Process for preparing copolymers and use of the products obtained

Claim 2

A process for preparing copolymers which comprises copolymerizing in a radical bulk polymerization the following components: (A) between 10 and 60 parts by weight of at least one diester of an α,β-olefinically unsaturated dicarboxylic acid with a monohydric alcohol having 1 to 8 carbon atoms in each ester group, (B) between 10 and 70 parts by weight of at least one vinyl derivative of a monocyclic aromatic hydrocarbon having but one vinyl group, in which any alkyl groups optionally in α-position or attached to the aromatic ring system have from 1 to 3 carbon atoms; (C) between 0 and 30 parts by weight of at least one glycidyl ester of an aliphatic saturated monocarboxylic acid being branched in α-position, the acid having from 9 to 11 carbon atoms, (D) between 0 and less than 51 parts by weight of at least one ester or amide of at least one α,β-olefinically unsaturated monocarboxylic acid or an anhydride of at least one α,β-olefinically unsaturated dicarboxylic acid, (E) between 0 and 40 parts by weight of at least one α,β-olefinically unsaturated monocarboxylic acid, wherein at least one of Components (D) and (E) is present, the total amount of Components (A) to (E) is 100 parts by weight, the polymerization is effected by introducing at first at least one part of Component A into the reaction vessel alone or in combination with at least a part of Component (C), heating the contents of the vessel to a temperature in the range between 140° and 200° C. and then copolymerizing by gradually adding a mixture of Component (B) with at least one of Components (D) and (E) or a combination of said mixture with remaining parts, if any, of Component A or of Components (C) and (A) or a combination of said mixture with the whole part of Component (C) into said vessel together with a radical initiator alone or in combination with a molecular weight regulator and wherein, if Component (C) is present, an at least equimolar amount, referred to Component (C), of Component (E) is added.

Claim 3

A process as claimed in claim 1 wherein component (A) is reacted in the form of a dialkylester of maleic or fumaric acid or of both, said ester having between 1 and 8 carbon atoms in each ester group.

Claim 4

A process as claimed in claim 1 wherein the initiator is present in a total amount between 0.5 and 2.5 percent by weight, referred to the total weight of the starting components.

Claim 5

A process as claimed in claim 1 wherein Component (D) is reacted in the form of at least one compound selected from the group consisting of an acrylic or methacrylic ester of a monohydric alcohol having between 1 and 12 carbon atoms, an acrylic or methacrylic ester of a polyhydric alcohol having between 2 and 10 carbon atoms, a glycidyl acrylate, a glycidyl methacrylate and an addition product of an α,β-olefinically unsaturated carboxylic acid with a monoglycidyl ester or monoglycidyl ether or both.

Claim 6

A process as claimed in claim 1 wherein a copolymer is prepared by copolymerizing an amount of at least 5% by weight of Component (E) which is then at least partially neutralized with at least one nitrogen compound selected from the group consisting of ammonia and amine.

Claim 7

A process as claimed in claim 1 wherein a Component (D) is used which contains hydroxy groups.

Claim 8

A process as claimed in claim 6 wherein the hydroxy groups are derived from the use of a Component (D) containing hydroxy alkyl groups or unsaturated glycidyl esters.

Claim 9

A process as claimed in claim 1 wherein a Component (C) or (D) is used which contains glycidyl groups.

Claim 10

A process for preparing copolymers which comprises copolymerizing in a radical bulk polymerization the following components: (A) between 10 and 30 parts by weight of at least one diester of an α,β-olefinically unsaturated dicarboxylic acid with a monohydric alcohol having 1 to 8 carbon atoms in each ester group, (B) between 35 and 60 parts by weight of at least one vinyl derivatives of a monocyclic aromatic hydrocarbon having but one vinyl group, in which any alkyl groups optionally in α-position or attached to the aromatic ring system having from 1 to 3 carbon atoms, (C) between 0 and 30 parts by weight of at least one glycidyl ester of an aliphatic saturated monocarboxylic acid being branched in α-postiion, the acid having from 9 to 11 carbon atoms, (D) between 0 and less than 51 parts by weight of at least one ester or amide of at least one α,β-olefinically unsaturated monocarboxylic acid or an anhydride of at least one α,β-olefinically unsaturated dicarboxylic acid, (E) between 0 and 40 parts by weight of at least one α,β-olefinically unsaturated monocarboxylic acid wherein at least one of Components (D) and (E) is present, the total amount of Components (A) to (E) is 100 parts by weight, the copolymerization is effected by first introducing at least one part of Component (A) into the reaction vessel alone or in combination with at least a part of Component (C), heating the contents of the vessel to a temperature in the range between 140° and 200° C. and then copolymerizing by gradually adding a mixture of Component (B) with at least one of Components (D) and (E) or a combination of said mixture with remaining parts if any, of Component (A) or Components (A) and (C) or a combination of said mixture with the whole part of Component (C) into said vessel together with a radical initiator alone or in combination with a molecular weight regulator and wherein, if Component (C) is present, an at least equimolar amount, referred to Component (C), of Component (E) is added.

Claim 11

A process for preparing copolymers which comprises copolymerizing in a radical bulk polymerization the following components: (A) between 10 and 30 parts by weight of at least one diester of an α,β-olefinically unsaturated dicarboxylic acid with a monohydric alcohol having 1 to 8 carbon atoms in each ester group, (B) between 35 and 60 parts by weight of at least one vinyl derivatives of a monocyclic aromatic hydrocarbon having but one vinyl group, in which any alkyl groups optionally in α-position or attached to the aromatic ring system having from 1 to 3 carbon atoms, (C) between 0 and 30 parts by weight of at least one glycidyl ester of an aliphatic saturated monocarboxylic acid being branched in α-postiion, the acid having from 9 to 11 carbon atoms, (D) between 0 and less than 51 parts by weight of at least one ester or amide of at least one α,β-olefinically unsaturated monocarboxylic acid or an anhydride of at least one α,β-olefinically unsaturated dicarboxylic acid, (E) between 0 and 40 parts by weight of at least one α,β-olefinically unsaturated monocarboxylic acid wherein at least one of Components (D) and (E) is present, the total amount of Components (A) to (E) is 100 parts by weight, the copolymerization is effected by first introducing at least one part of Component (A) into the reaction vessel alone or in combination with at least a part of Component (C), heating the contents of the vessel to a temperature in the range between 140° and 200° C. and then copolymerizing by gradually adding a mixture of Component (B) with at least one of Components (D) and (E) or a combination of said mixture with remaining parts if any, of Component (A) or Components (A) and (C) or a combination of said mixture with the whole part of Component (C) into said vessel together with a radical initiator alone or in combination with a molecular weight regulator and wherein, if Component (C) is present, an at least equimolar amount, referred to Component (C), of Component (E) is added.

Claim 12

A process for preparing copolymers which comprises copolymerization in a radical bulk polymerization the following components consisting essentially of: (A) between 10 and 60 parts by weight of at least one diester of an α,β-olefinically unsaturated dicarboxylic acid with a monohydric alcohol having 1 to 8 carbon atoms in each ester group, (B) between 10 and 70 parts by weight of at least one vinyl-derivative of a monocyclic aromatic hydrocarbon having but one vinyl group, in which any alkyl groups optionally in α-position or attached to the aromatic ring system have from 1 to 3 carbon atoms, (C) between 0 and 30 parts by weight of at least one glycidyl ester of an aliphatic saturated monocarboxylic acid being branched in α-position, the acid having from 9 to 11 carbon atoms, (D) between 0 and less than 51 parts by weight of at least one ester or amide of at least one, -olefinically unsaturated monocarboxylic acid or an anhydride of at least one, -olefinically unsaturated dicarboxylic acid, (E) between 0 and 40 parts by weight of at least one, -olefinically unsaturated monocarboxylic acid, wherein at least one of Components (D) and (E) is present, the total amount of Components (A) to (E) is 100 parts by weight and Component (A) is at first introduced into the reaction vessel alone or in combination with at least a part of Component (C), heating the contents of the vessel to a temperature in the range between 140° and 200° C. and then copolymerizing by gradually adding a mixture of Component (B) with at least one of Components (D) and (E) or a combination of said mixture with remaining parts of Components (C) in the portions referred to above into said vessel together with a radial initiator alone or in combination with a molecular weight regulator and wherein, if Component (C) is present, an at least equimolar amount, referred to Component (C), of Component (E) is added.

Claim 13

A process for preparing copolymers which comprises copolymerization in a radical bulk polymerization the following components consisting essentially of: (A) between 10 and 60 parts by weight of at least one diester of an α,β-olefinically unsaturated dicarboxylic acid with a monohydric alcohol having 1 to 8 carbon atoms in each ester group, (B) between 10 and 70 parts by weight of at least one vinyl-derivative of a monocyclic aromatic hydrocarbon having but one vinyl group, in which any alkyl groups optionally in α-position or attached to the aromatic ring system have from 1 to 3 carbon atoms, (C) between 0 and 30 parts by weight of at least one glycidyl ester of an aliphatic saturated monocarboxylic acid being branched in α-position, the acid having from 9 to 11 carbon atoms, (D) between 0 and less than 51 parts by weight of at least one ester or amide of at least one, -olefinically unsaturated monocarboxylic acid or an anhydride of at least one, -olefinically unsaturated dicarboxylic acid, (E) between 0 and 40 parts by weight of at least one, -olefinically unsaturated monocarboxylic acid, wherein at least one of Components (D) and (E) is present, the total amount of Components (A) to (E) is 100 parts by weight and Component (A) is at first introduced into the reaction vessel alone or in combination with at least a part of Component (C), heating the contents of the vessel to a temperature in the range between 140° and 200° C. and then copolymerizing by gradually adding a mixture of Component (B) with at least one of Components (D) and (E) or a combination of said mixture with remaining parts of Components (C) in the portions referred to above into said vessel together with a radial initiator alone or in combination with a molecular weight regulator and wherein, if Component (C) is present, an at least equimolar amount, referred to Component (C), of Component (E) is added.

Claim 14

A process as claimed in claim 1 wherein the amount of component (B), referred to the sum of components (B), (D) and (E), is up to 73.1 percent by weight.

Claim 15

A process as claimed in claim 1, wherein the component (C) is used in an amount of from 5 to 15 parts by weight.

Claim 16

A process as claimed in claim 1, wherein the reaction is carried out without using a molecular weight regulator.