Metal product fabrication
Assignee: United Kingdom Atomic Energy Authority
•
Filing: 1986-03-25
•
Granted: 1987-06-23
•
Expires: 2006-03-25
Abstract
Abstract A metal matrix composite (e.g. of SiC in a metal alloy) is made by the steps of atomizing a stream of molten metal to form a spray of hot metal particles by subjecting the stream to relatively cold gas directed at the stream, applying to the stream or spray relatively cold solid particles of a material of different composition from the metal, and depositing the metal having the particles incorporated therein. The deposit is made into a shaped metal matrix composite by reheating it to a controlled temperature substantially above the liquidus of the metal at which it flows under pressure and casting the fluid deposit to give the shaped product.
Inventors
- 👤 Eric A. Feest
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:23
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/10; C22C1/1036; C22C1/1042; B; B22; B22D; B22D23/00; B22D23/003; C23; C23C; C23C4/00; C23C4/12; C23C4/123; B22F; B22F2998/00
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
97 words
A method of making a shaped metal matrix composite product comprising the steps of atomising a stream of molten metal to form a spray of hot metal particles by subjecting the stream to relatively cold gas directed at the stream, applying to the stream or spray solid non-metallic particles depositing the metal having said particles incorporated therein, reheating the deposit to a temperature above the solidus of the metal, the temperature being such that the deposit possesses sufficient fluidity for it to be gravity or pressure cast, and casting the fluid deposit to give a shaped product.
Claim 2
Independent Claim
97 words
A method of making a shaped metal matrix composite product comprising the steps of atomising a stream of molten metal to form a spray of hot metal particles by subjecting the stream to relatively cold gas directed at the stream, applying to the stream or spray solid non-metallic particles depositing the metal having said particles incorporated therein, reheating the deposit to a temperature above the solidus of the metal, the temperature being such that the deposit possesses sufficient fluidity for it to be gravity or pressure cast, and casting the fluid deposit to give a shaped product.
Claim 3
Dependent Claim
16 words
A method according to claim 1 wherein the temperature is above the liquidus of the metal.
Claim 4
Dependent Claim
28 words
A method according to claim 1 wherein the metal is aluminium, an aluminium base alloy, a steel, a nickel base alloy, cobalt, copper or a titanium base alloy.
Claim 5
Dependent Claim
22 words
A method according to claim 1 wherein the composite product has from 0.5% to 50% by volume of particles uniformly dispersed therein.
Claim 6
Dependent Claim
22 words
A method according to claim 4 wherein the composite product has from 10% to 30% by volume of particles uniformly dispersed therein.
Claim 7
Dependent Claim
17 words
A method according to claim 1 wherein the size of the particles is less than 20 micrometers.
Claim 8
Dependent Claim
11 words
A method according to claim 1 wherein the particles are non-metallic.
Claim 9
Dependent Claim
16 words
A method according to claim 7 wherein the particles are of silicon carbide or of alumina.
Claim 10
Dependent Claim
30 words
A method according to claim 8 wherein the particles are of silicon carbide having a particle size of less than 10 micrometers and the metal is an aluminium base alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-22 | 1990-12-22 | 1991-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-22 | 1994-12-22 | 1995-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-22 | 1998-12-22 | 1999-06-23 | $7700.00 | Window Closed / Lapsed |