Abstract A polyimide-oxide-polyimide integrated circuit structure is utilized in the process for forming openings having tapered sidewalls and predetermined controlled sizes. At least one opening size is replicated and transferred to an exposed surface in a underlying surface of the structure by first forming a thick layer of oxide over the first cured polyimide layer, anisotropically etching the thick layer of oxide to form an opening of predetermined size therethrough to the surface of the first cured polyimide layer. Next, the first layer of cured polyimide is isotropically etched to form an opening therethrough of substantially said predetermined size and exposing a portion of a thin layer of oxide underlying the first layer of cured polyimide. The thin layer of oxide is then anisotropically etched using the thick layer of oxide as an etch mask to expose an opening of said predetermined size on a surface of a second layer of cured polyimide. The second layer of cured polyimide is then anisotropically etched again using the thick layer of oxide as the etch mask to transfer and replicate the opening in the thick layer onto the surface of the underlying region. Thereafter the thick layer of oxide is removed. Metalization can then be deposited on the resulting structure to make contact to the underlying surface.
A method for forming an opening through a polyimide layer to expose an underlying surface wherein the dimension of the opening exposing the underlying surface is controlled and is characterized by tapered sidewalls, comprising the steps of forming a first layer of cured polyimide on the underlying surface; forming a thin layer of oxide over said first layer of cured polyimide; forming a second layer of polyimide over said thin layer of oxide; forming a second layer of oxide over said second layer of polyimide; forming a masking layer over said second layer of oxide; selectively patterning said masking layer thereby forming at least one opening therethrough to expose a portion of said second layer of oxide wherein said at least one opening being of predetermined size; anisotropically etching said second layer of oxide exposed through said masking layer to expose a portion of said second layer of cured polyimide underlying said at least one opening; isotropically etching said second layer of cured polyimide using said second layer of oxide as an etch mask to form an opening exposing a portion of said first layer of oxide wherein said opening through said second layer of cured polyimide having tapered sidewalls and said exposed portion of said first layer of oxide being an opening of substantially the same dimensions as said at least one opening, said first layer of oxide acting as an etch stop; anisotropically etching said first layer of oxide using said second layer of oxide as an etch mask to expose an opening to said first layer of cured polyimide; anisotropically etching said first layer of cured polyimide using said second layer of oxide as an etch mask to form an opening of said predetermined size on the underlying surface.
Claim 2
Independent Claim
292 words
A method for forming an opening through a polyimide layer to expose an underlying surface wherein the dimension of the opening exposing the underlying surface is controlled and is characterized by tapered sidewalls, comprising the steps of forming a first layer of cured polyimide on the underlying surface; forming a thin layer of oxide over said first layer of cured polyimide; forming a second layer of polyimide over said thin layer of oxide; forming a second layer of oxide over said second layer of polyimide; forming a masking layer over said second layer of oxide; selectively patterning said masking layer thereby forming at least one opening therethrough to expose a portion of said second layer of oxide wherein said at least one opening being of predetermined size; anisotropically etching said second layer of oxide exposed through said masking layer to expose a portion of said second layer of cured polyimide underlying said at least one opening; isotropically etching said second layer of cured polyimide using said second layer of oxide as an etch mask to form an opening exposing a portion of said first layer of oxide wherein said opening through said second layer of cured polyimide having tapered sidewalls and said exposed portion of said first layer of oxide being an opening of substantially the same dimensions as said at least one opening, said first layer of oxide acting as an etch stop; anisotropically etching said first layer of oxide using said second layer of oxide as an etch mask to expose an opening to said first layer of cured polyimide; anisotropically etching said first layer of cured polyimide using said second layer of oxide as an etch mask to form an opening of said predetermined size on the underlying surface.
Claim 3
Dependent Claim
40 words
The method of claim 1 further including the steps of removing said masking layer simultaneously with etching said second layer of cured polyimide and removing said second layer of oxide after said predetermined opening is formed on the underlying surface.