Material for sliding surface bearings
Assignee: Kolbenschmidt AG
•
Filing: 1986-02-14
•
Granted: 1987-05-19
•
Expires: 2006-02-14
Abstract
Abstract A material which is intended for use in sliding surface bearings comprises a metallic backing, a porous metallic substrate layer applied to said backing, and a PTFE-filler mixture, which completely fills the pores of the substrate layer and constitutes an antifriction layer. The bond strength between the antifriction layer and the substrate layer is improved by coating that surface of the substrate layer which faces the antifriction layer with a primer.
Inventors
- 👤 Wolfgang Bickle
- 👤 Jurgen Braus
- 👤 Hans-Paul Baureis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:38
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/20; F16C33/203; F16C33/206; F16C33/208; F16C2208/00; F16C2208/02; F16C2208/20; F16C2208/30; F16C2208/32; F16C2220/00; F16C2220/20; F16C2220/40; F16C2220/44; F16C2226/00; F16C2226/30; F16C2226/40; F16C2240/00; F16C2240/40; F16C2240/48; Y; Y10; Y10S; Y10S384/00; Y10S384/90; Y10S384/908; Y10S384/912; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12042; Y10T428/12049; Y10T428/12493; Y10T428/12535; Y10T428/12556; Y10T428/12569; Y10T428/12736; Y10T428/1275; Y10T428/12757; Y10T428/12771; Y10T428/12861; Y10T428/12903; Y10T428/12917; Y10T428/12924; Y10T428/12951; Y10T428/12986
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
165 words
In a material for sliding surface bearings, where in the material comprises a metallic backing having a thickness of 0.5 to 2.5 mm and consisting of one of steel, bronze and a high-strength aluminum alloy, a porous substrate layer applied to the backing and having a thickness of 0.2 to 0.4 mm and consisting of one of tin bronze, tin-lead bronze and an aluminum bearing alloy, a mixture of polytetrafluoroethylene (PTFE) and 15 to 25% by volume of a filler for improving the thermal conductivity and wear resistance and completely filling the pores of said substrate layer, and an antifriction layer having a thickness of 0.01 to 0.03 mm and consisting of the PTFE-filler mixture and provided on said substrate layer, the improvement wherein: the surface of the substrate layer which faces the antifriction layer is coated with a primer layer in a thickness of 2 to 10 μm to improve the bond between the antifriction layer and the substrate layer while reducing the wear.
Claim 2
Dependent Claim
165 words
In a material for sliding surface bearings, where in the material comprises a metallic backing having a thickness of 0.5 to 2.5 mm and consisting of one of steel, bronze and a high-strength aluminum alloy, a porous substrate layer applied to the backing and having a thickness of 0.2 to 0.4 mm and consisting of one of tin bronze, tin-lead bronze and an aluminum bearing alloy, a mixture of polytetrafluoroethylene (PTFE) and 15 to 25% by volume of a filler for improving the thermal conductivity and wear resistance and completely filling the pores of said substrate layer, and an antifriction layer having a thickness of 0.01 to 0.03 mm and consisting of the PTFE-filler mixture and provided on said substrate layer, the improvement wherein: the surface of the substrate layer which faces the antifriction layer is coated with a primer layer in a thickness of 2 to 10 μm to improve the bond between the antifriction layer and the substrate layer while reducing the wear.
Claim 3
Dependent Claim
23 words
The material for sliding surface bearings according to claim 1, wherein the primer layer consists of chromium phosphate and of embedded polytetrafluoroethylene particles.
Claim 4
Dependent Claim
103 words
A process of manufacturing a material for sliding surface bearings, comprising: applying a porous metallic substrate layer to a metallic backing by one of sintering of a metallic powder having a particle size of 80 to 200 μm at a temperature of 800° to 850 ° C. or by plasma coating, immediately thereafter applying a mixture consisting of 90 to 110 parts polytetrafluoroethylene dispersion, 10 to 30 parts chromium phosphate and 20 to 50 parts distilled water to the substrate layer and drying same at 265° to 300° C., and applying a PTFE-filler mixture by rolling and sintering at 390° to 410° C.
Claim 5
Dependent Claim
103 words
A process of manufacturing a material for sliding surface bearings, comprising: applying a porous metallic substrate layer to a metallic backing by one of sintering of a metallic powder having a particle size of 80 to 200 μm at a temperature of 800° to 850 ° C. or by plasma coating, immediately thereafter applying a mixture consisting of 90 to 110 parts polytetrafluoroethylene dispersion, 10 to 30 parts chromium phosphate and 20 to 50 parts distilled water to the substrate layer and drying same at 265° to 300° C., and applying a PTFE-filler mixture by rolling and sintering at 390° to 410° C.
References Cited (Backward Citations)
US3883314A
Cited
US4000982A
Cited
US4200541A
Cited
US4208472A
Cited
US4268467A
Cited
US4439484A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-18 | 1990-11-17 | 1991-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-18 | 1994-11-17 | 1995-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-18 | 1998-11-17 | 1999-05-19 | $7700.00 | Window Closed / Lapsed |