Magnetic recording medium and method for making
Assignee: TDK Corp
•
Filing: 1984-04-25
•
Granted: 1986-06-24
•
Expires: 2004-04-25
Abstract
Abstract In a magnetic recording medium comprising a non-magnetic substrate and a magnetic layer of Co or Co-Ni in the form of a continuous thin film on the substrate, the magnetic layer has oxygen-rich sub-layers at its surfaces adjacent to and remote from the substrate. The oxygen-rich sub-layers are produced by injecting energy particles containing oxygen to the surface of the substrate during the initial and final stages of formation of the magnetic layer.
Inventors
- 👤 Kiyoshi Noguchi
- 👤 Koji Kobayashi
- 👤 Suguru Takayama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 01:30
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/64; G11B5/66; G11B5/672; G11B5/73; G11B5/739; G11B5/73923; G11B5/73927; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
71 words
In a magnetic recording medium comprising a non-magnetic substrate and a magnetic layer in the form of a continuous thin film on the substrate, the magnetic layer consisting essentially of cobalt, oxygen and at least one nickel and chromium, the improvement wherein said magnetic layer has at its surfaces adjacent to and remote from said substrate sub-layers which are richer in oxygen than the remaining intermediate portion of the magnetic layer.
Claim 2
Dependent Claim
71 words
In a magnetic recording medium comprising a non-magnetic substrate and a magnetic layer in the form of a continuous thin film on the substrate, the magnetic layer consisting essentially of cobalt, oxygen and at least one nickel and chromium, the improvement wherein said magnetic layer has at its surfaces adjacent to and remote from said substrate sub-layers which are richer in oxygen than the remaining intermediate portion of the magnetic layer.
Claim 3
Dependent Claim
34 words
The magnetic recording medium according to claim 1 wherein the oxygen content of each of the oxygen-rich sub-layers ranges from 0.2 to 0.5 in atomic ratio based on the metal content of said sub-layers.
Claim 4
Dependent Claim
26 words
The magnetic recording medium according to claim 1 or 2 wherein each of the oxygen-rich sub-layers has a thickness of about 50 to about 500 angstrom.
Claim 5
Dependent Claim
30 words
The magnetic recording medium according to claim 1 wherein the oxygen content of each of the oxygen rich sub-layers is at least 50% higher than that of the remaining portion.
Claim 6
Dependent Claim
25 words
The magnetic recording medium according to claim 1 wherein the magnetic layer contains nickel and the weight ratio of Co/Ni is at least about 1.5.
Claim 7
Dependent Claim
29 words
The magnetic recording medium according to claim 5 wherein the magnetic layer contains chromium and the weight ratio of Cr/Co or Cr/(Co+Ni) ranges from about 0.001 to about 0.1.
Claim 8
Dependent Claim
25 words
The magnetic recording medium according to claim 5 wherein the magnetic layer has an atomic ratio of O/Co or O/(Co+Ni) of about 0.5 or lower.
Claim 9
Dependent Claim
22 words
The magnetic recording medium according to claim 1 wherein the magnetic layer has a thickness of about 0.05 to about 0.5 micrometers.
Claim 10
Independent Claim
134 words
A method for making a magnetic recording medium comprising the steps of forming a magnetic layer in the form of a continuous thin film on a non-magnetic substrate by evaporating cobalt and at least one of nickel and chromium, and directing energy particles containing oxygen to the surface of the substrate on which the magnetic layer is being formed during an initial stage of formation of the magnetic layer and at least one of the periods during formation of that surface portion of the magnetic layer positioned remote from the substrate and after formation of that surface portion of the magnetic layer positioned remote from the substrate, thereby producing a magnetic layer consisting essentially of an oxygen-rich portion adjacent to the substrate, an oxygen-poor intermediate portion, and an oxygen-rich portion remote from the substrate.
Claim 11
Independent Claim
134 words
A method for making a magnetic recording medium comprising the steps of forming a magnetic layer in the form of a continuous thin film on a non-magnetic substrate by evaporating cobalt and at least one of nickel and chromium, and directing energy particles containing oxygen to the surface of the substrate on which the magnetic layer is being formed during an initial stage of formation of the magnetic layer and at least one of the periods during formation of that surface portion of the magnetic layer positioned remote from the substrate and after formation of that surface portion of the magnetic layer positioned remote from the substrate, thereby producing a magnetic layer consisting essentially of an oxygen-rich portion adjacent to the substrate, an oxygen-poor intermediate portion, and an oxygen-rich portion remote from the substrate.
Claim 12
Dependent Claim
12 words
The method according to claim 9 wherein the oxygen contain ionic oxygen.
Claim 13
Dependent Claim
14 words
The method according to claim 9 or 10 wherein the oxygen contain neutral oxygen.
Claim 14
Dependent Claim
58 words
The method according to claim 9 wherein the energy particles are directed during the initial stage of formation of the magnetic layer until the magnetic layer is formed to 1/3 of the final thickness and during a final stage of formation of the magnetic layer after the magnetic layer has been formed to 2/3 of the final thickness.
Claim 15
Dependent Claim
24 words
The method according to claim 9 wherein the energy particles have an energy in the range of about 10 eV to about 10 keV.
Claim 16
Dependent Claim
36 words
The method according to claim 9 wherein the magnetic layer is formed by depositing an evaporated source material to the surface of the substrate at an angle with respect to the normal to the substrate surface.
Claim 17
Independent Claim
119 words
A method for making a magnetic recording medium comprising the steps of forming a magnetic layer in the form of a continuous thin film on a non-magnetic substrate by evaporating cobalt and at least one of nickel and chromium, and directing energy particles containing oxygen to the surface of the substrate on which the magnetic layer is being formed during an initial stage of formation of the magnetic layer, and introducing oxygen gas into the layer-forming site during formation of that surface portion of the magnetic layer positioned remote from the substrate, thereby producing a magnetic layer consisting essentially of an oxygen-rich portion adjacent to the substrate, an oxygen-poor intermediate portion, and an oxygen-rich portion remote from the substrate.
Claim 18
Independent Claim
119 words
A method for making a magnetic recording medium comprising the steps of forming a magnetic layer in the form of a continuous thin film on a non-magnetic substrate by evaporating cobalt and at least one of nickel and chromium, and directing energy particles containing oxygen to the surface of the substrate on which the magnetic layer is being formed during an initial stage of formation of the magnetic layer, and introducing oxygen gas into the layer-forming site during formation of that surface portion of the magnetic layer positioned remote from the substrate, thereby producing a magnetic layer consisting essentially of an oxygen-rich portion adjacent to the substrate, an oxygen-poor intermediate portion, and an oxygen-rich portion remote from the substrate.
Claim 19
Dependent Claim
16 words
The method according to claim 15 wherein the oxygen in the energy particles contain ionic oxygen.
Claim 20
Dependent Claim
18 words
The method according to claim 15 or 16 wherein the oxygen in the energy particles contain neutral oxygen.
Claim 21
Dependent Claim
58 words
The method according to claim 15 wherein the energy particles are directed during the initial stage of formation of the magnetic layer until the magnetic layer is formed to 1/3 of the final thickness and during the final stage of formation of the magnetic layer after the magnetic layer has been formed to 2/3 of the final thickness.
Claim 22
Dependent Claim
24 words
The method according to claim 15 wherein the energy particles have an energy in the range of about 10 eV to about 10 keV.
Claim 23
Dependent Claim
36 words
The method according to claim 15 wherein the magnetic layer is formed by depositing an evaporated source material to the surface of the substrate at an angle with respect to the normal to the substrate surface.
Claim 24
Independent Claim
114 words
A method for making a magnetic recording medium comprising the steps of forming a magnetic layer in the form of a continuous thin film on a non-magnetic substrate by evaporating cobalt and at least one of nickel and chromium, and directing energy particles containing oxygen to the surface of the substrate on which the magnetic layer is being formed during an initial stage of formation of the magnetic layer, and subjecting the surface of the magnetic layer to an oxidizing treatment after formation of the magnetic layer thereby producing a magnetic layer consisting essentially of an oxygen-rich portion adjacent to the substrate, an oxygen-poor intermediate portion, and an oxygen-rich portion remote from the substrate.
Claim 25
Independent Claim
114 words
A method for making a magnetic recording medium comprising the steps of forming a magnetic layer in the form of a continuous thin film on a non-magnetic substrate by evaporating cobalt and at least one of nickel and chromium, and directing energy particles containing oxygen to the surface of the substrate on which the magnetic layer is being formed during an initial stage of formation of the magnetic layer, and subjecting the surface of the magnetic layer to an oxidizing treatment after formation of the magnetic layer thereby producing a magnetic layer consisting essentially of an oxygen-rich portion adjacent to the substrate, an oxygen-poor intermediate portion, and an oxygen-rich portion remote from the substrate.
Claim 26
Dependent Claim
12 words
The method according to claim 21 wherein the oxygen contains ionic oxygen.
Claim 27
Dependent Claim
14 words
The method according to claim 21 or 22 wherein the oxygen contains neutral oxygen.
Claim 28
Dependent Claim
34 words
The method according to claim 21 wherein the energy particles are directed during the initial stage of formation of the magnetic layer until the magnetic layer is formed to 1/3 of the final thickness.
Claim 29
Dependent Claim
24 words
The method according to claim 21 wherein the energy particles have an energy in the range of about 10 eV to about 10 keV.
Claim 30
Dependent Claim
36 words
The method according to claim 21 wherein the magnetic layer is formed by depositing an evaporated source material to the surface of the substrate at an angle with respect to the normal to the substrate surface.
Claim 31
Independent Claim
120 words
A method for making a magnetic recording medium comprising the steps of forming a magnetic layer in the form of a continuous thin film on a non-magnetic substrate by evaporating cobalt and at least one of nickel and chromium, and introducing oxygen to the layer-forming site during an initial stage of formation of the magnetic layer, and directing energy particles containing oxygen to that surface portion positioned remote from the substrate during at least one of the period of formation of said surface portion and the period after formation of said surface portion, thereby producing a magnetic layer consisting essentially of an oxygen-rich portion adjacent to the substrate, an oxygen-poor intermediate portion, and an oxygen-rich portion remote from the substrate.
Claim 32
Independent Claim
120 words
A method for making a magnetic recording medium comprising the steps of forming a magnetic layer in the form of a continuous thin film on a non-magnetic substrate by evaporating cobalt and at least one of nickel and chromium, and introducing oxygen to the layer-forming site during an initial stage of formation of the magnetic layer, and directing energy particles containing oxygen to that surface portion positioned remote from the substrate during at least one of the period of formation of said surface portion and the period after formation of said surface portion, thereby producing a magnetic layer consisting essentially of an oxygen-rich portion adjacent to the substrate, an oxygen-poor intermediate portion, and an oxygen-rich portion remote from the substrate.
Claim 33
Dependent Claim
12 words
The method according to claim 27 wherein the oxygen contains ionic oxygen.
Claim 34
Dependent Claim
14 words
The method according to claim 27 or 28 wherein the oxygen contains neutral oxygen.
Claim 35
Dependent Claim
64 words
The method according to claim 27 wherein the oxygen is introduced during the initial stage of formation of the magnetic layer until the magnetic layer is formed to about 1/3 of the final thickness, and the energy particles are directed during the final stage of formation of the magnetic layer after the magnetic layer has been formed to about 2/3 of the final thickness.
Claim 36
Dependent Claim
24 words
The method according to claim 27 wherein the energy particles have an energy in the range of about 10 eV to about 10 keV.
Claim 37
Dependent Claim
36 words
The method according to claim 27 wherein the magnetic layer is formed by depositing an evaporated source material to the surface of the substrate at an angle with respect to the normal to the substrate surface.
References Cited (Backward Citations)
US3795542A
Cited
US3829372A
Cited
US4013534A
Cited
US4220117A
Cited
US4323629A
Cited
US4387136A
Cited
US4450186A
Cited
US4477489A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-23 | 1989-12-23 | 1990-06-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-23 | 1993-12-23 | 1994-06-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-06-23 | 1997-12-23 | 1998-06-24 | $7700.00 | Window Closed / Lapsed |