Edge bead removal process for spin on films
Assignee: Motorola Solutions Inc
•
Filing: 1986-09-26
•
Granted: 1988-03-22
•
Expires: 2006-09-26
Abstract
Abstract A process for removing the edge bead of films that are spun onto a planar substrate, which edge bead collects at the edge of the substrate. In processes such as the manufacture of integrated circuits, the edge bead of brittle substances such as glass, SiO 2 , tends to shatter upon subsequent high temperature processing and generates particles which contaminate further processing of the integrated circuits. A pulsed or repeated application of a solvent on the edge of the substrate, a backwash step of constant rotational speed and a deceleration over time provides a means of smoothing and gradual cutting back of the spun on film edge. The deceleration spin has a starting rotational speed and a final rotational speed; and the subsequent backwash step is always at a constant rotational speed lower than the starting speed of the previous deceleration spin.
Inventors
- 👤 James M. Brewer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:48
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6342; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
125 words
A method for removing an edge bead of a film that has been spun on to the surface of a disc having an edge wherein the edge bead resides near the edge of the disc, the method comprising the steps of multiple treatments of the edge bead with a solvent application, wherein each treatment comprises the steps of: spinning the disc at a rotational speed that decreases over time, from a first speed to a second speed; and applying to the edge of the disc a solvent in which the edge bead is soluble, while spinning the disc at a third speed less than the first speed; wherein the first speed of each successive treatment is less than the first speed of the previous treatment.
Claim 2
Independent Claim
125 words
A method for removing an edge bead of a film that has been spun on to the surface of a disc having an edge wherein the edge bead resides near the edge of the disc, the method comprising the steps of multiple treatments of the edge bead with a solvent application, wherein each treatment comprises the steps of: spinning the disc at a rotational speed that decreases over time, from a first speed to a second speed; and applying to the edge of the disc a solvent in which the edge bead is soluble, while spinning the disc at a third speed less than the first speed; wherein the first speed of each successive treatment is less than the first speed of the previous treatment.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein the disc is a semiconductor wafer and the film is a spin-on-glass (SOG) film.
Claim 4
Dependent Claim
34 words
The method of claim 1 wherein the disc has two flat, opposite surfaces and the film is applied to the top surface and the solvent is applied to the bottom surface near the edge.
Claim 5
Dependent Claim
45 words
The method of claim 1 wherein the first speed of each successive treatment after a first treatment is between the first and second speeds of the previous treatment and the second speed of the successive treatment is below the second speed of the previous treatment.
Claim 6
Independent Claim
133 words
A method for removing an edge bead of a film that has been spun on to the surface of a disc having an edge wherein the edge bead resides near the edge of the disc, the method comprising the steps of multiple treatments of the edge bead with a solvent application, wherein each treatment comprises the steps of: spinning the disc at a rotational speed that decreases over time, from a first speed to a second speed; and applying to the edge of the disc a solvent in which the edge bead is soluble, while spinning the disc at a third speed less than the first speed, but at least equal to the second speed; wherein the first speed of each successive treatment is less than the first speed of the previous treatment.
Claim 7
Independent Claim
133 words
A method for removing an edge bead of a film that has been spun on to the surface of a disc having an edge wherein the edge bead resides near the edge of the disc, the method comprising the steps of multiple treatments of the edge bead with a solvent application, wherein each treatment comprises the steps of: spinning the disc at a rotational speed that decreases over time, from a first speed to a second speed; and applying to the edge of the disc a solvent in which the edge bead is soluble, while spinning the disc at a third speed less than the first speed, but at least equal to the second speed; wherein the first speed of each successive treatment is less than the first speed of the previous treatment.
Claim 8
Dependent Claim
20 words
The method of claim 5 wherein the disc is a semiconductor wafer and the film is a spin-on-glass (SOG) film.
Claim 9
Dependent Claim
34 words
The method of claim 5 wherein the disc has two flat, opposite surfaces and the film is applied to the top surface and the solvent is applied to the bottom surface near the edge.
Claim 10
Dependent Claim
47 words
The method of claim 5 wherein the first speed of the of each successive treatment after a first treatment is between the first and second speeds of the previous treatment and the second speed of the successive treatment is below the second speed of the previous treatment.
Claim 11
Independent Claim
155 words
A method for removing an edge bead of a film that has been spun on to the surface of a disc having an edge wherein the edge bead resides near the edge of the disc, the method comprising the steps of: a first treatment comprising: spinning the disc at a rotational speed that decreases over time, from a first speed to a second speed; applying to the edge of the disc a solvent in which the edge bead is soluble while spinning the disc at a third speed less than the first speed; and a successive treatment comprising: spinning the disc at a rotational speed that decreases over time, from a first speed which is less than the first speed of the first treatment, to a second speed; and reapplying fresh solvent to the edge of the disc while spinning the disc at a third speed less than the first speed of this successive treatment.
Claim 12
Independent Claim
155 words
A method for removing an edge bead of a film that has been spun on to the surface of a disc having an edge wherein the edge bead resides near the edge of the disc, the method comprising the steps of: a first treatment comprising: spinning the disc at a rotational speed that decreases over time, from a first speed to a second speed; applying to the edge of the disc a solvent in which the edge bead is soluble while spinning the disc at a third speed less than the first speed; and a successive treatment comprising: spinning the disc at a rotational speed that decreases over time, from a first speed which is less than the first speed of the first treatment, to a second speed; and reapplying fresh solvent to the edge of the disc while spinning the disc at a third speed less than the first speed of this successive treatment.
Claim 13
Dependent Claim
20 words
The method of claim 9 wherein the disc is a semiconductor wafer and the film is a spin-on-glass (SOG) film.
Claim 14
Dependent Claim
16 words
The method of claim 9 wherein the treatments are repeated until the edge bead is removed.
Claim 15
Dependent Claim
34 words
The method of claim 9 wherein the disc has two flat, opposite surfaces and the film is applied to the top surface and the solvent is applied to the bottom surface near the edge.
Claim 16
Independent Claim
150 words
A method for forming a film of material spun onto a semiconductor wafer wherein the material film has a smooth edge comprising the steps of: dispensing a solution of the material of the spin on film onto a semiconductor wafer having a surface and an edge; spinning the wafer at a starting speed for a constant speed time period to distribute the solution of material over the surface of the wafer incidentally forming an edge bead at or near the edge of the wafer; and performing a plurality of treatments, each treatment comprising the steps of: reducing the rotational speed of the wafer from a first speed to a second speed; applying a quantity of a fresh solvent to the edge of the wafer wherein the film material is soluble in the solvent while spinning the wafer at a third speed less than the first speed of the previous step.
Claim 17
Independent Claim
150 words
A method for forming a film of material spun onto a semiconductor wafer wherein the material film has a smooth edge comprising the steps of: dispensing a solution of the material of the spin on film onto a semiconductor wafer having a surface and an edge; spinning the wafer at a starting speed for a constant speed time period to distribute the solution of material over the surface of the wafer incidentally forming an edge bead at or near the edge of the wafer; and performing a plurality of treatments, each treatment comprising the steps of: reducing the rotational speed of the wafer from a first speed to a second speed; applying a quantity of a fresh solvent to the edge of the wafer wherein the film material is soluble in the solvent while spinning the wafer at a third speed less than the first speed of the previous step.
Claim 18
Dependent Claim
18 words
The method of claim 13 wherein the third speed is also at least equal to the second speed.
Claim 19
Dependent Claim
21 words
The method of claim 13 wherein the semiconductor wafer is silicon and the spin on film is a spin-on-glass (SOG) film.
Claim 20
Dependent Claim
34 words
The method of claim 13 wherein the wafer has two flat, opposite surfaces and the film is applied to the top surface and the solvent is applied to the bottom surface near the edge.
Claim 21
Independent Claim
357 words
A method for forming a film of spin-on-glass (SOG) on a semiconductor wafer wherein the SOG film has a smooth edge comprising the steps of: dispensing a SOG solution onto a semiconductor wafer having a flat top surface, a flat bottom surface and an edge; spinning the wafer at a first rotational speed for a first time period to distribute the spin-on-glass solution over the top surface of the wafer incidentally forming an edge bead near the edge of the wafer; a first solvent treatment comprising: reducing the rotational speed of the wafer from the first to a second speed; applying a first quantity of fresh solvent to the edge of the wafer from the bottom surface of the wafer, wherein the edge bead is soluble in the solvent while spinning the wafer at a third rotational speed that is less than the first speed but at least equal to the second speed; a second solvent treatment comprising: reducing the rotational speed of the wafer from a first speed to a second speed where the first speed is lower than the first speed of the previous treatment and the second speed is lower than the second speed of the previous treatment; applying a second quantity of fresh solvent to the edge of the wafer from the bottom surface of the wafer while spinning the wafer at a third rotational speed that is less than the first speed but at least equal to the second speed; and a third solvent treatment comprising: reducing the rotational speed of the wafer from a first speed to a second speed wherein the first speed is lower than the first speed of the previous treatment and the second speed is lower than the second speed of the previous treatment; and applying a third quantity of fresh solvent to the edge of the wafer from the bottom surface of the wafer while spinning the wafer at a third rotational speed that is less than the first speed but at least equal to the second speed of the third solvent treatment; and repeating the solvent treatments until the edge of the film is smooth.
Claim 22
Independent Claim
357 words
A method for forming a film of spin-on-glass (SOG) on a semiconductor wafer wherein the SOG film has a smooth edge comprising the steps of: dispensing a SOG solution onto a semiconductor wafer having a flat top surface, a flat bottom surface and an edge; spinning the wafer at a first rotational speed for a first time period to distribute the spin-on-glass solution over the top surface of the wafer incidentally forming an edge bead near the edge of the wafer; a first solvent treatment comprising: reducing the rotational speed of the wafer from the first to a second speed; applying a first quantity of fresh solvent to the edge of the wafer from the bottom surface of the wafer, wherein the edge bead is soluble in the solvent while spinning the wafer at a third rotational speed that is less than the first speed but at least equal to the second speed; a second solvent treatment comprising: reducing the rotational speed of the wafer from a first speed to a second speed where the first speed is lower than the first speed of the previous treatment and the second speed is lower than the second speed of the previous treatment; applying a second quantity of fresh solvent to the edge of the wafer from the bottom surface of the wafer while spinning the wafer at a third rotational speed that is less than the first speed but at least equal to the second speed; and a third solvent treatment comprising: reducing the rotational speed of the wafer from a first speed to a second speed wherein the first speed is lower than the first speed of the previous treatment and the second speed is lower than the second speed of the previous treatment; and applying a third quantity of fresh solvent to the edge of the wafer from the bottom surface of the wafer while spinning the wafer at a third rotational speed that is less than the first speed but at least equal to the second speed of the third solvent treatment; and repeating the solvent treatments until the edge of the film is smooth.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-22 | 1991-09-21 | 1992-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-22 | 1995-09-21 | 1996-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-22 | 1999-09-21 | 2000-03-22 | $7700.00 | Window Closed / Lapsed |