Method of forming a nitride layer
Assignee: Toyota Central R&D Labs Inc
•
Filing: 1985-05-14
•
Granted: 1986-02-11
•
Expires: 2005-05-14
Abstract
Abstract A method of forming a layer of a nitride or carbonitride of titanium, vanadium or the like on the surface of an article to be treated includes: disposing a treating material composed of refractory powder, powder of a metal or alloy of a nitride forming element and a halide power, and the article to be treated in a fluidized bed furnace; and introducing a nitrogen-containing gas into the furnace under a heated condition to fluidize the treating material, thereby effecting the surface treatment. This method provides a nitride or carbonitride layer having a smooth surface and a uniform thickness rapidly and safely without using hydrogen and a halogen vapor.
Inventors
- 👤 Tohru Arai
- 👤 Junji Endo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 01:30
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/34; C23C16/36; C23C16/44; C23C16/442; C23C16/448; C23C16/4488
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
120 words
A method of forming a nitride or carbonitride layer on the surface of an article to be treated, which comprises the steps of: disposing a treating material and the article to be treated in a fluidized bed furnace, said treating material comprising a refractory powder, a nitride forming powder composed of at least one nitride forming metal or alloy and a halide powder composed of at least one of a halogenated ammonium salt and a metal halide which is sublimable or vaporizable at a temperature not more than a treating temperature; and introducing a nitrogen-containing gas into said furnace under heat to fluidize said treating material to thereby form a nitride or carbonitride layer on the surface of said article.
Claim 2
Independent Claim
120 words
A method of forming a nitride or carbonitride layer on the surface of an article to be treated, which comprises the steps of: disposing a treating material and the article to be treated in a fluidized bed furnace, said treating material comprising a refractory powder, a nitride forming powder composed of at least one nitride forming metal or alloy and a halide powder composed of at least one of a halogenated ammonium salt and a metal halide which is sublimable or vaporizable at a temperature not more than a treating temperature; and introducing a nitrogen-containing gas into said furnace under heat to fluidize said treating material to thereby form a nitride or carbonitride layer on the surface of said article.
Claim 3
Dependent Claim
37 words
A method according to claim 1, wherein said treating material contains 5 to 50% by weight of said nitride forming powder and 0.2 to 3% by weight of said halide powder, the balance being said refractory powder.
Claim 4
Dependent Claim
22 words
A method according to claim 1, wherein said refractory powder comprises at least one of alumina, silicon oxide, titanium oxide and zirconia.
Claim 5
Dependent Claim
30 words
A method according to claim 1, wherein said nitride forming metal is at least one selected from the group consisting of titanium, vanadium, niobium, tantalum, chromium, manganese, molybdenum and tungsten.
Claim 6
Dependent Claim
30 words
A method according to claim 1, wherein said halogenated ammonium salt is at least one selected from the group consisting of ammonium chloride, ammonium bromide, ammonium iodide and ammonium fluoride.
Claim 7
Dependent Claim
31 words
A method according to claim 1, wherein said metal halide is at least one selected from the group consisting of titanium fluoride, vanadium fluoride, vanadium chloride, titanium bromide and ferric chloride.
Claim 8
Dependent Claim
19 words
A method according to claim 1, wherein said treating material has a grain size of 60 to 350 mesh.
Claim 9
Dependent Claim
22 words
A method according to claim 1, wherein said nitrogen-containing gas is selected from a nitrogen gas and a nitrogen gas containing ammonia.
Claim 10
Dependent Claim
24 words
A method according to claim 1, wherein said nitrogen-containing gas has a flow rate of at least 50 cm per minute in said furnace.
Claim 11
Dependent Claim
21 words
A method according to claim 9, wherein said flow rate is in the range of 50 to 700 cm per minute.
Claim 12
Dependent Claim
21 words
A method according to claim 10, wherein said flow rate is in the range of 60 to 600 cm per minute.
Claim 13
Dependent Claim
25 words
A method according to claim 1, wherein said nitrogen-containing gas has a pressure of 0.5 to 2 kg/cm 2 at an inlet of said furnace.
Claim 14
Dependent Claim
33 words
A method according to claim 1, wherein said article is formed of a material selected from the group consisting of iron, nickel, cobalt or an alloy thereof, a cemented carbide article and graphite.
Claim 15
Dependent Claim
28 words
A method according to claim 1, wherein said article contains at least 0.1% by weight of carbon to form a carbonitride layer on the surface of said article.
Claim 16
Dependent Claim
19 words
A method according to claim 1, wherein said heating temperature is in the range of 700° to 1200° C.
Claim 17
Dependent Claim
19 words
A method according to claim 1, wherein said heating time is in the range of 0.5 to 16 hours.
Claim 18
Dependent Claim
49 words
A method according to claim 1, wherein coarse particles of refractory powder having a grain size of 5 to 20 mesh are further disposed in said furnace between a gas inlet thereof and said treating material, thereby preventing said gas inlet from being closed due to said treating material.
Claim 19
Dependent Claim
46 words
A method according to claim 2, wherein said treating material has a grain size of 60 to 350 mesh, said flow rate is in the range of 50 to 700 cm per minute and said heating temperature is in the range of 700° to 1200° C.
Claim 20
Dependent Claim
43 words
A method according to claim 18, wherein coarse particles of refractory powder having a grain size of 5 to 20 mesh are further disposed in said furnace between a gas inlet thereof and said treating material, and said nitrogen-containing gas is nitrogen gas.
Claim 21
Dependent Claim
19 words
A method according to claim 19, wherein said treating material comprises ferrovanadium powder, ammonium chloride powder and alumina powder.
Claim 22
Dependent Claim
19 words
A method according to claim 19, wherein said treating material comprises ferrotitanium powder, ammonium chloride powder and alumina powder.
Claim 23
Dependent Claim
19 words
A method according to claim 19, wherein said treating material comprises ferrotitanium powder, titanium fluoride powder and alumina powder.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-10 | 1989-08-12 | 1990-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-10 | 1993-08-12 | 1994-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-10 | 1997-08-12 | 1998-02-11 | $7700.00 | Window Closed / Lapsed |