Optical recording member
Assignee: Xerox Corp
•
Filing: 1985-11-08
•
Granted: 1987-01-20
•
Expires: 2005-11-08
Abstract
Abstract A multi-layer optical recording member for use with a recording laser for optical recording and retrieving information thereon, as well as a method of fabricating and using said member is described. The optical recording member comprises in sequential order a structural substrate, a thermally degradable polymer layer, a light absorbing recording layer, a thermally degradable polymer dielectric layer, and a reflective layer. The substrate and the thermally degradable polymer layers are stable under ambient light and temperature conditions and substantially transparent to the recording and reading optical radiation. The combined thicknesses of the light absorbing layer and the dielectric layer are such as to provide anti-reflecting conditionsat the recording wavelength and optical contrast between marked and unmarked areas at the reading wavelength. The optical recording member may be used with a single laser source for both recording and reading. Upon exposure to recording radiation, the portion of the light absorbing layer exposed is heated by the absorbed energy which in turn heats adjacent areas of both thermally degradable polymer layers to a level where at least some polymer decomposition with a consequent evolution of gaseous decomposition products occurs resulting in the formation of a hole in the exposed area of the heat absorbing layer.
Inventors
- 👤 Thomas W. Smith
- 👤 Anthony T. Ward
- 👤 David J. Luca
- 👤 Gordon E. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 07:56
CPC Classifications
G; G11; G11B; G11B7/00; G11B7/004; G11B7/0045; G11B7/24; G11B7/241; G11B7/26; G11B7/242; G11B7/243; G11B2007/24302; G11B2007/24306; G11B2007/24308; G11B7/252; G11B7/257; G11B7/2572; G11B7/2575; G11B7/258; G11B7/2585; Y; Y10; Y10S; Y10S430/00; Y10S430/146; Y10S430/165
Claims Analysis
Total Claims: 48
Claim 1
Independent Claim
195 words
A multi-layer optical recording member for use with a recording laser for optically recording and retrieving information thereon comprising in sequential order a structural substrate, a thermally degradable polymer layer, a thin light absorbing recording layer, a thermally degradable polymer dielectric layer and a reflective layer, said substrate and said thermally degradable polymer layers being stable under ambient light and temperature conditions and substantially transparent to the recording and reading optical radiation, the combined thickness of said light absorbing layer and said dielectric layer being such as to provide anti-reflecting conditions at the recording wavelength and optical contrast between marked and unmarked areas at the reading wavelength, said thermally degradable polymer layers decomposing substantially to gaseous products at temperatures below the melting point of the light absorbing recording layer wherein, upon exposure to recording radiation the portion of the light absorbing layer exposed is heated by the absorbed energy which in turn heats adjacent areas of both thermally degradable polymer layers to a level where at least some polymer decomposition with the consequent evolution of gaseous decomposition products occurs resulting in the formation of a hole in the exposed area of the light absorbing layer.
Claim 2
Dependent Claim
195 words
A multi-layer optical recording member for use with a recording laser for optically recording and retrieving information thereon comprising in sequential order a structural substrate, a thermally degradable polymer layer, a thin light absorbing recording layer, a thermally degradable polymer dielectric layer and a reflective layer, said substrate and said thermally degradable polymer layers being stable under ambient light and temperature conditions and substantially transparent to the recording and reading optical radiation, the combined thickness of said light absorbing layer and said dielectric layer being such as to provide anti-reflecting conditions at the recording wavelength and optical contrast between marked and unmarked areas at the reading wavelength, said thermally degradable polymer layers decomposing substantially to gaseous products at temperatures below the melting point of the light absorbing recording layer wherein, upon exposure to recording radiation the portion of the light absorbing layer exposed is heated by the absorbed energy which in turn heats adjacent areas of both thermally degradable polymer layers to a level where at least some polymer decomposition with the consequent evolution of gaseous decomposition products occurs resulting in the formation of a hole in the exposed area of the light absorbing layer.
Claim 3
Dependent Claim
70 words
The optical recording member according to claim 1, wherein said member is capable of being recorded with radiation of a first wavelength and first energy level to produce a pattern of minute open holes in the light absorbing recording layer which minute pattern is capable of being read with radiation of the same wavelength but at lower energy level below that necessary to form a hole in the recording layer.
Claim 4
Dependent Claim
22 words
The multi-layer optical recording member according to claim 2, wherein said light absorbing recording layer is a thin metal or metal alloy.
Claim 5
Dependent Claim
20 words
The multi-layer optical recording member according to claim 3, wherein said light absorbing layer is gold or a gold alloy.
Claim 6
Dependent Claim
43 words
The multi-layer optical recording member according to claim 4, wherein said light absorbing layer is a gold chromium alloy, the amount of chromium in said alloy being sufficient to lower the thermal conductivity of the layer while retaining its malleable and deformable properties.
Claim 7
Dependent Claim
24 words
The multi-layer optical recording member according to claim 5, wherein said gold chromium alloy comprises from about 20 to about 90 atomic percent chromium.
Claim 8
Dependent Claim
24 words
The multi-layer optical recording member according to claim 6, wherein said gold chromium alloy comprises chromium in an amount greater than 40 atomic percent.
Claim 9
Dependent Claim
26 words
The multi-layer optical recording member according to claim 2, wherein said light absorbing recording layer is from about 25 angstroms to about 200 angstroms in thickness.
Claim 10
Dependent Claim
26 words
The multi-layer optical recording member according to claim 8, wherein said light absorbing recording layer is from about 50 angstroms to about 100 angstroms in thickness.
Claim 11
Dependent Claim
33 words
The multi-layer optical recording member according to claim 2, wherein said thermally degradable polymer layer between said structural substrate and said light absorbing recording layer is at least about 500 angstroms in thickness.
Claim 12
Dependent Claim
32 words
The multi-layer optical recording member according to claim 2, wherein said thermally degradable polymer layer between the light absorbing layer and the reflective layer is at least about 500 angstroms in thickness.
Claim 13
Dependent Claim
20 words
The multi-layer optical recording member according to claim 2, wherein said thermally degradable polymer layers are nitrocellulose or polymethyl methacrylate.
Claim 14
Dependent Claim
15 words
The multi-layer optical recording member according to claim 2, wherein said reflective layer is aluminum.
Claim 15
Dependent Claim
18 words
The multi-layer optical recording member according to claim 2, further including a protective overcoating on said reflective layer.
Claim 16
Dependent Claim
26 words
The multi-layer optical recording member according to claim 2, further including a preformatted information layer between said structural substrate and said first thermally degradable polymer layer.
Claim 17
Independent Claim
220 words
The method of making a multi-layer optical recording member for use with a recording laser for optically recording and retrieving information thereon comprising; providing in sequence a structural substrate which is substantially transparent to the recording and reading optical radiation, spin coating a first substantially transparent thermally degradable polymer layer onto said substrate, vacuum evaporating a light absorbing metal layer onto said first polymer layer, spin coating a substantially transparent thermally degradable dielectric polymer on said metal layer, and vacuum evaporating a light reflective layer on said second polymer layer, the combined thickness of said light absorbing layer and said dielectric layer being such as to provide anti-reflecting conditions at the recording wavelength and optical contrast between marked and unmarked areas at the reading wavelength, said thermally degradable polymer layers decomposing substantially to gaseous products at temperatures below the melting point of the light absorbing recording layer, whereby an optical recording member is provided wherein upon exposure to recording radiation the portion of the light absorbing layer exposed is heated by the absorbed energy which in turn heats adjacent areas of both thermally degradable polymer layers to a level where at least some polymer decomposition with the consequent evolution of gaseous decomposition products occurs resulting in the formation of a hole in the exposed area of the light absorbing layer.
Claim 18
Independent Claim
220 words
The method of making a multi-layer optical recording member for use with a recording laser for optically recording and retrieving information thereon comprising; providing in sequence a structural substrate which is substantially transparent to the recording and reading optical radiation, spin coating a first substantially transparent thermally degradable polymer layer onto said substrate, vacuum evaporating a light absorbing metal layer onto said first polymer layer, spin coating a substantially transparent thermally degradable dielectric polymer on said metal layer, and vacuum evaporating a light reflective layer on said second polymer layer, the combined thickness of said light absorbing layer and said dielectric layer being such as to provide anti-reflecting conditions at the recording wavelength and optical contrast between marked and unmarked areas at the reading wavelength, said thermally degradable polymer layers decomposing substantially to gaseous products at temperatures below the melting point of the light absorbing recording layer, whereby an optical recording member is provided wherein upon exposure to recording radiation the portion of the light absorbing layer exposed is heated by the absorbed energy which in turn heats adjacent areas of both thermally degradable polymer layers to a level where at least some polymer decomposition with the consequent evolution of gaseous decomposition products occurs resulting in the formation of a hole in the exposed area of the light absorbing layer.
Claim 19
Dependent Claim
18 words
The method of claim 16, wherein said light absorbing recording layer is a thin metal or metal alloy.
Claim 20
Dependent Claim
16 words
The method of claim 17, wherein said light absorbing layer is gold or a gold alloy.
Claim 21
Dependent Claim
39 words
The method of claim 18, wherein said light absorbing layer is a gold chromium alloy, the amount of chromium in said alloy being sufficient to lower the thermal conductivity of the layer while retaining its malleable and deformable properties.
Claim 22
Dependent Claim
20 words
The method of claim 19, wherein said gold chromium alloy comprises from about 20 to about 90 atomic percent chromium.
Claim 23
Dependent Claim
20 words
The method of claim 20, wherein said gold chromium alloy comprises chromium in an amount greater than 40 atomic percent.
Claim 24
Dependent Claim
22 words
The method of claim 16, wherein said light absorbing recording layer is from about 25 angstroms to about 200 angstroms in thickness.
Claim 25
Dependent Claim
22 words
The method of claim 22, wherein said light absorbing recording layer is from about 50 angstroms to about 100 angstroms in thickness.
Claim 26
Dependent Claim
29 words
The method of claim 16, wherein said thermally degradable polymer layer being said structural substrate and said light absorbing recording layer is at least about 500 angstroms in thickness.
Claim 27
Dependent Claim
28 words
The method of claim 16, wherein said thermally degradable polymer layer between the light absorbing layer and the reflection layer is at least abut 500 angstroms in thickness.
Claim 28
Dependent Claim
16 words
The method of claim 16, wherein said thermally degradable polymer layers are nitrocellulose or polymethyl methacrylate.
Claim 29
Dependent Claim
11 words
The method of claim 16, wherein said reflective layer is aluminum.
Claim 30
Dependent Claim
18 words
The method of claim 16, including the additional step of providing a protective overcoating on said reflective layer.
Claim 31
Dependent Claim
24 words
The method of claim 16, including the step of embossing a preformatted information layer between said structural substrate and said first thermally degradable layer.
Claim 32
Dependent Claim
29 words
The method of claim 16 including the step of subjecting said first thermally degradable polymer layer to ion bombardment sufficient to increase the nucleation sites in the polymer layer.
Claim 33
Independent Claim
236 words
The method of optically recording information on an optical recording member comprising the steps of: providing a multi-layer optical recording member comprising in sequential order a structural substrate, a thermally degradable polymer layer, a thin light absorbing recording layer, a thermally degradable polymer dielectric layer and a reflective layer, said substrate and said thermally degradable polymer layers being stable under ambient light and temperature conditions and substantially transparent to the recording and reading optical radiation; the combined thickness of said light absorbing layer and said dielectric layer being such as to provide anti-reflecting conditions at the recording wavelength and optical contrast between marked and unmarked areas at the reading wavelength, said thermally degradable polymer layers decomposing substantially to gaseous products at temperatures below the melting point of the light absorbing recording layer; exposing said multi-layer optical recording member to a pattern of recording radiation of a first wavelength and at a first energy level to produce a pattern of minute open holes in the light absorbing recording layer corresponding to said pattern of recording radiation by the light absorbing recording layer becoming heated by the absorbed energy in exposed areas which in turn heat adjacent areas of both thermally degradable polymer layers to a level where at least some polymer decomposition with the consequent evolution of gaseous decomposition products occurs resulting in the formation of a hole in the exposed area of the light absorbing area.
Claim 34
Independent Claim
236 words
The method of optically recording information on an optical recording member comprising the steps of: providing a multi-layer optical recording member comprising in sequential order a structural substrate, a thermally degradable polymer layer, a thin light absorbing recording layer, a thermally degradable polymer dielectric layer and a reflective layer, said substrate and said thermally degradable polymer layers being stable under ambient light and temperature conditions and substantially transparent to the recording and reading optical radiation; the combined thickness of said light absorbing layer and said dielectric layer being such as to provide anti-reflecting conditions at the recording wavelength and optical contrast between marked and unmarked areas at the reading wavelength, said thermally degradable polymer layers decomposing substantially to gaseous products at temperatures below the melting point of the light absorbing recording layer; exposing said multi-layer optical recording member to a pattern of recording radiation of a first wavelength and at a first energy level to produce a pattern of minute open holes in the light absorbing recording layer corresponding to said pattern of recording radiation by the light absorbing recording layer becoming heated by the absorbed energy in exposed areas which in turn heat adjacent areas of both thermally degradable polymer layers to a level where at least some polymer decomposition with the consequent evolution of gaseous decomposition products occurs resulting in the formation of a hole in the exposed area of the light absorbing area.
Claim 35
Dependent Claim
84 words
The method of optically recording information according to claim 31, further including the steps of reading the information recorded on the multi-layer optical recording member by exposing said recorded member to recording optical radiation of said first wavelength but at a lower energy level below that necessary to form a hole in the recording layer whereby the recording optical radiation is reflected by the reflected substrate where it has been exposed by the recording radiation and absorbed by the recording member in other areas.
Claim 36
Dependent Claim
23 words
The method of optically recording information according to claim 31, wherein said light absorbing recording layer is a thin metal or metal alloy.
Claim 37
Dependent Claim
21 words
The method of optically recording information according to claim 33, wherein said light absorbing layer is gold or a gold alloy.
Claim 38
Dependent Claim
44 words
The method of optically recording information according to claim 34, wherein said light absorbing layer is a gold chromium alloy, the amount of chromium in said alloy being sufficient to lower the thermal conductivity of the layer while retaining its mallable and deformable properties.
Claim 39
Dependent Claim
25 words
The method of optically recording information according to claim 35, wherein said gold chromium alloy comprises from about 20 to about 90 atomic percent chromium.
Claim 40
Dependent Claim
25 words
The method of optically recording information according to claim 36, wherein said gold chromium alloy comprises chromium in an amount greater than 40 atomic percent.
Claim 41
Dependent Claim
27 words
The method of opticlly recording information according to claim 31, wherein said light absorbing recording layer is from about 25 angstroms to about 200 angstroms in thickness.
Claim 42
Dependent Claim
27 words
The method of optically recording information according to claim 31, wherein said light absorbing recording layer is from about 50 angstroms to about 100 angstroms in thickness.
Claim 43
Dependent Claim
34 words
The method of optically recording information according to claim 31, wherein said thermally degradable polymer layer between said structural substrate and said light absorbing recording layer is at least about 500 angstroms in thickness.
Claim 44
Dependent Claim
33 words
The method of optically recording information according to claim 31, wherein said thermally degradable polymer layer between the light absorbing layer and the reflection layer is at least about 500 angstroms in thickness.
Claim 45
Dependent Claim
21 words
The method of optically recording information according to claim 31, wherein said thermally degradable polymer layers are nitrocellulose or polymethyl methacrylate.
Claim 46
Dependent Claim
16 words
The method of optically recording information according to claim 31, wherein said reflective layer is aluminum.
Claim 47
Dependent Claim
19 words
The method of optically recording information according to claim 31, further including a protective overcoating on said reflective layer.
Claim 48
Dependent Claim
27 words
The method of optically recording information according to claim 31, further including a preformatted information layer between said structural substrate and said first thermally degradable polymer layer.
References Cited (Backward Citations)
US3560994A
Cited
US3696344A
Cited
US3825233A
Cited
US4032691A
Cited
US3911444A
Cited
US4335198A
Cited
US4097895A
Cited
US4176277A
Cited
US4405862A
Cited
US4237468A
Cited
US4216501A
Cited
US4329697A
Cited
US4230939A
Cited
US4269137A
Cited
US4310614A
Cited
US4283777A
Cited
US4290122A
Cited
EP0024136A1
Cited
US4268840A
Cited
US4410581A
Cited
GB2061594A
Cited
US4285056A
Cited
US4404656A
Cited
US4360895A
Cited
US4371954A
Cited
US4340655A
Cited
US4379299A
Cited
EP0096504A1
Cited
WO1984002421A1
Cited
EP0199656A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-19 | 1990-07-21 | 1991-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-19 | 1994-07-21 | 1995-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-19 | 1998-07-21 | 1999-01-20 | $7700.00 | Window Closed / Lapsed |