US4663226A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fire retardant
Assignee: F R SYSTEMS Inc
•
Filing: 1986-07-25
•
Granted: 1987-05-05
•
Expires: 2006-07-25
Abstract
Abstract The present invention relates to coatings which provide fire resistance or fireproofing of an underlying product. In particular, the invention relates to a flexible coating which provides fire resistance by the formation of two stages of fire protection.
Inventors
- 👤 Lubomir Vajs
- 👤 Daniel M. Pettit
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:50
CPC Classifications
C; C09; C09K; C09K21/00; C09K21/14; C04; C04B; C04B26/00; C04B26/30; C04B26/32; C09D; C09D5/00; C09D5/18; C09D5/185; C04B2111/00; C04B2111/00474; C04B2111/00482; C04B2111/20; C04B2111/28; C04B2111/50; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/23; Y10T428/233; Y10T428/239; Y10T428/249921; Y10T428/249953; Y10T428/249954; Y10T428/26; Y10T428/269
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
121 words
A flexible coating applied to the surface of a product to provide a protective fireproof layer, said coating comprising; a base of an elastomeric material; a known carbon base intumescent material dispersed throughout the base which when exposed to heat of combustion foams and produces a protective cellular layer; and a vitrifying agent, dispersed throughout said coating which commences vitrification at a temperature substantially above the commencement of said cellular layer and prior to temperature decomposition of said foamed intumescent, said vitrifying agent stabilizing the carbon of said foamed intumescent when exposed to temperature which otherwise would cause decomposition of the cellular layer, said vitrifying agent increasing the effective maximum temperature of said intumescent foam layer by at least 100° C.
Claim 2
Dependent Claim
121 words
A flexible coating applied to the surface of a product to provide a protective fireproof layer, said coating comprising; a base of an elastomeric material; a known carbon base intumescent material dispersed throughout the base which when exposed to heat of combustion foams and produces a protective cellular layer; and a vitrifying agent, dispersed throughout said coating which commences vitrification at a temperature substantially above the commencement of said cellular layer and prior to temperature decomposition of said foamed intumescent, said vitrifying agent stabilizing the carbon of said foamed intumescent when exposed to temperature which otherwise would cause decomposition of the cellular layer, said vitrifying agent increasing the effective maximum temperature of said intumescent foam layer by at least 100° C.
Claim 3
Dependent Claim
21 words
A coating as claimed in claim 1, wherein said coating is of a thickness less than about 0.060 of an inch.
Claim 4
Dependent Claim
16 words
A coating as claimed in claim 1, wherein said elastomeric base is a water based elastomer.
Claim 5
Dependent Claim
18 words
A coating as claimed in claim 3, wherein said product is of a flexible and/or rigid foam shape.
Claim 6
Dependent Claim
20 words
A coating as claimed in claim 4, wherein at least a portion of said coating is reinforced with glass fibers.
Claim 7
Dependent Claim
35 words
A coating as claimed in claim 1, capable of protecting said product for at least 2 minutes when exposed to a temperature of about 1000° C., as said vitrifying agent is of a silicic base.
Claim 8
Dependent Claim
28 words
A coating as claimed in claim 6, wherein said vitrifying material is selected from the group consisting of hydrated magnesium silicate, silica powder, silicon resins, and nepheline syenite.
Claim 9
Dependent Claim
24 words
A coating as claimed in claim 6, wherein said vitrifying material and said elastomeric material are combined by using a silicone water based elastomer.
Claim 10
Dependent Claim
49 words
A coating as claimed in claim 4, wherein said coating comprises by weight 17 to 40 parts of diammonium phosphate, 17 to 27 parts of pentaerythritol, 7 to 27 parts of dicyandiamide, 45 to 75 parts of water based elastomer, and 5 to 50 parts of said vitrifying material.
Claim 11
Dependent Claim
37 words
A coating as claimed in claim 9, wherein said vitrifying material is selected from or a suitable mixture of, the following materials, silica powder nepheline syenite powder, sodium tetraborate, hydrated magnesium silicate, aluminium silicate and silicon resins.
Claim 12
Dependent Claim
45 words
A coating as claimed in claim 4, comprising; 17 to 40 parts by weight of ammonium polyphosphate, 17 to 27 parts by weight of pentaerythritol, 7 to 27 parts by weight of dicyandiamide, and 45 to 75 parts by weight of silicone water based elastomer.
Claim 13
Dependent Claim
54 words
A coating as claimed in claim 6 comprising; 17 to 40 parts by weight of diammonium phosphate, 17 to 27 parts by weight of pentaerythritol, 7 to 27 parts by weight of dicyandiamide, 45 to 75 parts by weight of water based elastomer, 5 to 50 parts by weight of a silicate vitrifying agent.
Claim 14
Dependent Claim
73 words
A coating as claimed in claim 4, comprising; 17 to 40 parts by weight of ammonium polyphosphate, 17to 27 parts by weight of pentaerythritol, 7 to 27 parts by weight of dicyandiamide, 45 to 75 parts by weight of water based elastomer, and 5 to 50 parts by weight or vitrification agent selected from the group consisting of silica powder, nepheline syenite powder, sodium tetraborate, hydrated magnesium silicate, aluminium silicate and silicone resins.
Claim 15
Dependent Claim
44 words
A coating as claimed in claim 6 comprising; 17 to 40 parts by weight of diammonium phosphate, 17 to 27 parts by weight of pentaerithritol, 7 to 27 parts by weight of disyandiamide, 45 to 55 parts by weight of silicone water based elastomer.
Claim 16
Independent Claim
147 words
A method of treating a preshaped rigid and/or flexible shape comprising; applying a coating containing a base of elastomer material, a known carbon based intumescent foaming material dispersed throughout the base material, and a known vitrifying material suitable for a fire protection layer when vitrified, said vitrifying material being dispersed throughout the coating, said intumescent when exposed to a temperature of about 200° C. producing a cellular foam layer which provides a first stage of fire protection for the foam shape, said vitrifying material vitrifying after substantial formation of said cellular layer resulting in said layer and said vitrifying agent forming a stable insulating layer which protects said rigid and/or flexible foam shape to a temperature substantially greater than said foam layer alone; said coating being applied to said form shape to at least essentially encapsulate the same while still retaining the resiliency of the foam shape.
Claim 17
Independent Claim
147 words
A method of treating a preshaped rigid and/or flexible shape comprising; applying a coating containing a base of elastomer material, a known carbon based intumescent foaming material dispersed throughout the base material, and a known vitrifying material suitable for a fire protection layer when vitrified, said vitrifying material being dispersed throughout the coating, said intumescent when exposed to a temperature of about 200° C. producing a cellular foam layer which provides a first stage of fire protection for the foam shape, said vitrifying material vitrifying after substantial formation of said cellular layer resulting in said layer and said vitrifying agent forming a stable insulating layer which protects said rigid and/or flexible foam shape to a temperature substantially greater than said foam layer alone; said coating being applied to said form shape to at least essentially encapsulate the same while still retaining the resiliency of the foam shape.
Claim 18
Dependent Claim
19 words
A method as claimed in claim 15, wherein components of said coating are combined during application of said coating.
Claim 19
Dependent Claim
23 words
A method as claimed in claim 16, wherein said coating is sprayed on said cushion and said components are combined in the spray.
Claim 20
Dependent Claim
24 words
A method as claimed in claim 16, including applying reinforcing glass fibers to selected portions of said cushion which are retained in said coating.
Claim 21
Dependent Claim
24 words
A method as claimed in claim 16, wherein said coating is applied to achieve a thickness of at least about 0.010 of an inch.
Claim 22
Dependent Claim
33 words
A method as claimed in claim 16, wherein said coating is mixed with a colour pigment and the thickness of the coating is approximated by comparing the coating colour with predetermined colour standards.
Claim 23
Dependent Claim
18 words
A method as claimed in claim 16, wherein said vitrifying material starts to vitrify at about 600° C.
Claim 24
Dependent Claim
124 words
A coating applied to the surface of a low temperature combustible product to provide a fireproof protective layer capable of withstanding temperatures up to a predetermined minimum temperature, said coating comprising; an intumescent material which when exposed to the heat of combustion produces a cellular foam layer which provides a first stage of fire protection of the product, and a vitrifying agent of the type recognized as providing fire protection which vitrifies after formation of the intumescent cellular foam layer and before decomposition of said layer to thereby protect both the intumescent cellular foam layer and the product from temperatures greater than said intumescent cellular foam layer alone could withstand; said intumescent material and said vitrifying agent being combined in a suitable elastomeric base.
Claim 25
Dependent Claim
124 words
A coating applied to the surface of a low temperature combustible product to provide a fireproof protective layer capable of withstanding temperatures up to a predetermined minimum temperature, said coating comprising; an intumescent material which when exposed to the heat of combustion produces a cellular foam layer which provides a first stage of fire protection of the product, and a vitrifying agent of the type recognized as providing fire protection which vitrifies after formation of the intumescent cellular foam layer and before decomposition of said layer to thereby protect both the intumescent cellular foam layer and the product from temperatures greater than said intumescent cellular foam layer alone could withstand; said intumescent material and said vitrifying agent being combined in a suitable elastomeric base.
Claim 26
Dependent Claim
21 words
A coating as claimed in claim 22, wherein said coating is of a thickness less than about 0.060 of an inch.
Claim 27
Dependent Claim
21 words
A coating as claimed in claim 22, wherein said intumescent and said vitrifying agent are combined in a water based elastomer.
Claim 28
Dependent Claim
18 words
A coating as claimed in claim 24, wherein said product is of a rigid and/or flexible foam shape.
Claim 29
Dependent Claim
24 words
A coating as claimed in claim 25, wherein at least a portion of said coating is reinforced with glass fibers embedded in said coating.
Claim 30
Dependent Claim
38 words
A coating as claimed in claim 25, wherein said vitrifying agent is of a silicic base rendering the coating capable of protecting said product for at least 2 minutes when exposed to a temperature of about 1034° C.
Claim 31
Dependent Claim
28 words
A coating as claimed in claim 27, wherein said vitrifying material is selected from the group consisting of hydrated magnesium silicate, silica powder, silicon resins, and nepheline syenite.
Claim 32
Dependent Claim
24 words
A coating as claimed in claim 27, wherein said vitrifying material and said elastomeric material are combined by using a silicone water based elastomer.
Claim 33
Dependent Claim
49 words
A coating as claimed in claim 22, wherein said coating comprises by weight 17 to 40 parts of ammonium polyphosphate, 17 to 27 parts of pentaerythritol, 7 to 27 parts of dicyandiamide, 45 to 75 parts of water based elastomer, and 5 to 50 parts of said vitrifying material.
Claim 34
Dependent Claim
37 words
A coating as claimed in claim 30, wherein said vitrifying material is selected from or a suitable mixture of the following materials, silica powder, nepheline syenite powder, sodium tetraborate, hydrated magnesium silicate, aluminium silicate and silicon resins.
Claim 35
Dependent Claim
45 words
A coating as claimed in claim 27, comprising; 17 to 40 parts by weight of ammonium polyphosphate, 17 to 27 parts by weight of pentaerythritol, 7 to 27 parts by weight of dicyandiamide, and 45 to 75 parts by weight of silicone water base elastomer.
Claim 36
Dependent Claim
55 words
A coating as claimed in claim 27, comprising; 17 to 40 parts by weight of diammonium phosphate, 17 to 27 parts by weight of pentaerythritol, 7 to 27 parts by weight of dicyandiamide, and 45 to 75 parts by weight of water based elastomer, and 5 to 50 parts by weight of a vitrifying agent.
Claim 37
Dependent Claim
72 words
A coating as claimed in claim 22, comprising; 17 to 40 parts by weight of ammonium polyphosphate, 17 to 27 parts by weight of pentaerythritol, 7to 27 parts by weight of dicayndiamide, 45 to 75 parts by weight of water based elastomer, 5 to 50 parts by weight of vitrification agent selected from the group consisting of silica powder, nepheline syenite powder, sodium tetraborate, hydrated magnesium silicate, aluminium silicate and silicone resins.
Claim 38
Independent Claim
82 words
A method of forming a two stage fire protective coating applied to a product comprising; forming an initial intumescent cellular foam layer on a product when first exposed to heat in excess of about 200° C., and thereafter vitrifying an agent throughout said foam layer at a temperature less than the temperature at which said layer decomposes, said agent stabilizing carbon of said intumescent to thereby protect a coated product at elevated temperatures at which the intumescent layer alone is not capable.
Claim 39
Independent Claim
82 words
A method of forming a two stage fire protective coating applied to a product comprising; forming an initial intumescent cellular foam layer on a product when first exposed to heat in excess of about 200° C., and thereafter vitrifying an agent throughout said foam layer at a temperature less than the temperature at which said layer decomposes, said agent stabilizing carbon of said intumescent to thereby protect a coated product at elevated temperatures at which the intumescent layer alone is not capable.
Claim 40
Dependent Claim
68 words
A fireproofing compound comprising: a carrier of an elastomeric material; a known carbon base intumescent material which when exposed to heat of combustion produces a protective cellular foam layer; and a vitrifying agent which stabilizes the carbon of the intumescent when exposed to a temperature which would otherwise cause decomposition of the foamed intumescent, said vitrifying agent stabilizing the carbon of the intumescent by vitrifying and combining therewith.
Claim 41
Dependent Claim
68 words
A fireproofing compound comprising: a carrier of an elastomeric material; a known carbon base intumescent material which when exposed to heat of combustion produces a protective cellular foam layer; and a vitrifying agent which stabilizes the carbon of the intumescent when exposed to a temperature which would otherwise cause decomposition of the foamed intumescent, said vitrifying agent stabilizing the carbon of the intumescent by vitrifying and combining therewith.
Claim 42
Dependent Claim
38 words
A fireproofing compound as claimed in claim 36, wherein said carrier is of a water based neoprene or silicone and said compound includes a suitable buffer to avoid PH shock of the carrier when combined with the intumescent.
References Cited (Backward Citations)
GB1598197A
Cited
US4265963A
Cited
GB2052305A
Cited
US4324835A
Cited
US4530877A
Cited
EP0096489A1
Cited
US4594368A
Cited
GB2130122A
Cited
US4529467A
Cited
US4572862A
Cited
US4588523A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-04 | 1990-11-03 | 1991-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-04 | 1994-11-03 | 1995-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-04 | 1998-11-03 | 1999-05-05 | $7700.00 | Window Closed / Lapsed |