Laser marking method and ablative coating for use therein
Assignee: NXP USA Inc
•
Filing: 1984-12-17
•
Granted: 1986-06-10
•
Expires: 2004-12-17
Abstract
Abstract Laser marking of metal surfaces, particularly semiconductor device packages, is accomplished by depositing an electroless nickel layer on the surface, converting the nickel surface to a form in which it is highly absorptive of radiant energy and exposing the converted nickel surface to laser energy through a mask. The resulting mark is highly resistant to abrasion and corrosion. In addition, the method is highly suitable for use with automated laser marking equipment. Furthermore, it appears that the presence of the converted electroless nickel surface in the region of welds increases the hermeticity of the welds. This is particularly useful in packages of the TO-3 type and similar types.
Inventors
- 👤 Lee E. Folk
- 👤 Reginald K. Asher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 07:05
CPC Classifications
C; C23; C23F; C23F4/00; C23F4/02; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/32; B; B41; B41M; B41M5/00; B41M5/24; Y; Y10; Y10S; Y10S438/00; Y10S438/94
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
85 words
A method of marking a metal surface comprising the steps of: forming a layer of electroless nickel on said surface; exposing said layer of electroless nickel to an acid solution capable of converting at least a portion of said electroless nickel layer to a radiant energy absorptive form; baking said converted electroless nickel layer at an elevated temperature for a predetermined length of time; and exposing a portion of said converted, baked electroless nickel layer to radiant energy sufficient to substantially remove said exposed portion.
Claim 2
Independent Claim
85 words
A method of marking a metal surface comprising the steps of: forming a layer of electroless nickel on said surface; exposing said layer of electroless nickel to an acid solution capable of converting at least a portion of said electroless nickel layer to a radiant energy absorptive form; baking said converted electroless nickel layer at an elevated temperature for a predetermined length of time; and exposing a portion of said converted, baked electroless nickel layer to radiant energy sufficient to substantially remove said exposed portion.
Claim 3
Dependent Claim
24 words
A method according to claim 1 wherein said acid solution comprises: approximately 75% by volume acetic acid; and approximately 25% by volume nitric acid.
Claim 4
Dependent Claim
18 words
A method according to claim 2 wherein said acid solution further comprises: approximately 0.2% by volume wetting agent.
Claim 5
Dependent Claim
28 words
A method according to claim 1 wherein said step of baking further comprises: holding said layer at a temperature of approximately 200 degrees C. for approximately one hour.
Claim 6
Dependent Claim
30 words
A method according to claim 1 wherein said step of baking further comprises: holding said layer at a temperature of approximately 400 degrees C. for approximately 2 to 5 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-09 | 1989-12-09 | 1990-06-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-09 | 1993-12-09 | 1994-06-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-09 | 1997-12-09 | 1998-06-10 | $7700.00 | Window Closed / Lapsed |