Abstract
Abstract A process for preparing an iodine stainable polyester polarizer film which comprises: (a) extruding a moving molten web of polyester film; and (b) quenching said moving web to solidify it in a substantially amorphous form; and (c) applying an anchor coating to at least a portion of the surface of said film wherein said anchor coating improves adhesion of polyvinyl alcohol to polyester film; and (d) applying a coating of a dispersed aqueous composition of polyvinyl alcohol to at least a portion of the surface of said film; and (e) stretching said moving web in a direction transverse to the direction of motion while heating said web at a temperature of from about its glass transition temperature to about 160° C.; and (f) crystallizing said moving web by heating it to a temperature in the range of 130° C. to 240° C. without stretching said web; and (g) cooling said web to substantially ambient atmospheric temperature.
Inventors
- 👤 John H. Rogers
- 👤 Michael J. Hopper
- 👤 Michael R. Martin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 02:38
CPC Classifications
B; B29; B29D; B29D7/00; B29D7/01; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; B29K; B29K2995/00; B29K2995/0018; B29K2995/0034; C08J2367/00; C08J2367/02; C08J2429/00; C08J2429/02; C08J2429/04
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
231 words
A process for preparing an iodine stainable polyester film which consists of: (a) extruding a moving molten web of polyester film; and (b) quenching said moving beg to solidify it in a substantially amorphous form; and (c) applying an anchor coating to at least a portion of the surface of said film wherein said anchor coating promotes adhesion of polyvinyl alcohol to polyester film; and (d) applying a coating of a dispersed aqueous composition of polyvinyl alcohol to at least a portion of the surface of said film; and (e) stretching the moving web in a direction transverse to the direction of motion while heating said web at a temperature of from about its glass transition temperature to about 160° C.; and (f) crystallizing said moving web by heating it to a temperature in the range of 130° C. to 240° C. without stretching said web; and (g) cooling said web to substantially ambient atmospheric room temperature (h) subsequently passing said web through a staining bath containing iodine and one or more iodine salts; (i) subsequently passing said web through an aqueous stabilizing bath containing boric acid and borax, with the proviso that said polyvinyl alcohol be from 95 to 99 percent hydrolyzed and that the dry coating weight of said polyvinyl alcohol be from 1.0 to about 2.1 pound of coating per thousand square feet of film prior to stretching.
Claim 2
Dependent Claim
231 words
A process for preparing an iodine stainable polyester film which consists of: (a) extruding a moving molten web of polyester film; and (b) quenching said moving beg to solidify it in a substantially amorphous form; and (c) applying an anchor coating to at least a portion of the surface of said film wherein said anchor coating promotes adhesion of polyvinyl alcohol to polyester film; and (d) applying a coating of a dispersed aqueous composition of polyvinyl alcohol to at least a portion of the surface of said film; and (e) stretching the moving web in a direction transverse to the direction of motion while heating said web at a temperature of from about its glass transition temperature to about 160° C.; and (f) crystallizing said moving web by heating it to a temperature in the range of 130° C. to 240° C. without stretching said web; and (g) cooling said web to substantially ambient atmospheric room temperature (h) subsequently passing said web through a staining bath containing iodine and one or more iodine salts; (i) subsequently passing said web through an aqueous stabilizing bath containing boric acid and borax, with the proviso that said polyvinyl alcohol be from 95 to 99 percent hydrolyzed and that the dry coating weight of said polyvinyl alcohol be from 1.0 to about 2.1 pound of coating per thousand square feet of film prior to stretching.
Claim 3
Dependent Claim
12 words
The process of claim 1 wherein said polyester film comprises polyethylene terephthalate.
Claim 4
Dependent Claim
20 words
The process of claim 1 wherein the temperature in step (e) ranges from about 80° C. to about 110° C.
Claim 5
Dependent Claim
20 words
The process of claim 3 wherein the temperature in step (e) ranges from about 90° C. to about 100° C.
Claim 6
Dependent Claim
20 words
The process of claim 1 wherein the temperature of step (f) ranges from about 150° C. to about 180° C.
Claim 7
Dependent Claim
20 words
The process of claim 2 wherein said web is stretched from about 2 to about 6 times its original width.
Claim 8
Dependent Claim
20 words
The process of claim 6 wherein said web is stretched from about 2.5 to about 4.5 times its original width.
Claim 9
Dependent Claim
16 words
The process of claim 1 wherein step (f) is performed for about five seconds or more.
Claim 10
Dependent Claim
39 words
The process of claim 1 wherein said polyvinyl alcohol coating composition of step (d) comprises an aqueous solution of polyvinyl alcohol wherein said polyvinyl alcohol is present in an amount of from about 2% to about 25% by weight.
Claim 11
Dependent Claim
23 words
The process of claim 9 wherein said polyvinyl alcohol is present in an amount of from about 15% to about 20% by weight.
Claim 12
Dependent Claim
25 words
The process of claim 1 wherein said polyvinyl alcohol coating weight is about 1.5 dry pounds of coating per thousand square feet of unstretched film.
Claim 13
Dependent Claim
75 words
The process of claim 1 wherein said anchor coating of step (c) is produced by polycondensing (A) terephthalic acid; (B) an aliphatic dicarboxylic acid having the formula HOOC(CH 2 ) n COOH, n being an integer of from 1 to 11; (c) a sulfomonomer containing an alkali metal sulfonate group attached to a difunctional dicarboxylic aromatic nucleus; and (d) at least one aliphatic or cycloaliphatic alkylene glycol having from about 2 to 11 carbon atoms.
Claim 14
Dependent Claim
30 words
The process of claim 12 in said anchor coating comprises an aqueous solution wherein said coating is present in an amount of from about 3% to about 22% by weight.
Claim 15
Dependent Claim
18 words
The process of claim 13 wherein said coating is present in an amount of about 10% by weight.
Claim 16
Dependent Claim
34 words
The process of claim 12 wherein said anchor coating is present at a coating weight range of from about 0.025 to about 0.1 dry pounds of coating per thousand square feet of unstretched film.
Claim 17
Dependent Claim
27 words
The process of claim 15 wherein the coating weight of said anchor coating is about 0.05 dry pounds of coating per thousand square feet of unstretched film.
References Cited (Backward Citations)
US4268127A
Cited
JPS55117107A
Cited
JPS5633612A
Cited
JPS56158301A
Cited
US4388375A
Cited
US4396642A
Cited
JPS5898709A
Cited
EP0089493A1
Cited
US4476189A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |