Ceramic spheroids having low density and high crush resistance
Assignee: Kinetico Inc
•
Filing: 1985-06-12
•
Granted: 1986-12-30
•
Expires: 2005-06-12
Abstract
Abstract Ceramic spheroids having: A. a core made by firing raw materials comprising about: 50-99.8 parts by weight mineral particulates; 0.1 to 50 parts by weight silicon carbide; and 0.1 to 15 parts by weight binder (e.g. bentonite); and B. an outer shell comprising Al 2 O 3 or MgO. More alumina or magnesium oxide is contained in the outer shell than in the core. The core of the ceramic spheroid has closed cell microporosity. The inventive spheroids are characterized by a density less than 2.2 g/cc and can be readily made to have a density less than 1 g/cc. These ceramic spheroids combine high strength (due to the tough outer shell) with low density (due to the closed cell microporosity) and have applications (among others) as buoyant water filtration media and low density fillers.
Inventors
- 👤 James A. Laird
- 👤 Warren R. Beck
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:21
CPC Classifications
C; C09; C09K; C09K8/00; C09K8/60; C09K8/80; B; B01; B01D; B01D39/00; B01D39/02; B01D39/06; B01J; B01J19/00; B01J19/30; C04; C04B; C04B20/00; C04B20/02; C04B20/04; C04B20/06; C04B20/068; E; E21; E21B; E21B43/00; E21B43/25; E21B43/26; E21B43/267; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2998
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
182 words
Fired ceramic spheroids having: A. a core: 1. made from raw materials comprising about: a. 50 to 99.8 parts by weight mineral particulates, 0.1 to 50 parts by weight silicon carbide, and 0.1 to 15 parts by weight binder; 2. wherein the mineral particulates comprise a mineral mixture which has a fired density of less than about 2.9 grams per cubic centimeter when fired above about 1100° C. and includes at least one mineral having chemically bound water or sulphur, in a form which is not substantially water soluble, in amounts sufficient to yield 0.5 to 5.0 weight percent water or 0.04 to 2.0 weight percent sulfur in the total mass of mineral particulates; 3. wherein the binder is characterized by adhering the raw materials together after they are converted to spheroids but before they are fired; 4. said core having a plurality of closed air cells; and B. an outer shell, surrounding the core, comprising a metal oxide selected from aluminum oxide and magnesium oxide; said fired ceramic spheroids having a fired density less than about 2.2 grams per cubic centimeter.
Claim 2
Dependent Claim
182 words
Fired ceramic spheroids having: A. a core: 1. made from raw materials comprising about: a. 50 to 99.8 parts by weight mineral particulates, 0.1 to 50 parts by weight silicon carbide, and 0.1 to 15 parts by weight binder; 2. wherein the mineral particulates comprise a mineral mixture which has a fired density of less than about 2.9 grams per cubic centimeter when fired above about 1100° C. and includes at least one mineral having chemically bound water or sulphur, in a form which is not substantially water soluble, in amounts sufficient to yield 0.5 to 5.0 weight percent water or 0.04 to 2.0 weight percent sulfur in the total mass of mineral particulates; 3. wherein the binder is characterized by adhering the raw materials together after they are converted to spheroids but before they are fired; 4. said core having a plurality of closed air cells; and B. an outer shell, surrounding the core, comprising a metal oxide selected from aluminum oxide and magnesium oxide; said fired ceramic spheroids having a fired density less than about 2.2 grams per cubic centimeter.
Claim 3
Dependent Claim
17 words
The ceramic spheroids of claim 1 having a density less than about 1 gram per cubic centimeter.
Claim 4
Dependent Claim
17 words
The ceramic spheroids of claim 1 having a size within the range of 180 and 840 micrometers.
Claim 5
Dependent Claim
28 words
The ceramic spheroids of claim 1 in which about 3 to 15 parts by weight alumina are included in the raw materials for the core of part A.
Claim 6
Dependent Claim
52 words
The ceramic spheroids of claim 1 in which the mineral particulate of part A.1 comprises a mineral selected from the group consisting of: perlite; mixtures of orthoclase, nepheline, hornblende and diopside; and mixtures of plagioclase and orthoclase feldspar containing at least one mineral selected from apatite, hornblende, biotite, pyrite, perlite and vermiculite.
Claim 7
Dependent Claim
27 words
The ceramic spheroids of claim 1 in which the binder is selected from the group consisting of bentonite, cellulose gum, starch, polyvinyl alcohol, polyvinylacetate, and sodium liginosulphonate.
References Cited (Backward Citations)
US2123536A
Cited
US2566117A
Cited
US2699409A
Cited
US3207588A
Cited
US3354024A
Cited
US3505089A
Cited
US3486706A
Cited
US3657847A
Cited
US3666506A
Cited
DE2921336A1
Cited
GB2037727A
Cited
CA1117987A
Cited
GB2090275A
Cited
EP0087852A1
Cited
EP0101855A1
Cited
EP0116369A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-29 | 1990-06-30 | 1990-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-29 | 1994-06-30 | 1994-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-29 | 1998-06-30 | 1998-12-30 | $7700.00 | Window Closed / Lapsed |