures below the glass transition temperature of the epoxy.
Claim 6
Independent Claim
165 words
A method of making a bonded permanent magnet comprising the steps of mixing particles of rapidly quenched rare earth-iron-boron alloy with about 2-5 weight percent of a dry, free-flowing powder consisting essentially of an uncured epoxy resin which is a polyglycidyl ether of a polyphenol alkane having a glass transition temperature of at least about 150° C. and an imidazole catalyst for said resin which is inactive at the mixing temperature to cure the resin; pressing the mixture into a compact having a density of at least about 70 percent of the alloy density; heating said compact for a time and to a temperature at which the epoxy powder melts to coat and fill the voids between the alloy particles and the catalyst is activated to fully cure the epoxy resin; and magnetizing the compacted alloy particles in an applied magnetic field, said method providing a magnet that is durable and resistant to flux loss at temperatures below the glass transition temperature of the epoxy.
Claim 7
Dependent Claim
19 words
The compact of claim 1 where the dry epoxy powder particles average less than about 15 microns in diameter.
Claim 8
Dependent Claim
20 words
The compact of claim 1 where the alloy particles consist essentially of crushed, melt-spun ribbon of neodymium and/or praseodymium-iron-boron alloy.
Claim 9
Dependent Claim
19 words
The compact of claim 1 where the resin constituent of the dry epoxy powder has the idealized structure ##STR5##
Claim 10
Dependent Claim
31 words
The compact of claim 1 where the resin constituent of the dry epoxy powder is a tetraglycidyl ether of tetraphenol ethane and the catalyst is 1-(2-hydroxy propyl)-2-methyl imidazole and/or 2-ethyl-4-methyl imidazole.
Claim 11
Dependent Claim
27 words
The compact of claim 1 where the epoxy powder is present in an amount of about 2-5 weight percent based on the weight of the alloy particles.
Claim 12
Dependent Claim
140 words
A mechanically strong, flux loss resistant permanent magnet which is formed by mixing particles of rapidly quenched rare earth-iron-boron alloy with about 2-5 weight percent of a dry, free-flowing powder consisting essentially of an uncured epoxy resin which is a polyglycidyl ether of a polyphenol alkane having a glass transition temperature of at least about 150° C. and an imidazole catalyst for said resin which is inactive at the mixing temperature to cure the resin; pressing the mixture into a compact having a density of at least about 70 percent of the alloy density; heating the compact for a time and to a temperature at which the epoxy powder melts to fill the voids between the alloy particles and the catalyst is activated to fully cure the epoxy resin; and magnetizing the compacted alloy particles in an applied magnetic field.
Claim 13
Dependent Claim
140 words
A mechanically strong, flux loss resistant permanent magnet which is formed by mixing particles of rapidly quenched rare earth-iron-boron alloy with about 2-5 weight percent of a dry, free-flowing powder consisting essentially of an uncured epoxy resin which is a polyglycidyl ether of a polyphenol alkane having a glass transition temperature of at least about 150° C. and an imidazole catalyst for said resin which is inactive at the mixing temperature to cure the resin; pressing the mixture into a compact having a density of at least about 70 percent of the alloy density; heating the compact for a time and to a temperature at which the epoxy powder melts to fill the voids between the alloy particles and the catalyst is activated to fully cure the epoxy resin; and magnetizing the compacted alloy particles in an applied magnetic field.
Claim 14
Dependent Claim
32 words
The permanent magnet of claim 9 where the resin constituent of the dry epoxy powder is a tetraglycidyl ether of tetraphenol ethane and the catalyst is 1-(2-hydroxy propyl)-2-methyl imidazole and/or 2-ethyl-4-methyl imidazole.
Claim 15
Dependent Claim
28 words
The permanent magnet of claim 9 where the epoxy resin is present in an amount of about 2-5 weight percent based on the weight of the alloy particles.
Claim 16
Dependent Claim
55 words
The permanent magnet of claim 9 where the resin constituent of the dry epoxy powder is a tetraglycidyl ether of tetraphenol ethane and the catalyst is 1-(2-hydroxy propyl)-2-methyl imidazole and/or 2-ethyl-4-methyl imidazole and wherein the epoxy powder is present in an amount of about 2-5 weight percent based on the weight of the alloy particles.
Claim 17
Dependent Claim
137 words
A strong, flux loss resistant permanent magnet which is formed by mixing particles of rare earth-iron-boron alloy with about 2-5 weight percent of a dry, free-flowing powder consisting essentially of an uncured epoxy resin which is a polyglycidyl ether of a polyphenol alkane having a glass transition temperature of at least about 150° C. and an imidazole catalyst for said resin which is inactive at the mixing temperature to cure the resin; pressing the mixture into a compact having a density of at least about 70 percent of the alloy density; heating the compact for a time and to a temperature at which the epoxy powder melts to fill the voids between the alloy particles and the catalyst is activated to fully cure the epoxy resin; and magnetizing the compacted alloy particles in an applied magnetic field.
Claim 18
Dependent Claim
137 words
A strong, flux loss resistant permanent magnet which is formed by mixing particles of rare earth-iron-boron alloy with about 2-5 weight percent of a dry, free-flowing powder consisting essentially of an uncured epoxy resin which is a polyglycidyl ether of a polyphenol alkane having a glass transition temperature of at least about 150° C. and an imidazole catalyst for said resin which is inactive at the mixing temperature to cure the resin; pressing the mixture into a compact having a density of at least about 70 percent of the alloy density; heating the compact for a time and to a temperature at which the epoxy powder melts to fill the voids between the alloy particles and the catalyst is activated to fully cure the epoxy resin; and magnetizing the compacted alloy particles in an applied magnetic field.
Claim 19
Dependent Claim
93 words
A rare earth-iron alloy permanent magnet in which particles of the alloy are bonded together with about 2 to 5 weight percent based on the alloy weight of an epoxy resin which is a tetraglycidyl ether of tetraphenol ethane having a glass transition temperature greater than about 150° C. which resin contains about 2 to 10 weight percent based on the resin of an imidazole catalyst therefor which is substituted in the two position with an alkyl group, the density of said magnet being at least about 70 percent of the alloy density.
Claim 20
Dependent Claim
93 words
A rare earth-iron alloy permanent magnet in which particles of the alloy are bonded together with about 2 to 5 weight percent based on the alloy weight of an epoxy resin which is a tetraglycidyl ether of tetraphenol ethane having a glass transition temperature greater than about 150° C. which resin contains about 2 to 10 weight percent based on the resin of an imidazole catalyst therefor which is substituted in the two position with an alkyl group, the density of said magnet being at least about 70 percent of the alloy density.
References Cited (Backward Citations)
US3438937A
Cited
US3596350A
Cited
US3634323A
Cited
US3933536A
Cited
US4141943A
Cited
US4335228A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-09 | 1989-06-10 | 1989-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-09 | 1993-06-10 | 1993-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-09 | 1997-06-10 | 1997-12-10 | $7700.00 | Window Closed / Lapsed |