Coatings which are abrasion resistant
Assignee: Aerojet Rocketdyne Holdings Inc
•
Filing: 1987-03-05
•
Granted: 1988-01-19
•
Expires: 2007-03-05
Abstract
Abstract Thermoplastic polymers or resins containing amide groups such as the nylons can readily be brominated or chlorinated in organic solvents to convert the (--NH--) units to (--NBr--) or (--NCl--) units and to form solutions of the N-brominated or N-chlorinated thermoplastic polymers or resins. These N-brominated or N-chlorinated thermoplastic polymer or resin solutions can be blended with silicones (siloxanes) and optionally with at least one finely divided material selected from the group consisting of inorganic and organic fillers and pigments and then can be coated on a cellular or solid rubbery hydrocarbon polymer substrate, such as an EPDM rubber in the form of a weatherstrip or glass run channel, dried and irradiated with ultraviolet light or heated at a temperature and for a period of time sufficient to reform the amide groups and to provide the rubbery substrate with an adherent and abrasion resistant coating which also exhibits a reduced coefficient of friction.
Inventors
- 👤 Kohji Y. Chihara
- 👤 Hubert J. Fabris
- 👤 Earl G. Melby
- 👤 James L. Cowell
- 👤 Harry W. Cocain
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:17
CPC Classifications
C; C08; C08G; C08G69/00; C08G69/48; C08K; C08K5/00; C08K5/54; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31569; Y10T428/31652; Y10T428/31663; Y10T428/31725
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
168 words
A composition useful as a coating comprising a solution in an organic solvent of (I) at least one chlorinated or brominated thermoplastic amide group containing polymer or resin in which the (--NH--) units have been changed to (--NBr--) or (--NCl--) units, (II) dispersed or dissolved in said solution at least one linear or branched siloxane or silicone compound which may be terminally saturated or terminally unsaturated having a viscosity of from about 25 to 2,750,000, or from about 50 to 300,000, centistokes at 25° C. and, optionally dispersed in said solution, (III) at least one finely divided material selected from the group consisting of inorganic and organic fillers and pigments having a particle size of from about 0.1 to 100, preferably from about 2 to 70, microns, (I) being used in an amount of about 100 parts by weight, (II) being used in an amount of from 5 to 80 parts by weight and (III) being used in an amount of from 5 to 60 parts by weight.
Claim 2
Dependent Claim
168 words
A composition useful as a coating comprising a solution in an organic solvent of (I) at least one chlorinated or brominated thermoplastic amide group containing polymer or resin in which the (--NH--) units have been changed to (--NBr--) or (--NCl--) units, (II) dispersed or dissolved in said solution at least one linear or branched siloxane or silicone compound which may be terminally saturated or terminally unsaturated having a viscosity of from about 25 to 2,750,000, or from about 50 to 300,000, centistokes at 25° C. and, optionally dispersed in said solution, (III) at least one finely divided material selected from the group consisting of inorganic and organic fillers and pigments having a particle size of from about 0.1 to 100, preferably from about 2 to 70, microns, (I) being used in an amount of about 100 parts by weight, (II) being used in an amount of from 5 to 80 parts by weight and (III) being used in an amount of from 5 to 60 parts by weight.
Claim 3
Dependent Claim
32 words
A composition according to claim 1 where said thermoplastic polymer or resin is selected from the group consisting of polyacrylamides, polyamideimides, polysulfonamides, polyurethanes, polyureas, polyurethane-ureas and polyamides and mixtures of the same.
Claim 4
Dependent Claim
35 words
A composition according to claim 2 where said thermoplastic polymer or resin is a nylon and where said siloxane is at least one material selected from the group consisting of trimethylsiloxy-terminated polydimethylsiloxane and dimethylvinylsiloxy-terminated polydimethylsiloxane.
Claim 5
Dependent Claim
12 words
A composition according to claim 3 where said nylon is nylon 6.
Claim 6
Dependent Claim
12 words
A composition according to claim 3 where said nylon is nylon 6,6.
Claim 7
Dependent Claim
12 words
A composition according to claim 3 where said nylon is nylon 11.
Claim 8
Dependent Claim
12 words
A composition according to claim 3 where said nylon is nylon 12.
Claim 9
Independent Claim
239 words
The method which comprises coating the surface of a cellular or solid cured rubbery hydrocarbon polymer with a composition comprising a solution in an organic solvent of (I) at least one chlorinated or brominated thermoplastic amide group containing polymer or resin in which the (--NH--) units have been changed to (13 NBr--) or (--NCl--) units, (II) dispersed or dissolved in said solution at least one linear or branched siloxane or silicone compound which may be terminally saturated or terminally unsaturated having a viscosity of from about 25 to 2,750,000, or from about 50 to 300,000, centistokes at 25° C. and optionally dispersed in said solution, (III) at least one finely divided material selected from the group consisting of inorganic and organic fillers and pigments having a particle size of from about 0.1 to 100, preferably from about 2 to 70, microns, (I) being used in an amount of about 100 parts by weight, (II) being used in an amount of from 5 to 80 parts by weight and (III) being used in an amount of from 5 to 60 parts by weight, drying and irradiating with ultraviolet light or heating the coated rubbery polymer for a period time and at a temperature sufficient to convert the (--NBr--) or (--NCl--) units to (--NH--) units to form the original amide, (--CONH--), groups of the thermoplastic polymer or resin and to form an adherent and abrasion resistant coating on the rubbery polymer.
Claim 10
Independent Claim
239 words
The method which comprises coating the surface of a cellular or solid cured rubbery hydrocarbon polymer with a composition comprising a solution in an organic solvent of (I) at least one chlorinated or brominated thermoplastic amide group containing polymer or resin in which the (--NH--) units have been changed to (13 NBr--) or (--NCl--) units, (II) dispersed or dissolved in said solution at least one linear or branched siloxane or silicone compound which may be terminally saturated or terminally unsaturated having a viscosity of from about 25 to 2,750,000, or from about 50 to 300,000, centistokes at 25° C. and optionally dispersed in said solution, (III) at least one finely divided material selected from the group consisting of inorganic and organic fillers and pigments having a particle size of from about 0.1 to 100, preferably from about 2 to 70, microns, (I) being used in an amount of about 100 parts by weight, (II) being used in an amount of from 5 to 80 parts by weight and (III) being used in an amount of from 5 to 60 parts by weight, drying and irradiating with ultraviolet light or heating the coated rubbery polymer for a period time and at a temperature sufficient to convert the (--NBr--) or (--NCl--) units to (--NH--) units to form the original amide, (--CONH--), groups of the thermoplastic polymer or resin and to form an adherent and abrasion resistant coating on the rubbery polymer.
Claim 11
Dependent Claim
35 words
The method according to claim 8 where said thermoplastic amide group containing polymer or resin is selected from the group consisting of polyacrylamides, polyamide-imides, polysulfonamides, polyurethanes, polyureas, polyurethane-ureas and polyamides and mixtures of the same.
Claim 12
Dependent Claim
16 words
The method according to claim 9 where said rubbery hydrocarbon polymer is an ethylene-propylenenon-conjugated diene terpolymer.
Claim 13
Dependent Claim
38 words
The method according to claim 10 where said thermoplastic amide group containing polymer or resin is a nylon and where said siloxane is at least one material selected from the group consisting of trimethylsiloxy-terminated polydimethylsiloxane and dimethylvinylsiloxy-terminated polydimethylsiloxane.
Claim 14
Dependent Claim
12 words
The method according to claim 11 where said nylon is nylon 6.
Claim 15
Dependent Claim
12 words
The method according to claim 11 where said nylon is nylon 6,6.
Claim 16
Dependent Claim
12 words
The method according to claim 11 where said nylon is nylon 11.
Claim 17
Dependent Claim
12 words
The method according to claim 11 where said nylon is nylon 12.
Claim 18
Dependent Claim
9 words
The product produced by the method of claim 11.
Claim 19
Dependent Claim
9 words
The product produced by the method of claim 12.
Claim 20
Dependent Claim
9 words
The product produced by the method of claim 13.
Claim 21
Dependent Claim
9 words
The product produced by the method of claim 14.
Claim 22
Dependent Claim
9 words
The product produced by the method of claim 15.
Claim 23
Dependent Claim
38 words
An automotive weatherstrip or glass run channel comprising a cured substrate of a rubbery ethylene-propylene-non conjugated diene terpolymer having an adherent and abrasion resistant coating on the surface of said terpolymer produced by the method of claim 11.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-18 | 1991-07-20 | 1992-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-18 | 1995-07-20 | 1996-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-18 | 1999-07-20 | 2000-01-19 | $7700.00 | Window Closed / Lapsed |