Copper etching system
Assignee: Honeywell International Inc
•
Filing: 1984-05-07
•
Granted: 1986-02-11
•
Expires: 2004-05-07
Abstract
Abstract The invention relates to a novel process of etching a metal clad substrate which comprises contacting said substrate with one or more reactive gases, as for example ozone, to form one or more reaction products on the surface of the said metal which are more friable than said metal, and striking said reaction products with a plurality of abrasive particles.
Inventors
- 👤 Thomas A. Schmitkons
- 👤 George J. Samuels
- 👤 Joseph M. Ilardi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:51
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/10; C23F1/12; H; H05; H05K; H05K3/00; H05K3/02; H05K3/06; H05K3/067; H05K2203/00; H05K2203/08; H05K2203/087; H05K2203/09; H05K2203/095; H05K3/40; H05K3/42; H05K3/425; H05K3/427; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T29/49165
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
81 words
A method of etching metal which comprises: (a) exposing all or a portion of the surfaces of said metal to a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said metal which are more friable than said metal; and (b) striking said reaction products on said metal surface with plurality of abrasive particles for a time sufficient to erode away all or a portion of said products from said surface.
Claim 2
Independent Claim
81 words
A method of etching metal which comprises: (a) exposing all or a portion of the surfaces of said metal to a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said metal which are more friable than said metal; and (b) striking said reaction products on said metal surface with plurality of abrasive particles for a time sufficient to erode away all or a portion of said products from said surface.
Claim 3
Independent Claim
91 words
A method of etching metal from a metal clad substrate which comprises: (a) exposing all or a portion of the surfaces of the metal cladding to a reactive effective amount of one or more reactive gases forming one or more reaction products on the surfaces of said metal which are more friable than said metal; and (b) striking said reaction products on said metal surfaces with a plurality of abrasive particles in an amount and for a time sufficient to erode away a pre-determined amount of said products from said surfaces.
Claim 4
Independent Claim
91 words
A method of etching metal from a metal clad substrate which comprises: (a) exposing all or a portion of the surfaces of the metal cladding to a reactive effective amount of one or more reactive gases forming one or more reaction products on the surfaces of said metal which are more friable than said metal; and (b) striking said reaction products on said metal surfaces with a plurality of abrasive particles in an amount and for a time sufficient to erode away a pre-determined amount of said products from said surfaces.
Claim 5
Dependent Claim
11 words
A method according to claim 2 wherein said metal is copper.
Claim 6
Independent Claim
104 words
A method of preparing a printed circuit board from a copper clad substrate which comprises: (a) covering the surface of said copper cladding with a pre-determined pattern of protective material to form a desired exposed pattern; (b) contacting the uncovered copper cladding with a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said metal which are more friable than said metal; and (c) striking said reaction products with a plurality of abrasive particles at a velocity and for a time sufficient to erode all or a portion of said products from said surface.
Claim 7
Independent Claim
104 words
A method of preparing a printed circuit board from a copper clad substrate which comprises: (a) covering the surface of said copper cladding with a pre-determined pattern of protective material to form a desired exposed pattern; (b) contacting the uncovered copper cladding with a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said metal which are more friable than said metal; and (c) striking said reaction products with a plurality of abrasive particles at a velocity and for a time sufficient to erode all or a portion of said products from said surface.
Claim 8
Dependent Claim
13 words
A method according to claim 4 which further comprises removing the protective material.
Claim 9
Dependent Claim
36 words
A method according to claim 4 wherein said protective material is a polymerized photoresist adhered to the surface of said copper cladding which photoresist is resistant to said reactive gases and abrasion by said abrasive particles.
Claim 10
Dependent Claim
37 words
A method according to claim 4 wherein said protective material is a thixotropic material screen printed on the surface of said copper cladding which thixotropic material is resistant to said reactive gases and abrasive particles after curing.
Claim 11
Dependent Claim
36 words
A method according to claim 4 wherein said protective material is a metal etch resist adhered to the surface of said copper cladding which resist is resistant to said reactive gas and to said abrasive particles.
Claim 12
Dependent Claim
23 words
A method according to claim 4 wherein said unprotected copper cladding is contacted with said gases and struck with said abrasive particles concurrently.
Claim 13
Dependent Claim
31 words
A process according to claim 1 wherein said one or more reactive gases are selected from the group consisting of ozone, hydrogen chloride, sulfur trioxide, chlorine, bromine, flourine and silicon tetrachloride.
Claim 14
Dependent Claim
26 words
A process according to claim 10 wherein said one or more reactive gases are selected from the group consisting of ozone, hydrogen chloride, and sulfur trioxide.
Claim 15
Dependent Claim
21 words
A process according to claim 11 wherein said one or more reactive gases comprises a mixture of ozone and hydrogen chloride.
Claim 16
Dependent Claim
37 words
A process according to claim 1 wherein the amount of said one or more reactive gases in the exposing atmosphere is at least about 0.1 weight percent based on the total weight of gases in the atmosphere.
Claim 17
Dependent Claim
28 words
A process according to claim 13 wherein said amount is from about 0.5 to about 90 weight percent based on the total weight of gases in the atmosphere.
Claim 18
Dependent Claim
29 words
A process according to claim 14 wherein said amount is from about 0.5 to about 40 weight percent based on the total weight of gases in said exposing atmosphere.
Claim 19
Dependent Claim
29 words
A process according to claim 15 wherein said amount is from about 1 to about 5 weight percent based on the total weight of gases in the exposing atmosphere.
Claim 20
Dependent Claim
17 words
A process according to claim 1 wherein said particles are composed of materials which are non-hygroscopic materials.
Claim 21
Dependent Claim
20 words
A process according to claim 17 wherein said materials are selected from the group consisting of glass, alumina and silica.
Claim 22
Dependent Claim
19 words
A process according to claim 18 wherein said materials are selected from the group consisting of alumina and silica.
Claim 23
Dependent Claim
23 words
A process according to claim 1 wherein said abrasive particles have an average dimensional size equal to or less than about 100 μM.
Claim 24
Dependent Claim
20 words
A process according to claim 20 wherein said average dimensional size is equal to or less than about 50 μM.
Claim 25
Dependent Claim
20 words
A process according to claim 21 wherein said average dimensional size is equal to or less than about 25 μM.
Claim 26
Dependent Claim
20 words
A process according to claim 22 wherein said average dimensional size is equal to or less than about 10 μM.
Claim 27
Independent Claim
176 words
A method of preparing a printed circuit board from a copper clad substrate which comprises: (a) covering at least one surface of the copper cladding with a coating of a polymerizable protective material; (b) masking the protective material with a predetermined circuit design image; (c) exposing the protective material through the masking image to a source of energy to polymerize the exposed protective material; (d) removing the non-polymerized protective material not exposed to the source of energy to provide the desired exposed pattern on the surface of the copper cladding; (e) contacting said surface with a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said metal which are more friable than said metal; (f) striking said reaction products with a plurality of abrasive particles at a velocity and for a time sufficient to erode away all or a portion of said reaction products from said surface; and (g) removing the polymerized protective material to provide copper circuits on one or more surfaces of said board.
Claim 28
Independent Claim
176 words
A method of preparing a printed circuit board from a copper clad substrate which comprises: (a) covering at least one surface of the copper cladding with a coating of a polymerizable protective material; (b) masking the protective material with a predetermined circuit design image; (c) exposing the protective material through the masking image to a source of energy to polymerize the exposed protective material; (d) removing the non-polymerized protective material not exposed to the source of energy to provide the desired exposed pattern on the surface of the copper cladding; (e) contacting said surface with a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said metal which are more friable than said metal; (f) striking said reaction products with a plurality of abrasive particles at a velocity and for a time sufficient to erode away all or a portion of said reaction products from said surface; and (g) removing the polymerized protective material to provide copper circuits on one or more surfaces of said board.
Claim 29
Dependent Claim
95 words
A method according to claim 24 for manufacturing an electrical circuit board having plated through holes for electrically interconnecting circuits on opposite surfaces of said board which further comprises (a) forming apertures through said substrate at the locations of the desired plated through holes, and electroless copper plating the exposed surfaces of said apertures and opposite surfaces of said substrate prior to covering one or more surfaces of said substrate with said protective material; and (b) electrolytic copper plating said electroless plated apertures and said circuit image after removing said portions of said protective material.
Claim 30
Dependent Claim
88 words
A method according to claim 24 for manufacturing an electrical circuit board having plated through holes for electrically interconnecting circuits on opposite surfaces of said board which further comprises forming apertures through said substrate at the locations of the desired plated through holes, electroless copper plating the exposed surfaces of said apertures and opposite surfaces of said substrate, and electrolytically copper plating said surfaces of said apertures and said surfaces of said substrate prior to covering said one or more surfaces of said substrate with said protective material.
Claim 31
Dependent Claim
38 words
A method according to claim 24 which comprises covering at least two surfaces of said copper cladding with a coating of a polymerizable protective material and electrically interconnecting said copper circuits with one or more plated through holes.
Claim 32
Dependent Claim
22 words
A method according to claim 24 wherein said protective material is a polymerized photoresist adhered to the surface of said copper cladding.
Claim 33
Dependent Claim
195 words
In an improved method of manufacturing printed circuit boards of the type which comprises the steps of: (a) electrolessplating a metal plate onto at least one surface of a substrate composed of an insulating material; (b) applying to a portion of said metal plating a protective material to provide the desired circuit pattern on said surfaces of the metal plating; (c) electroplating the desired circuit pattern with a metal plating; (d) removing said protective material from said metal plated substrate; and (e) differentially etching said metal from a portion of metal cladding covered by said protective material to provide a board having the desired metal circuit pattern on at least one surface thereof; wherein said improvement comprises differentially etching said metal from said board by contacting said metal with a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said metal, which products are more friable than said metal; and striking said reaction products with a plurality of abrasive particles at a velocity and for a time sufficient to erode away all or a portion of said reaction products from the surface of said metal.
Claim 34
Dependent Claim
195 words
In an improved method of manufacturing printed circuit boards of the type which comprises the steps of: (a) electrolessplating a metal plate onto at least one surface of a substrate composed of an insulating material; (b) applying to a portion of said metal plating a protective material to provide the desired circuit pattern on said surfaces of the metal plating; (c) electroplating the desired circuit pattern with a metal plating; (d) removing said protective material from said metal plated substrate; and (e) differentially etching said metal from a portion of metal cladding covered by said protective material to provide a board having the desired metal circuit pattern on at least one surface thereof; wherein said improvement comprises differentially etching said metal from said board by contacting said metal with a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said metal, which products are more friable than said metal; and striking said reaction products with a plurality of abrasive particles at a velocity and for a time sufficient to erode away all or a portion of said reaction products from the surface of said metal.
Claim 35
Independent Claim
245 words
A method of preparing a printed circuit board from a copper clad substrate which comprises: (a) covering one or more surfaces of the copper clad substrate with a coating of a protective material; (b) masking the protective material with a predetermined circuit design image; (c) exposing the protective material to a source of energy to provide a resist layer portion susceptible to an etchant over a desired circuit image on one or more surfaces, and a resist layer portion resistant to said etchant over the remainder of said surfaces; (d) removing those portions of the protective material which are susceptible to the etchant to provide the desired circuit image on said surfaces of the copper cladding; (e) electroplating the desired circuit image with a metallic etch resist; (f) removing the remaining portions of the photoresist from said board exposing a portion of the copper cladding; and (g) removing the exposed copper cladding from the board to provide a board having copper circuit covered by a metallic etch resist, said improvement comprising contacting said exposed copper cladding of step (f) with a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said cladding, which products are more friable than copper; and striking said reaction products with a plurality of abrasive particles at a velocity and for a time sufficient to erode away all or a portion of said reaction products from the surface of said cladding.
Claim 36
Independent Claim
245 words
A method of preparing a printed circuit board from a copper clad substrate which comprises: (a) covering one or more surfaces of the copper clad substrate with a coating of a protective material; (b) masking the protective material with a predetermined circuit design image; (c) exposing the protective material to a source of energy to provide a resist layer portion susceptible to an etchant over a desired circuit image on one or more surfaces, and a resist layer portion resistant to said etchant over the remainder of said surfaces; (d) removing those portions of the protective material which are susceptible to the etchant to provide the desired circuit image on said surfaces of the copper cladding; (e) electroplating the desired circuit image with a metallic etch resist; (f) removing the remaining portions of the photoresist from said board exposing a portion of the copper cladding; and (g) removing the exposed copper cladding from the board to provide a board having copper circuit covered by a metallic etch resist, said improvement comprising contacting said exposed copper cladding of step (f) with a reactive effective amount of one or more reactive gases forming one or more reaction products on the surface of said cladding, which products are more friable than copper; and striking said reaction products with a plurality of abrasive particles at a velocity and for a time sufficient to erode away all or a portion of said reaction products from the surface of said cladding.
Claim 37
Dependent Claim
31 words
A method according to claim 30 wherein the remaining portions of the photoresist after the metallic etch resist is electroplated are removed by the action of reactive gases and abrasive particles.
Claim 38
Dependent Claim
59 words
A method according to claim 30 which further comprises: (a) electroless copper plating one or more surfaces of said copper clad substrate prior to covering said one or more surfaces of said substrate with said protective material; and (b) electrolytic copper plating said circuit image after removing said portions of said protective material which are susceptible to said etchant.
Claim 39
Dependent Claim
102 words
A method according to claim 30 for manufacturing an electrical circuit board having plated through holes for electrically inter connecting circuits on opposite surfaces of said board which further comprises (a) forming apertures through said substrate at the locations of the desired plated through holes, and electroless copper plating the exposed surfaces of said apertures and opposite surfaces of said substrate prior to covering one or more surfaces of said substrate with said protective material; and (b) electrolytic copper plating said electroless plated apertures and said circuit image after removing said portions of said protective material which are susceptible to said etchant.
Claim 40
Dependent Claim
35 words
A method according to claim 30 which further comprises electroless copper plating one or more surfaces of said substrate, and thereafter electrolytically copper plating said surfaces prior to covering said surfaces with said protective material.
Claim 41
Dependent Claim
89 words
A method according to claim 34 for manufacturing an electrical circuit board having plated through holes for electrically inter connecting circuits on opposite surfaces of said board which further comprises forming apertures through said substrate at the locations of the desired plated through holes, electroless copper plating the exposed surfaces of said apertures and opposite surfaces of said substrate, and electrolytically copper plating said surfaces of said apertures and said surfaces of said substrate prior to covering said one or more surfaces of said substrate with said protective material.
References Cited (Backward Citations)
US4451327A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-10 | 1989-08-12 | 1990-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-10 | 1993-08-12 | 1994-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-10 | 1997-08-12 | 1998-02-11 | $7700.00 | Window Closed / Lapsed |