Composite hollow fibers and method of making same
Assignee: Mitsubishi Chemical Corp
•
Filing: 1985-06-27
•
Granted: 1988-05-03
•
Expires: 2005-06-27
Abstract
Abstract The present invention provides a novel composite porous hollow fiber comprising at least two layers joined to each other, characterized in that the layers consist of thermoplastic organic polymers of different types or of the same type and have micropores of different sizes, the micropores of these layers are interconnected to form contiguous micropores extending from the external surface to the internal surface of the hollow fiber, and the layer having larger micropores is thicker than the layer having smaller micropores, as well as a method of making such a hollow fiber, which method comprises melt-spinning a hollow fiber by feeding polymers of different types or of the same type through a nozzle having two or more concentrically disposed annular orifices, then stretching the hollow fiber, and subsequently heat setting the stretched hollow fiber. The composite hollow fiber gives higher permeation rates for permeative substances, as compared with prior art hollow fibers. Moreover, this composite hollow fiber makes it possible to ameliorate its chemical and physical interaction with certain substances while retaining its desired fractionation capability.
Inventors
- 👤 Tohru Takemura
- 👤 Haruhiko Yoshida
- 👤 Osamu Hukunaga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 09:36
CPC Classifications
D; D01; D01D; D01D5/00; D01D5/24; B; B01; B01D; B01D69/00; B01D69/08; D01D5/28; D01D5/30; D01D5/34
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
97 words
A method of making a composite hollow fiber, which comprises: melt-spinning a hollow fiber composed of at least two layer consisting of different thermoplastic polymers or the same type of thermoplastic organic polymers having different MI values and having different thicknesses, through a hollow fiber-forming nozzle having at least two concentrically disposed annualr orifices, wherein said polymers are separately fed through said orifices; immediately stretching said hollow fiber to produce a multiplicity of micropores in each of said layers so that the thicker has larger micropores than the thinner layer; and subsequently heat-setting the stretched hollow fiber.
Claim 2
Independent Claim
97 words
A method of making a composite hollow fiber, which comprises: melt-spinning a hollow fiber composed of at least two layer consisting of different thermoplastic polymers or the same type of thermoplastic organic polymers having different MI values and having different thicknesses, through a hollow fiber-forming nozzle having at least two concentrically disposed annualr orifices, wherein said polymers are separately fed through said orifices; immediately stretching said hollow fiber to produce a multiplicity of micropores in each of said layers so that the thicker has larger micropores than the thinner layer; and subsequently heat-setting the stretched hollow fiber.
Claim 3
Dependent Claim
37 words
The method of making a composite hollow fiber as claimed in claim 1 wherein at least the high polymer constituting said thicker layer has a melt index of 0.1 to 50 at the time of its spinning.
Claim 4
Dependent Claim
53 words
A method of making a composite hollow fiber as claimed in claim 1 wherein, with respect to each of the polymers being fed, said melt spinning is carried out at a spinning temperature ranging from the melting point of the polymer to a temperature higher than said melting point by about 80° C.
Claim 5
Dependent Claim
29 words
A method of making a composite hollow fiber as claimed in claim 1 wherein said melt spinning is carried out with a spinning draw ratio of 30 or greater.
Claim 6
Dependent Claim
24 words
A method of making a composite hollow fiber as claimed in claim 1 wherein said stretching is carried out in a plurality of stages.
Claim 7
Dependent Claim
43 words
The method of making a composite hollow fiber as claimed in claim 5 wherein the first stage of said multi-stage stretching is carried out at a stretching temperature ranging from 0° C. to a temperature lower than the melting points by 50° C.
Claim 8
Dependent Claim
38 words
The method of making a composite hollow fiber as claimed in claim 1 wherein said stretching is carried out in such a way that the ratio of fiber elongation to original fiber length ranges from 0.1 to 8.
Claim 9
Dependent Claim
23 words
The method of making a composite hollow fiber as claimed in claim 1 wherein said heat setting is carried out under constant-length conditions.
Claim 10
Dependent Claim
34 words
The method of making a composite hollow fiber as claimed in claim 1 wherein said heat setting is carried out while said hollow fiber is relaxed by 80% or less of the fiber elongation.
Claim 11
Dependent Claim
31 words
The method of making a composite hollow fiber as claimed in claim 1 wherein said heat setting is carried out at a temperature equal to or higher than the stretching temperature.
Claim 12
Dependent Claim
22 words
The method of claim 1, which process further comprises, before stretching said hollow fiber, annealing the hollow fiber which hs been melt-spun.
Claim 13
Dependent Claim
86 words
A melt-spun and stretched composite hollow fiber comprising at least two layers joined to each other said layer consisting of different thermoplastic organic polymers or the same type of thermoplastic organic polymer having different MI values and having micropores of different sizes, said micropores being internconnected within each of said layers or between siad layers to form contiguous micropores extending from the external surface of said hollow fiber to its internal surface, with the layer having larger micropores being thicker than the layer having smaller micropores.
Claim 14
Dependent Claim
86 words
A melt-spun and stretched composite hollow fiber comprising at least two layers joined to each other said layer consisting of different thermoplastic organic polymers or the same type of thermoplastic organic polymer having different MI values and having micropores of different sizes, said micropores being internconnected within each of said layers or between siad layers to form contiguous micropores extending from the external surface of said hollow fiber to its internal surface, with the layer having larger micropores being thicker than the layer having smaller micropores.
Claim 15
Dependent Claim
58 words
The composite hollow fiber of claim 12, wherein the internal diameter of said hollow fiber ranges from 50 to 5000 μm, the combined thickness of said layers ranges from 5 to 500 μm, and the rate of air premeation from the inside to the outside of said hollow fiber is not less than 100 liters/m 2 ·hr·0.5 atm.
Claim 16
Dependent Claim
43 words
The composite hollow fiber of claim 12, wherein said thermoplastic organic polymers are selected from the group consisting of polyethylene, polyporpylene, poly-3-methylbutene-1, poly-4-methylpentene-1, polyvinylidene fluroide, polyethylene terephthalate, polytetramethylene terephthalate, polyhexamethylene adipate, polycarprolactam, polyoxymethyleen, crystalline copolymers composed chiefly of these homopolymers, and combinations thereof.
Claim 17
Dependent Claim
61 words
The composite hollow fiber of claim 14, wherein the thermoplastic organic polymers of said two layers are combinations of at least one of the polymer materials of claim 14 in combination with at least one polymer selected from the group consisting of silicone resins, polyurethanes, ethylene-vinyl acetate coppolymers, hydrolyzates of said ethylene-vinyl acetate copolymers, ethylene-vinyl alcohol copolymers and ethylene-vinyl chloride copolymers.
References Cited (Backward Citations)
US4164437A
Cited
JPS5410282A
Cited
JPS5442424A
Cited
JPS55107507A
Cited
US4385094A
Cited
JPS55155704A
Cited
JPS56152704A
Cited
JPS5766114A
Cited
US4401567A
Cited
US4444710A
Cited
JPS607853A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-03 | 1991-11-02 | 1992-05-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-03 | 1995-11-02 | 1996-05-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-03 | 1999-11-02 | 2000-05-03 | $7700.00 | Window Closed / Lapsed |