Lightly crosslinked linear olefinic polymer foams and process for making

Claim 2

A process for preparing a lightly crosslinked linear olefin polymer foam material having a substantially closed-cell structure, comprising the steps of: (a) melt processing under pressure a linear olefin polymer or blend of linear olefin polymers, (b) mixing a volatile blowing agent and a sufficient amount of one crosslinking agent selected from the group consisting of azido functional silanes. multifunctional vinyl monomers, and oxygen, together with said linear olefin polymer or blend of linear olefin polymers to form a flowable admixture, and, (c) extruding said admixture through a die to a zone of lower pressure and activating said blowing agent to expand said linear olefin polymer or blend of linear olefin polymers to a closed-cell structure crosslinked with itself to form said lightly crosslinked foam material.

Claim 3

The process of claim 1 in which said linear olefin polymer is linear low density polyethylene.

Claim 4

The process of claim 1 in which said linear olefin polymer is high density polyethylene.

Claim 5

The process of claim 1 in which said linear olefin polymer is polypropylene.

Claim 6

The process of claim 1 in which said linear olefin polymer is polystyrene.

Claim 7

The process of claim 1 in which the pressure at said die is at least 400 psig.

Claim 8

The process of claim 1 in which said crosslinking agent is 2-(trimethoxysilyl ethyl phenyl sulfonyl) azide, and a catalyst which catalyzes the condensation of silanols is added with the crosslinking agent.

Claim 9

The process of claim 1 in which said crosslinking agent is trimethylolpropane triacrylate.

Claim 10

A process for preparing a lightly crosslinked linear olefin polymer foam material having a substantially closed-cell structure, comprising the steps of: (a) melt process under pressure a linear olefin polymer or blend of linear olefin polymers together with a volatile blowing agent to form a flowable admixture, (b) introducing an amount of crosslinking agent sufficient to initiate crosslinking of said linear olefin polymer or blend and increase the pressure of said admixture to at least 400 psig, said crosslinking agent consisting of one of azido functional silanes, multifunctional vinyl monomers, or oxygen, and (c) extruding said admixture through a die to a zone of lower pressure and activating said blowing agent to expand said linear olefin polymer or blend to a substantially closed-cell structure crosslinked with itself to form said lightly crosslinked foam material.

Claim 11

A process for preparing a lightly crosslinked linear olefin polymer foam material having a substantially closed-cell structure, comprising the steps of: (a) melt process under pressure a linear olefin polymer or blend of linear olefin polymers together with a volatile blowing agent to form a flowable admixture, (b) introducing an amount of crosslinking agent sufficient to initiate crosslinking of said linear olefin polymer or blend and increase the pressure of said admixture to at least 400 psig, said crosslinking agent consisting of one of azido functional silanes, multifunctional vinyl monomers, or oxygen, and (c) extruding said admixture through a die to a zone of lower pressure and activating said blowing agent to expand said linear olefin polymer or blend to a substantially closed-cell structure crosslinked with itself to form said lightly crosslinked foam material.

Claim 12

The process of claim 9 in which said crosslinking agent is from 0.01 to 2.0 pph of an azido functional silane, and a catalyst which catalyzes the condensation of silanols is added.

Claim 13

The process of claim 9 in which said crosslinking agent is from 0.01 to 2.0 pph of a multifunctional vinyl monomer.

Claim 14

A process for preparing a lightly crosslinked linear olefin polymer foam material having a substantially closed-cell structure comprising the steps of: (a) melt processing under pressure a linear olefin polymer or blend of linear olefin polymers, (b) mixing a volatile blowing agent and a sufficient amount of a crosslinking agent selected from the group consisting of azido functional silanes, multifunctional vinyl monomers, oxygen, and mixtures thereof, together with said linear olefin polymer or blend of linear olefin polymers to form a flowable admixture, and, (c) extruding said admixtures through a die to a zone of lower pressure and activating said blowing agent to expand said linear olefin polymer or blend of linear olefin polymers to a substantially closed-cell structure crosslinked with itself to form said lightly crosslinked foam material.

Claim 15

A process for preparing a lightly crosslinked linear olefin polymer foam material having a substantially closed-cell structure comprising the steps of: (a) melt processing under pressure a linear olefin polymer or blend of linear olefin polymers, (b) mixing a volatile blowing agent and a sufficient amount of a crosslinking agent selected from the group consisting of azido functional silanes, multifunctional vinyl monomers, oxygen, and mixtures thereof, together with said linear olefin polymer or blend of linear olefin polymers to form a flowable admixture, and, (c) extruding said admixtures through a die to a zone of lower pressure and activating said blowing agent to expand said linear olefin polymer or blend of linear olefin polymers to a substantially closed-cell structure crosslinked with itself to form said lightly crosslinked foam material.