US4629659A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Corrosion resistant surface-treated steel strip and process for making
Assignee: JFE Steel Corp
•
Filing: 1984-05-14
•
Granted: 1986-12-16
•
Expires: 2004-05-14
Abstract
Abstract Highly corrosion resistant plated steel strips or sheets adapted for phosphate treatment and cathodic electrodeposition and intended for use in automobiles, are produced by electroplating at least one surface of a steel strip with an alloy consisting essentially of 0.0003 to 15% by weight of phosphorous, balance essentially iron, in a plating bath containing Fe 2+ ions in an amount of from 0.3 mol/liter to the solubility limit and hypophosphorous acid and/or a hypophosphite in an amount of 0.001 to 25 g/liter expressed as NaH 2 PO 2 .H 2 O at a pH of 1.0 to 5.0, a temperature of 30° to 60° C., and a current density of from more than 20 to 200 A/dm 2 , preferably 40 to 150 A/dm 2 . A top coat can be applied thereover, of one element selected from the group consisting of Ni, Zn, Mn, and Ti, deposited on the Fe-P plating layer to a build-up of 5 to 50 mg/m 2 . A lower layer of zinc or a zinc alloy can also be electrodeposited on at least one surface of the steel strip, prior to formation of the Fe-P layer. A surface film can be formed by chemically treating the Fe-P plating layer with a phosphate.
Inventors
- 👤 Kazuaki Kyono
- 👤 Shigeo Kurokawa
- 👤 Hajime Kimura
- 👤 Toshio Irie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 11:15
CPC Classifications
C; C12; C12N; C12N15/00; C25; C25D; C25D5/00; C25D5/10; C23; C23C; C23C22/00; C23C22/78; C25D3/00; C25D3/02; C25D3/56; C25D3/562; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12799; Y10T428/12861; Y10T428/12951
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
108 words
An Fe-P/Zn or Zn alloy double layer plated steel strip adapted for phosphate treatment, comprising a steel strip, a lower layer of zinc or a zinc alloy deposited on at least one surface of the steel strip, and an upper layer consisting essentially of 0.0003 to 15% by weight of phosphorus, balance essentially iron, electrodeposited at a current density of from more than 20 to 200 A/dm 2 on said lower layer to a build-up of at least 0.5 g/m 2 , said Fe-P layer ensuring the formation of fine crystals of phosphophyllite having an average size of up to about 5 μm after a subsequent phosphate treatment.
Claim 2
Dependent Claim
108 words
An Fe-P/Zn or Zn alloy double layer plated steel strip adapted for phosphate treatment, comprising a steel strip, a lower layer of zinc or a zinc alloy deposited on at least one surface of the steel strip, and an upper layer consisting essentially of 0.0003 to 15% by weight of phosphorus, balance essentially iron, electrodeposited at a current density of from more than 20 to 200 A/dm 2 on said lower layer to a build-up of at least 0.5 g/m 2 , said Fe-P layer ensuring the formation of fine crystals of phosphophyllite having an average size of up to about 5 μm after a subsequent phosphate treatment.
Claim 3
Dependent Claim
23 words
An Fe-P plated steel strip according to claim 1, wherein the Fe-P layer has a phosphorus content of 0.0003 to 5% by weight.
Claim 4
Dependent Claim
30 words
An Fe-P/Zn or Zn alloy double layer plated steel strip according to claim 1 wherein the Fe-P layer is deposited to a build-up of 0.5 to 8 g/m 2 .
Claim 5
Dependent Claim
30 words
An Fe-P/Zn or Zn alloy double layer plated steel strip according to claim 1 wherein the Fe-P layer is deposited to a build-up of 0.5 to 3 g/m 2 .
Claim 6
Dependent Claim
137 words
An Fe-P/Zn or Zn alloy double layer plated steel strip adapted for phosphate treatment, comprising a steel strip, a lower layer of zinc or zinc alloy deposited on at least one surface of the steel strip, a layer consisting essentially of 0.0003 to 15% by weight of phosphorus, balance essentially iron electrodeposited on said lower layer at a current density of from more than 20 to 200 A/dm 2 to a build-up of at least 0.5 g/m 2 , said Fe-P layer ensuring the formation of fine crystals of phosphophyllite having an average size of up to about 5 μm after a subsequent phosphate treatment, and a topcoat of one element selected from the group consisting of Ni, Zn, Mn and Ti, deposited on said Fe-P layer to a build-up of 5 to 50 mg/m 2 .
Claim 7
Dependent Claim
137 words
An Fe-P/Zn or Zn alloy double layer plated steel strip adapted for phosphate treatment, comprising a steel strip, a lower layer of zinc or zinc alloy deposited on at least one surface of the steel strip, a layer consisting essentially of 0.0003 to 15% by weight of phosphorus, balance essentially iron electrodeposited on said lower layer at a current density of from more than 20 to 200 A/dm 2 to a build-up of at least 0.5 g/m 2 , said Fe-P layer ensuring the formation of fine crystals of phosphophyllite having an average size of up to about 5 μm after a subsequent phosphate treatment, and a topcoat of one element selected from the group consisting of Ni, Zn, Mn and Ti, deposited on said Fe-P layer to a build-up of 5 to 50 mg/m 2 .
Claim 8
Dependent Claim
30 words
An Fe-P/Zn or Zn alloy double layer plated steel strip according to claim 5 wherein the Fe-P layer is deposited to a build-up of 0.5 to 8 g/m 2 .
Claim 9
Dependent Claim
30 words
An Fe-P/Zn or Zn alloy double layer plated steel strip according to claim 5 wherein the Fe-P layer is deposited to a build-up of 0.5 to 3 g/m 2 .
Claim 10
Dependent Claim
101 words
A phosphate treated steel strip having improved corrosion resistance without paint coating, comprising a steel strip, a layer of zinc or a zinc alloy deposited on at least one surface of the steel strip, an uppermost layer consisting essentially of 0.0003 to 15% by weight of phosphorus, balance essentially iron, electrodeposited on said zinc or zinc alloy layer to a build-up of at least 0.5 g/m 2 , and a surface film formed by chemically treating the Fe-P plating layer with a phosphate and consisting essentially of fine crystals of phosphophyllite having an average size of up to about 5 μm.
Claim 11
Dependent Claim
101 words
A phosphate treated steel strip having improved corrosion resistance without paint coating, comprising a steel strip, a layer of zinc or a zinc alloy deposited on at least one surface of the steel strip, an uppermost layer consisting essentially of 0.0003 to 15% by weight of phosphorus, balance essentially iron, electrodeposited on said zinc or zinc alloy layer to a build-up of at least 0.5 g/m 2 , and a surface film formed by chemically treating the Fe-P plating layer with a phosphate and consisting essentially of fine crystals of phosphophyllite having an average size of up to about 5 μm.
Claim 12
Dependent Claim
125 words
A process for making an Fe-P/Zn or Zn alloy double layer plated steel strip, comprising depositing zinc or a zinc alloy on at least one surface of a steel strip, and electroplating on the zinc or zinc alloy layer an alloy consisting essentially of 0.0003 to 15% by weight of phosphorus, balance essentially iron, in a plating bath essentially containing Fe 2+ ions in an amount of from 0.3 mol/liter to the solubility limit and hypophosphorus acid and/or a hypophosphite in an amount of 0.001 to 25 g/liter expressed as NaH 2 PO 2 .H 2 O at a pH of 1.0 to 5.0, a temperature of 30° to 60° C., and a current density of from more than 20 to 200 A/dm 2 .
Claim 13
Dependent Claim
125 words
A process for making an Fe-P/Zn or Zn alloy double layer plated steel strip, comprising depositing zinc or a zinc alloy on at least one surface of a steel strip, and electroplating on the zinc or zinc alloy layer an alloy consisting essentially of 0.0003 to 15% by weight of phosphorus, balance essentially iron, in a plating bath essentially containing Fe 2+ ions in an amount of from 0.3 mol/liter to the solubility limit and hypophosphorus acid and/or a hypophosphite in an amount of 0.001 to 25 g/liter expressed as NaH 2 PO 2 .H 2 O at a pH of 1.0 to 5.0, a temperature of 30° to 60° C., and a current density of from more than 20 to 200 A/dm 2 .
Claim 14
Dependent Claim
15 words
A process according to claim 9, wherein said current density is 40-150 A/dm 2 .
Claim 15
Dependent Claim
46 words
A process according to claim 9, wherein the plating bath contains hypophosphorous acid and/or a hypophosphite in an amount of 0.001 to 8 g/liter expressed as NaH 2 PO 2 .H 2 O thereby electroplating an Fe-P layer containing 0.0003 to 5% by weight of phosphorus.
References Cited (Backward Citations)
SU264098A1
Cited
US2412543A
Cited
US2994126A
Cited
US3086927A
Cited
US3574566A
Cited
US3713902A
Cited
JPS5230728A
Cited
GB1519125A
Cited
JPS56142885A
Cited
JPS5767195A
Cited
JPS57198293A
Cited
JPS5834192A
Cited
JPS5852483A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-15 | 1990-06-16 | 1990-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-15 | 1994-06-16 | 1994-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-15 | 1998-06-16 | 1998-12-16 | $7700.00 | Window Closed / Lapsed |