Method of manufacturing an object of a powdered material by isostatic pressing
Assignee: ABB Norden Holding AB
•
Filing: 1984-02-07
•
Granted: 1986-02-04
•
Expires: 2004-02-07
Abstract
Abstract An object is manufactured from a powdered material by isostatic pressing of a body, preformed from the powdered material, with a pressure medium, whereby the preformed body, in which at least the surface layer consists of a ceramic material in the form of a nitride, is surrounded by a casing which is rendered impenetrable to the pressure medium, before the isostatic pressing is carried out and the powder sintered. As the material in the casing there is used boron oxide or a glass containing boron oxide or a material forming glass while being heated, in which the content of boron oxide is sufficiently high for the glass--or the glass formed during heating--to be removable by water. The preformed body surrounded by the casing is subjected to a heat treatment for the formation of boron nitride on the surface of the preformed body, before the isostatic pressing is carried out. The casing is removed from the finished product by means of water or water vapor.
Inventors
- 👤 Jan Adlerborn
- 👤 Hans Larker
- 👤 Jan Nilsson
- 👤 Bertil Mattsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 04:38
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/12; B22F3/1208; B22F3/1216; B22F3/1225; C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593; C04B35/622; C04B35/64; C04B35/645; C04B35/6455; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/4932; Y10T29/49325
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
194 words
A method of manufacturing an object of a powdered material by isostatic pressing of a body, preformed from the powdered material, with a pressure medium, whereby the preformed body, in which at least the surface layer consists of a ceramic material in the form of a nitride, is surrounded by a boron oxide-containing casing which is made impenetrable to the pressure medium, before the isostatic pressing is carried out while sintering the powder, wherein for the material in the casing there is used boron oxide, or a glass containing boron oxide or a material containing boron oxide which forms glass upon heating and in which the content of boron oxide is at least 30% by weight such that the glass, or the glass formed upon heating, is removable by water, that the preformed body surrounded by a casing is subjected to a heat treatment for the formation of boron nitride on the surface of the preformed body and the boron oxide in the casing, before the isostatic pressing is carried out, and that at least that part of the casing which is located nearest the manufactured object is removed by water or water vapour.
Claim 2
Independent Claim
194 words
A method of manufacturing an object of a powdered material by isostatic pressing of a body, preformed from the powdered material, with a pressure medium, whereby the preformed body, in which at least the surface layer consists of a ceramic material in the form of a nitride, is surrounded by a boron oxide-containing casing which is made impenetrable to the pressure medium, before the isostatic pressing is carried out while sintering the powder, wherein for the material in the casing there is used boron oxide, or a glass containing boron oxide or a material containing boron oxide which forms glass upon heating and in which the content of boron oxide is at least 30% by weight such that the glass, or the glass formed upon heating, is removable by water, that the preformed body surrounded by a casing is subjected to a heat treatment for the formation of boron nitride on the surface of the preformed body and the boron oxide in the casing, before the isostatic pressing is carried out, and that at least that part of the casing which is located nearest the manufactured object is removed by water or water vapour.
Claim 3
Dependent Claim
29 words
Method according to claim 1, wherein the boron oxide content in the glass or in the material forming glass upon heating amounts to at least 50 percent by weight.
Claim 4
Dependent Claim
33 words
Method according to claim 1, wherein the heat treatment for the formation of boron nitride on the surface of the preformed body is carried out at a temperature of at least 900° C.
Claim 5
Dependent Claim
26 words
Method according to claim 1, wherein the material in the casing has a viscosity of at most 10 4 poises at a temperature of 1000° C.
Claim 6
Dependent Claim
26 words
Method according to claim 1, wherein the preformed body consists of silicon nitride or of a material built up with silicon nitride as the main constituent.
Claim 7
Dependent Claim
27 words
Method according to claim 1, wherein the preformed body consists of a ceramic or a metallic material provided with a coating in the form of a nitride.
Claim 8
Dependent Claim
78 words
Method according to claim 1, wherein the preformed body and the casing, when the casing is made impenetrable to the pressure medium, is placed in an open vessel which is resistant to the temperature at which the sintering of the powdered material is carried out, and that the casing is transformed into a melt with a surface limited by the walls of the vessel, below which the preformed body is located when the isostatic pressing is carried out.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-03 | 1989-08-05 | 1990-02-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-03 | 1993-08-05 | 1994-02-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-03 | 1997-08-05 | 1998-02-04 | $7700.00 | Window Closed / Lapsed |