Process for drying polymeric beads and associating shading pigments therewith
Assignee: PRC Desoto International Inc
•
Filing: 1984-10-09
•
Granted: 1986-07-15
•
Expires: 2004-10-09
Abstract
Abstract A process for drying a water-wet paste containing polymeric beads without agglomeration is disclosed in which there is added to the wet paste a proportion of an organic solvent which forms an azeotrope with water, such as methyl isobutyl ketone, in an amount providing a stirrable mixture, and the solvent-containing aqueous paste is heated to remove the water as an azeotrope with the solvent and to produce a water free suspension of the beads in organic solvent. The proportion of azeotropic solvent can be minimized by adding a resinous vehicle in organic solvent solution to the solvent-containing aqueous paste after substantially all the water has been removed, and continuing the application of heat to remove undesired organic solvent and thereby increase the solids content. As a feature of the invention, a pigment which is incompatible with the azeotropic solvent, such as an aqueous dispersion of lamp black, is added to the aqueous paste either before or after the addition of azeotropic organic solvent to be present while the water is azeotropically removed to avoid flooding.
Inventors
- 👤 Laura M. Wells
- 👤 Fred D. Hawker
- 👤 Maryam L. Dachniwskyj
- 👤 Charles W. Strobel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:29
CPC Classifications
C; C08; C08F; C08F6/00; C08F6/008; C08J; C08J3/00; C08J3/20; C08J3/205; C08J3/21; C08J3/215
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
119 words
A process for drying a water-wet paste containing polymeric beads without agglomeration comprising, adding to said wet paste a proportion of an organic solvent which forms an azeotrope with water in an amount providing a stirrable mixture, and heating the solvent-containing aqueous paste to remove the water as an azeotrope with said solvent and to produce a water free suspension of said beads in organic solvent, the proportion of said organic solvent in the suspension which is formed being minimized by adding a resinous vehicle in organic solvent solution to the solvent-containing aqueous paste after substantially all the water has been removed, and continuing the application of heat to remove undesired organic solvent and thereby increase the solids content.
Claim 2
Dependent Claim
119 words
A process for drying a water-wet paste containing polymeric beads without agglomeration comprising, adding to said wet paste a proportion of an organic solvent which forms an azeotrope with water in an amount providing a stirrable mixture, and heating the solvent-containing aqueous paste to remove the water as an azeotrope with said solvent and to produce a water free suspension of said beads in organic solvent, the proportion of said organic solvent in the suspension which is formed being minimized by adding a resinous vehicle in organic solvent solution to the solvent-containing aqueous paste after substantially all the water has been removed, and continuing the application of heat to remove undesired organic solvent and thereby increase the solids content.
Claim 3
Dependent Claim
14 words
A process as recited in claim 1 in which said polymeric beads are vesiculated.
Claim 4
Dependent Claim
16 words
A process as recited in claim 1 in which said organic azeotropic solvent is water immiscible.
Claim 5
Dependent Claim
34 words
A process as recited in claim 1 in which azeotropic organic solvent is added to the aqueous paste in an amount to provide a ratio of solvent to paste of from 0.5:1 to 10:1.
Claim 6
Dependent Claim
16 words
A process as recited in claim 1 in which said azeotropic solvent is methyl isobutyl ketone.
Claim 7
Dependent Claim
112 words
A process for drying a water-wet paste containing polymeric beads without agglomeration comprising, adding to said wet paste a proportion of an organic solvent which forms an azeotrope with water in an amount providing a stirrable mixture, and heating the solvent-containing aqueous paste to remove the water as an azeotrope with said solvent and to produce a water free suspension of said beads in organic solvent, a pigment dispersion which is incompatible with said organic solvent being added to the aqueous paste either before or after the addition of azeotropic organic solvent to be present while the water is azeotropically removed, whereby said pigment adheres to the surface of the vesiculated beads.
Claim 8
Dependent Claim
112 words
A process for drying a water-wet paste containing polymeric beads without agglomeration comprising, adding to said wet paste a proportion of an organic solvent which forms an azeotrope with water in an amount providing a stirrable mixture, and heating the solvent-containing aqueous paste to remove the water as an azeotrope with said solvent and to produce a water free suspension of said beads in organic solvent, a pigment dispersion which is incompatible with said organic solvent being added to the aqueous paste either before or after the addition of azeotropic organic solvent to be present while the water is azeotropically removed, whereby said pigment adheres to the surface of the vesiculated beads.
Claim 9
Dependent Claim
14 words
A process as recited in claim 6 in which said pigment dispersion is water-based.
Claim 10
Dependent Claim
14 words
A process as recited in claim 6 in which said pigment is lamp black.
Claim 11
Dependent Claim
44 words
A process as recited in claim 6 in which said polymeric beads are vesiculated, said organic azeotropic solvent is water immiscible, and is added to said aqueous paste in an amount to provide a ratio of solvent to paste of from 0.5:1 to 10:1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-14 | 1990-01-13 | 1990-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-14 | 1994-01-13 | 1994-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-14 | 1998-01-13 | 1998-07-15 | $7700.00 | Window Closed / Lapsed |