Blend of wholly aromatic polyester and poly(ester-amide) capable of exhibiting an anisotropic melt phase

Claim 2

A polymer blend formed by melt-mixing which when molten is capable of exhibiting an anisotropic melt phase and which following injection-molding is capable of exhibiting at least one property selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus, which exceeds that of each of the polymeric components of the blend when separately injection-molded comprising: (a) approximately 5 to approximately 95 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable wholly aromatic polyester which is capable of forming an anisotropic melt phase and which is substantially free of amide linkages; and (b) approximately 5 to approximately 95 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable poly(ester-amide) which is capable of forming an anisotropic melt phase.

Claim 3

A polymer blend according to claim 1 which is capable of being melt-processed at a temperature in the range of approximately 250° C. to 400° C.

Claim 4

A polymer blend according to claim 1 which is capable of being melt-processed at a temperature in the range of approximately 260° C. to 350° C.

Claim 5

A polymer blend according to claim 1 which is capable of being melt-processed at a temperature in the range of approximately 280° C. to 330° C.

Claim 6

A polymer blend according to claim 1 which following injection-molding is capable of exhibiting at least two properties selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection-molded.

Claim 7

A polymer blend according to claim 1 which following injection-molding is capable of exhibiting a least three properties selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection-molded.

Claim 8

A polymer blend according to claim 1 which following injection-molding is capable of exhibiting a tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection molded.

Claim 9

A polymer blend according to claim 1 wherein polymer components (a) and (b) each exhibit an inherent viscosity of at least 2.0 dl./g. when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 60° C.

Claim 10

A polymer blend according to claim 1 which comprises approximately 20 to approximately 80 percent by weight of component (a), based upon the total weight of components (a) and (b), and approximately 20 to approximately 80 percent by weight of component (b), based upon the total weight of components (a) and (b).

Claim 11

A polymer blend according to claim 1 which comprises approximately 25 to approximately 75 percent by weight of component (a), based upon the total weight of components (a) and (b), and approximately 25 to approximately 75 percent by weight of component (b) based upon the total weight of components (a) and (b).

Claim 12

A polymer blend according to claim 1 which comprises approximately 30 percent by weight of component (a), based upon the total weight of components (a) and (b), and approximately 70 percent by weight of component (b), based upon the total weight of components (a) and (b).

Claim 13

A polymer blend according to claim 1 wherein component (a) is a melt-processable wholly aromatic polyester and consists essentially of moieties I and II which may include substitution of at least some of the hydrogen atoms present upon an aromatic ring wherein: ##STR4## with said optional substitution if present being selected from the group consisting of an alkyl group to 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, phenyl, and mixtures thereof, and wherein said wholly aromatic polyester comprises approximately 10 to 90 mole percent of moiety I and approximately 10 to 90 mole percent of moiety II.

Claim 14

A polymer blend according to claim 1 wherein component (b) is a melt-processable poly(ester-amide) and consists essentially of moieties I, II, III, and optionally IV, wherein: I is ##STR5## II is ##STR6## where A is a divalent radical comprising at least one aromatic ring or a divalent trans-1,4-cyclohexylene radical; III is - Y - Ar - Z - where Ar is a divalent radical comprising at least one aromatic ring, Y is O, NH or NR, and Z is NH or NR, where R is an alkyl group of 1 to 6 carbon atoms; and IV is - O - Ar'- O - where Ar' is a divalent radical comprising at least one aromatic ring; wherein at least some of the hydrogen atoms present upon the rings optionally may be replaced by substitution selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, phenyl, and mixtures thereof, and wherein said poly(ester-amide) comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, approximately 5 to 45 mole percent of moiety III, and approximately 0 to 40 mole percent of moiety IV.

Claim 15

A polymer blend according to claim 1 wherein the aromatic rings of the polymeric components are substantially free of ring substitution.

Claim 16

A polymer blend according to claim 1 which following injection-molding is capable of exhibiting a tensile strength of at least 35,000 psi.

Claim 17

A polymer blend according to claim 1 which following injection-molding is capable of exhibiting a tensile strength of at least 40,000 psi.

Claim 18

A polymer blend according to claim 1 which following injection-molding is capable of exhibiting a tensile strength of at leat 45,000 psi.

Claim 19

A molding compound comprising the polymer blend of claim 1 which incorporates approximately 1 to approximately 60 percent by weight, based upon the total weight of the molding compound, of a material selected from the group consisting of solid filler, reinforcing agent, and mixtures thereof.

Claim 20

A molded article comprising the polymer blend of claim 1.

Claim 21

A melt-extruded three-dimensional article comprising the polymer blend of claim 1.

Claim 22

A shaped article comprising the polymer blend of claim 1 which has been subjected to heat treatment in a non-oxidizing atmosphere at approximately 10° C. to 30° C. below the melting temperature of the blend.

Claim 23

A polymer blend formed by melt-mixing which when molten is capable of exhibiting an anisotropic melt phase and which following injection-molding is capable of exhibiting at least one property selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceeds that of each of the polymeric components of the blend when separately injection molded comprising: (a) approximately 5 to approximately 95 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable wholly aromatic polyester which is capable of forming an anisotropic melt phase and which is substantially free of amide linkages and which consists essentially of moieties I and II which may include substitution of at least some of the hydrogen atoms present upon an aromatic ring wherein: ##STR7## with said optional substitution if present being selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, hydrogen, phenyl, and mixtures thereof, wherein said melt-processable wholly aromatic polyester comprises approximately 10 to 90 mole percent of moiety I and approximately 10 to 90 mole percent of moiety II, and (b) approximately 5 to approximately 95 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable poly(ester-amide) which is capable of forming an anisotropic melt phase which consists essentially of moieties I, II, III, and optionally, IV wherein: I is ##STR8## II is ##STR9## where A is a divalent radical comprising at least one aromatic ring or a divalent trans-1,4-cyclohexylene radical; III is - Y - Ar - Z - where Ar is a divalent radical comprising at least one aromatic ring, Y is O, NH or NR and Z is NH or NR, where R is an alkyl group of 1 to 6 carbon atoms; and IV is - O - Ar'- O - where Ar' is a divalent radical comprising at least one aromatic ring; wherein at least some of the hydrogen atoms present upon the rings optionally may be replaced by substitution selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, phenyl, and mixtures thereof, and wherein said poly(ester-amide) comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, approximately 5 to 45 mole percent of moiety III, and approximately 0 to 40 mole percent of moiety IV.

Claim 24

A polymer blend formed by melt-mixing which when molten is capable of exhibiting an anisotropic melt phase and which following injection-molding is capable of exhibiting at least one property selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceeds that of each of the polymeric components of the blend when separately injection molded comprising: (a) approximately 5 to approximately 95 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable wholly aromatic polyester which is capable of forming an anisotropic melt phase and which is substantially free of amide linkages and which consists essentially of moieties I and II which may include substitution of at least some of the hydrogen atoms present upon an aromatic ring wherein: ##STR7## with said optional substitution if present being selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, hydrogen, phenyl, and mixtures thereof, wherein said melt-processable wholly aromatic polyester comprises approximately 10 to 90 mole percent of moiety I and approximately 10 to 90 mole percent of moiety II, and (b) approximately 5 to approximately 95 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable poly(ester-amide) which is capable of forming an anisotropic melt phase which consists essentially of moieties I, II, III, and optionally, IV wherein: I is ##STR8## II is ##STR9## where A is a divalent radical comprising at least one aromatic ring or a divalent trans-1,4-cyclohexylene radical; III is - Y - Ar - Z - where Ar is a divalent radical comprising at least one aromatic ring, Y is O, NH or NR and Z is NH or NR, where R is an alkyl group of 1 to 6 carbon atoms; and IV is - O - Ar'- O - where Ar' is a divalent radical comprising at least one aromatic ring; wherein at least some of the hydrogen atoms present upon the rings optionally may be replaced by substitution selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, phenyl, and mixtures thereof, and wherein said poly(ester-amide) comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, approximately 5 to 45 mole percent of moiety III, and approximately 0 to 40 mole percent of moiety IV.

Claim 25

A polymer blend according to claim 22 which is capable of being melt-processed at a temperature in the range of approximately 250° C. to 400° C.

Claim 26

A polymer blend according to claim 22 which is capable of being melt-processed at a temperature in the range of approximately 260° C. to 350° C.

Claim 27

A polymer blend according to claim 22 which is capable of being melt-processed at a temperature in the range of approximately 280° C. to 330° C.

Claim 28

A polymer blend according to claim 22 which following injection-molding is capable of exhibiting at least two properties selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection-molded.

Claim 29

A polymer blend according to claim 22 which following injection-molding is capable of exhibiting at least three properties selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection-molded.

Claim 30

A polymer blend according to claim 22 which following injection-molding is capable of exhibiting a tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection-molded.

Claim 31

A polymer blend according to claim 22 wherein polymer components (a) and (b) each exhibit an inherent viscosity of at least 2.0 dl./g. when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 60° C.

Claim 32

A polymer blend according to claim 22 which comprises approximately 20 to approximately 80 percent by weight of component (a), based upon the total weight of components (a) and (b), and approximately 20 to approximately 80 percent by weight of component (b), based upon the total weight of components (a) and (b).

Claim 33

A polymer blend according to claim 22 which comprises approximately 25 to approximately 75 percen by weight of component (a), based upon the total weight of components (a) and (b), and approximately 25 to approximately 75 percent by weight of component (b), based upon the total weight of components (a) and (b).

Claim 34

A polymer blend according to claim 22 which comprises approximately 30 percent by weight of component (a), based upon the total weight of components (a) and (b), and approximately 70 percent by weight of component (b), based upon the total weight of components (a) and (b).

Claim 35

A polymer blend according to claim 22 wherein component (a) comprises approximately 15 to 35 mole percent of moiety I and approximately 65 to 85 mole percent of moiety II.

Claim 36

A polymer blend according to claim 22 wherein component (b) comprises approximately 40 to 60 mole percent of moiety I, approximately, 20 to 30 mole percent of moiety II, approximately 5 to 30 mole percent of moiety III, and approximately 0 to 15 mole percent of moiety IV.

Claim 37

A polymer blend according to claim 22 wherein the aromatic rings of the polymer components are substantially free of ring substitution.

Claim 38

A polymer blend according to claim 22 which following injection-molding is capable of exhibiting a tensile strength of at least 35,000 psi.

Claim 39

A polymer blend according to claim 22 which following injection-molding is capable of exhibiting a tensile strength of at least 40,000 psi.

Claim 40

A polymer blend according to claim 22 which following injection-molding is capable of exhibiting a tensile strength of at least 45,000 psi.

Claim 41

A molding compound comprising the polymer blend of claim 22 which incorporates approximately 1 to approximately 60 percent by weight, based upon the total weight of the molding compound, of a material selected from the group consisting of solid filler, reinforcing agent, and mixtures thereof.

Claim 42

A molded article comprising the polymer blend of claim 22.

Claim 43

A melt-extruded three-dimensional article comprising the polymer blend of claim 22.

Claim 44

A shaped article comprising the polymer blend of claim 22 which has been subjected to heat treatment in a non-oxidizing atmosphere at approximately 10° C. to 30° C. below the melting temperature of the polymer blend.

Claim 45

A polymer blend which is capable of being melt-processed at a temperature in the range of approximately 280° C. to 330° C. formed by melt-mixing which when molten is capable of exhibiting an anisotropic melt phase and which following injection-molding is capable of exhibiting at least one property selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceeds that of each of the polymeric components of the blend when separately injection-molded comprising: (a) approximately 25 to approximately 75 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable wholly aromatic polyester which is capable of forming an anisotropic melt phase and which is substantially free of amide linkages and which consists essentially of approximately 27 mole percent of recurring 6-oxy-2-naphthoyl moieties and approximately 73 mole percent of recurring 4-oxybenzoyl moieties; and (b) approximately 25 to approximately 75 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable poly(ester-amide) which is capable of forming an anisotropic melt phase and which consists essentially of approximately 60 mole percent of recurring 6-oxy-2-naphthoyl moieties, approximately 20 mole percent of recurring terephthaloyl moieties, and approximately 20 mole percent of recurring 4-oxyaminophenylene moieties.

Claim 46

A polymer blend which is capable of being melt-processed at a temperature in the range of approximately 280° C. to 330° C. formed by melt-mixing which when molten is capable of exhibiting an anisotropic melt phase and which following injection-molding is capable of exhibiting at least one property selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceeds that of each of the polymeric components of the blend when separately injection-molded comprising: (a) approximately 25 to approximately 75 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable wholly aromatic polyester which is capable of forming an anisotropic melt phase and which is substantially free of amide linkages and which consists essentially of approximately 27 mole percent of recurring 6-oxy-2-naphthoyl moieties and approximately 73 mole percent of recurring 4-oxybenzoyl moieties; and (b) approximately 25 to approximately 75 percent by weight, based upon the total weight of components (a) and (b), of a melt-processable poly(ester-amide) which is capable of forming an anisotropic melt phase and which consists essentially of approximately 60 mole percent of recurring 6-oxy-2-naphthoyl moieties, approximately 20 mole percent of recurring terephthaloyl moieties, and approximately 20 mole percent of recurring 4-oxyaminophenylene moieties.

Claim 47

A polymer blend according to claim 43 which following injection-molding is capable of exhibiting at least two properties selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection-molded.

Claim 48

A polymer blend according to claim 43 which following injection-molding is capable of exhibiting at least three properties selected from the group consisting of tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection-molded.

Claim 49

A polymer blend according to claim 43 which following injection-molding is capable of exhibiting a tensile strength, tensile modulus, flexural strength, and flexural modulus which exceed those of each of the polymeric components of the blend when separately injection-molded

Claim 50

A polymer blend according to claim 43 wherein polymer components (a) and (b) each exhibit an inherent viscosity in the range of approximately 2.0 to 12.0 dl./g. when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 60° C.

Claim 51

A polymer blend according to claim 43 which comprises approximately 30 percent by weight of component (a), based upon the total weight of components (a) and (b), and approximately 70 percent by weight of component (b), based upon the total weight of components (a) and (b).

Claim 52

A polymer blend according to claim 43 which following injection-molding is capable of exhibiting a tensile strength of at least 35,000 psi.

Claim 53

A polymer blend according to claim 41 which following injection-molding is capable of exhibiting a tensile strength of at least 40,000 psi.

Claim 54

A polymer blend according to claim 43 which following injection-molding is capable of exhibiting a tensile strength of at least 45,000 psi.

Claim 55

A molding compound comprising the polymer blend of claim 43 which incorporates approximately 1 to approximately 60 percent by weight, based upon the total weight of the molding compound, of a material selected from the group consisting of solid filler, reinforcing agent, and mixtures thereof.

Claim 56

A molded article comprising the polymer blend of claim 43.

Claim 57

A melt-extruded three-dimensional article comprising the polymer blend of claim 43.

Claim 58

A shaped article comprising the polymer blend of claim 43 which has been subjected to heat treatment in a non-oxidizing atmosphere at approximately 10° C. to 30° C. below the melting temperature of the polymer blend.