Method of producing wear-protection layers on surfaces of structural parts of titanium or titanium-base alloys
Assignee: MTU Aero Engines AG
•
Filing: 1984-05-22
•
Granted: 1986-05-13
•
Expires: 2004-05-22
Abstract
Abstract A method of producing a wear protection coating on a surface of a structural part of titanium or a titanium base alloy comprising applying a metallic nickel layer which adheres to the surface of the structural part and thereafter subjecting the thus coated structural part to a heat treatment to form diffusion layers of Ti 2 Ni and TiNi 3 between the titanium and the nickel. Thereafter, the layer of nickel alone or with the layer of TiNi 3 is removed to leave the titanium part covered by a protection layer of the remaining diffusion layer.
Inventors
- 👤 Martin Thoma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:48
CPC Classifications
C; C23; C23C; C23C10/00; C23C10/28; C23C10/60
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
93 words
A method of producing a wear-protection coating on a surface of a structural part of titanium or a titanium-base alloy comprising applying a metallic nickel layer which adheres to the surface of the structural part, and subjecting the thus coated structural part to a heat treatment to form diffusion layers of Ti 2 Ni and TiNi 3 between the titanium material, on the one hand, and the layer of nickel, on the other hand, and thereafter chemically removing all of the layer of nickel still present to expose one of the diffusion layers.
Claim 2
Independent Claim
93 words
A method of producing a wear-protection coating on a surface of a structural part of titanium or a titanium-base alloy comprising applying a metallic nickel layer which adheres to the surface of the structural part, and subjecting the thus coated structural part to a heat treatment to form diffusion layers of Ti 2 Ni and TiNi 3 between the titanium material, on the one hand, and the layer of nickel, on the other hand, and thereafter chemically removing all of the layer of nickel still present to expose one of the diffusion layers.
Claim 3
Dependent Claim
21 words
A method as claimed in claim 1, comprising removing the layer of TiNi 3 in addition to the layer of nickel.
Claim 4
Dependent Claim
38 words
A method as claimed in claim 1, comprising eroding the surface of the structural part containing titanium material before applying the nickel layer to enhance the strength of bond between the metallic nickel layer and the titanium material.
Claim 5
Dependent Claim
20 words
A method as claimed in claim 3 wherein the eroding of the surface comprises etching and activation of said surface.
Claim 6
Dependent Claim
38 words
A method as claimed in claim 4, wherein said etching is effected in a solution of nitric acid and hydrofluoric acid and the activation is effected in a bath consisting of chromic acid, hydrofluoric acid and hexafluorosilicic acid.
Claim 7
Dependent Claim
24 words
A method as claimed in claim 1 wherein the metallic nickel is applied in a layer having a thickness of 5 to 50 μm.
Claim 8
Dependent Claim
15 words
A method as claimed in claim 6, wherein the layer of nickel is deposited electrolytically.
Claim 9
Dependent Claim
22 words
A method as claimed in claim 7 wherein the electrolytic deposit of nickel is effected in a galvanic bath containing nickel sulfamate.
Claim 10
Dependent Claim
15 words
A method as claimed in claim 6, wherein the layer of nickel is deposited chemically.
Claim 11
Dependent Claim
36 words
A method as claimed in claim 9 wherein the chemical deposit of nickel is effected by reaction of the titanium surface with a bath consisting of Ni salt, a complexing agent, and a chemical reducing agent.
Claim 12
Dependent Claim
14 words
A method as claimed in claim 10 wherein the chemical reducing agent is hypophosphite.
Claim 13
Dependent Claim
30 words
A method as claimed in claim 1 wherein the heat treatment is effected at a temperature of 400° to 950° C. for a period of 30 minutes to 300 hours.
Claim 14
Dependent Claim
36 words
A method as claimed in claim 1, wherein the chemical removal of the layer of nickel is effected by the action of HNO 3 or a cyanidic nitroaromatic solution at temperatures between 10° and 60° C.
Claim 15
Dependent Claim
36 words
A method as claimed in claim 2 wherein the chemical removal of the TiNi 3 layer is effected by the action of HNO 3 or a cyanidic nitroaromatic solution at temperatures between 10° and 60° C.
Claim 16
Dependent Claim
16 words
A method as claimed in claim 1 wherein the heat treatment is effected at 600° C.
Claim 17
Dependent Claim
16 words
A method as claimed in claim 15 wherein the heat treatment is effected for 8 hours.
Claim 18
Dependent Claim
37 words
A method as claimed in claim 15 wherein the layers of Ti 2 Ni and TiNi 3 are of equal thickness, the layer of TiNi 3 being of greater hardness than the layer of Ti 2 Ni.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-12 | 1989-11-11 | 1990-05-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-12 | 1993-11-11 | 1994-05-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-12 | 1997-11-11 | 1998-05-13 | $7700.00 | Window Closed / Lapsed |