US4720366A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing fiber reinforced thermoplastic material
Assignee: Fiberite Inc
•
Filing: 1986-05-16
•
Granted: 1988-01-19
•
Expires: 2006-05-16
Abstract
Abstract A fiber reinforced material is made by passing a preheated tensioned filament array over an arcuate extruder head where thermoplastic polymer is flowed through the filament array to expel air from the array while coating the filaments with polymer. The filaments comprise 50 to 75 percent by volume of the material and the polymer has a relative viscosity of at least 50.
Inventors
- 👤 Edwin K. Binnersley
- 👤 William H. Krueger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 03:21
CPC Classifications
B; B29; B29B; B29B15/00; B29B15/08; B29B15/10; B29B15/12; B29B15/122; B29C; B29C48/00; B29C48/03; B29C48/05; B29C48/07; B29C48/08; B29C48/15; B29C48/156; B29K; B29K2077/00; B29K2105/00; B29K2105/0094; B29K2707/00; B29K2707/04; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/249942; Y10T428/249947
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
128 words
A method of making a fiber reinforced thermoplastic material comprising: advancing a tensioned array of fiber bundles comprised of continuous filaments in sliding contact with an arcuate surface of a heated extruder head; moving a molten thermoplastic polymer having a relative viscosity of at least 50 in a flow under pressure from one side to the other through the tensioned array of filaments from a slot in the arcuate surface of the extruder head, said slot being tranverse to said one side of the filament array said filaments having a melting point that exceeds the temperature of said molten thermoplastic polymer; expelling air from the other side of said filament array by means of said flow; and forming polymeric protrusions on said other side of said filament array.
Claim 2
Independent Claim
128 words
A method of making a fiber reinforced thermoplastic material comprising: advancing a tensioned array of fiber bundles comprised of continuous filaments in sliding contact with an arcuate surface of a heated extruder head; moving a molten thermoplastic polymer having a relative viscosity of at least 50 in a flow under pressure from one side to the other through the tensioned array of filaments from a slot in the arcuate surface of the extruder head, said slot being tranverse to said one side of the filament array said filaments having a melting point that exceeds the temperature of said molten thermoplastic polymer; expelling air from the other side of said filament array by means of said flow; and forming polymeric protrusions on said other side of said filament array.
Claim 3
Dependent Claim
20 words
The method of claim 1, including the step of spreading said protrusions uniformly along said other side of said array.
Claim 4
Dependent Claim
27 words
The method of claim 1 or claim 2 wherein the filament array is preheated to a temperature below its melting point prior to contacting said extruder head.
Claim 5
Dependent Claim
27 words
The method of claim 1, including the step of twisting said material while hot to modify the cross section of said material and redistribute the thermoplastic material.
Claim 6
Dependent Claim
17 words
The method of claim 4 wherein said cross-section is modified to a round or an oval form.
References Cited (Backward Citations)
US4640861A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-18 | 1991-07-20 | 1992-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-18 | 1995-07-20 | 1996-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-18 | 1999-07-20 | 2000-01-19 | $7700.00 | Window Closed / Lapsed |