Process for preparing printed circuits
Assignee: Preh GmbH
•
Filing: 1986-12-23
•
Granted: 1988-02-02
•
Expires: 2006-12-23
Abstract
Abstract The present invention describes an improved reverse lamination process forreparing printed circuits with resistors, conductor strips and/or contacts integrated in the circuit. A separating layer is applied on a metallic intermediate carrier. The intermediate carrier thus coated is then printed with a conductive paste in a desired. mirror-inverted layout to provide the resistors, conductor strips and/or contacts. This is followed by the lamination which is carried out under temperature effect and under pressure, the thus laminated package comprising the intermediate carrier, an intermediate layer and the final substrate. The intermediate carrier is subsequently removed, and the separating layer is etched off. The separating layer acts as a parting agent to permit easy mechanical separation and reuse of the metallic intermediate carrier.
Inventors
- 👤 Peter Ambros
- 👤 Walter Budig
- 👤 Gisela Westermeir
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 23:58
CPC Classifications
H; H10; H10W; H10W72/00; H10W72/01; H10W72/0198; H05; H05K; H05K1/00; H05K1/16; H05K1/167; H05K3/00; H05K3/10; H05K3/20; H05K3/207; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/036; H05K1/09; H05K1/092; H05K1/095; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0364; H05K2201/0376; H05K2203/00; H05K2203/01; H05K2203/0147; H05K2203/0152; H05K2203/0156; H05K2203/03; H05K2203/0315; H05K3/38; H05K3/386; H10P; H10P72/00; H10P72/70; H10P72/74; H10P72/743; H10P72/7432; H10W74/00; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T428/00; Y10T428/12; Y10T428/12389; Y10T428/12396; Y10T428/12493; Y10T428/12535; Y10T428/12611; Y10T428/12771; Y10T428/12861; Y10T428/12903
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
172 words
A reverse laminated process for producing printed circuits, said circuits having elements selected from electrical resistors, conductor strips and connectors integrated therein, characterized by the following process steps: polishing a heat sensitive, copper alloy intermediate carrier to a high gloss on a given coating side; preparing a metal oxide separating layer directly on said coating side of said intermediate carrier, said separating layer being removable by etching; printing said separating layer of said coated intermediate carrier with said elements in a desired mirror-inverted lay-out and then drying same; subjecting said coated, printed and dried intermediate carrier to heat treatment at an elevated temperature to cure said lay-out; laminating said heat treated carrier onto a substrate; removing only said intermediate carrier from said oxide separating layer, said oxide separating layer remaining affixed to said substrate and said intermediate carrier removed in a condition suitable for reuse in the same process; and etching off said oxide separating layer from said substrate after said intermediate carrier has been removed to form a laminated printed circuit.
Claim 2
Dependent Claim
172 words
A reverse laminated process for producing printed circuits, said circuits having elements selected from electrical resistors, conductor strips and connectors integrated therein, characterized by the following process steps: polishing a heat sensitive, copper alloy intermediate carrier to a high gloss on a given coating side; preparing a metal oxide separating layer directly on said coating side of said intermediate carrier, said separating layer being removable by etching; printing said separating layer of said coated intermediate carrier with said elements in a desired mirror-inverted lay-out and then drying same; subjecting said coated, printed and dried intermediate carrier to heat treatment at an elevated temperature to cure said lay-out; laminating said heat treated carrier onto a substrate; removing only said intermediate carrier from said oxide separating layer, said oxide separating layer remaining affixed to said substrate and said intermediate carrier removed in a condition suitable for reuse in the same process; and etching off said oxide separating layer from said substrate after said intermediate carrier has been removed to form a laminated printed circuit.
Claim 3
Dependent Claim
39 words
The process according to claim 1, comprising cleaning, washing and then drying said polished intermediate carrier before preparing said separating layer, and further characterized in that said drying of said intermediate carrier is carried out in a Freon apparatus.
Claim 4
Dependent Claim
33 words
The process according to claim 1, characterized in that said step of preparing a separating layer comprises exposing said intermediate carrier to the effect of oxygen to form the metal oxide separating layer.
Claim 5
Dependent Claim
26 words
The process according to claim 3, characterized by preparing said metal oxide separating layer at a temperature of 250° C.±10° C. in about half an hour.
Claim 6
Dependent Claim
26 words
The process according to claim 1, characterized by forming said elements from a resistor paste consisting of an organic binder with a filler dispersed in it.
Claim 7
Dependent Claim
17 words
The process according to claim 5, characterized in that the binder is a melamine-formaldehyde and/or alkyd resin.
Claim 8
Dependent Claim
34 words
The process according to claim 5, characterized in that the filler consists of graphite and/or carbon black and/or silver and/or nickel particles and/or of refractory particles coated with carbon with a size of <5μ.
Claim 9
Dependent Claim
40 words
The process according to claim 3 wherein said step of preparing a separating layer comprises the step of oxidizing a surface of said intermediate carrier to form a metal oxide separating layer of said metallic composition directly on said surface.
Claim 10
Dependent Claim
24 words
The process according to claim 1, characterized by preparing on said substrate a prepeg film prepared from an epoxy resin-coated nonwoven material or fabric.
Claim 11
Dependent Claim
61 words
The process according to claim 1, characterized in that said laminating is carried out at a temperature within the range of 100° to 200° C. and preferably at about 120° C., and under a pressure within the range of 1 to 5 N/mm 2 and preferably about 1.5 N/mm 2 , for within a time of 20 minutes to 3 hours.
Claim 12
Dependent Claim
20 words
The process according to claim 1, characterized by the step of applying an intermediate layer on said coated intermediate carrier.
Claim 13
Dependent Claim
28 words
The process according to claim 11, characterized by forming said intermediate layer of a laminating resin which is selected from epoxy, phenol, polyester resin or a mixture thereof.
Claim 14
Dependent Claim
25 words
The process according to claim 1, characterized in that said substrate is an insulating material or a metal plate electrically insulated by an intermediate layer.
Claim 15
Dependent Claim
19 words
The process according to claim 11 characterized in that said intermediate layer and said substrate are one substrate element.
Claim 16
Dependent Claim
20 words
The process according to claim 14, characterized in that said substrate is a duroplast, preferably a polyphenol or a polyester.
Claim 17
Dependent Claim
100 words
A process of preparing a reverse laminated printed circuit, comprising the steps of: preparing a metal oxide separating layer directly on a monolithic, copper alloy composition intermediate carrier, printing resistive type circuit elements directly on said separating layer, laminating a resinous substrate onto said separating layer so as to envelope said elements except where they adjoin said separating layer, removing only said intermediate carrier from said separating layer, said separating layer remaining affixed to said substrate so that said intermediate carrier can be reused in carrying out the same process, and etching away said separating layer from said resinous substrate.
Claim 18
Dependent Claim
100 words
A process of preparing a reverse laminated printed circuit, comprising the steps of: preparing a metal oxide separating layer directly on a monolithic, copper alloy composition intermediate carrier, printing resistive type circuit elements directly on said separating layer, laminating a resinous substrate onto said separating layer so as to envelope said elements except where they adjoin said separating layer, removing only said intermediate carrier from said separating layer, said separating layer remaining affixed to said substrate so that said intermediate carrier can be reused in carrying out the same process, and etching away said separating layer from said resinous substrate.
References Cited (Backward Citations)
DE738414C
Cited
US3181986A
Cited
US3324014A
Cited
US3984598A
Cited
DE3031751A1
Cited
DE3131688A1
Cited
US4357395A
Cited
US4383003A
Cited
US4431710A
Cited
US4394419A
Cited
DE3135554A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-01 | 1991-08-03 | 1992-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-01 | 1995-08-03 | 1996-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-01 | 1999-08-03 | 2000-02-02 | $7700.00 | Window Closed / Lapsed |