Abstract A protective layer for carbonaceous materials, especially graphite electrodes, applied by plasma-coating method comprised of 65-98 w /o of metal aluminum, 1-20 w /o of combined metal silicon with silica (SiO l ) and up to 15 w /o of oxygenous compounds of aluminum. The resistivity of the layer is 0.07.10 -6 ohm.m up to 0.3.10 -6 ohm.m at 20° C. and 0.12.10 -6 ohm.m up to 0.7.10 -6 ohm.m at 400° C. The method of producing the protective layer comprises the following steps of directing a plasma flame of a water stabilized plasma burner toward the carbonaceous material, and feeding into a plasma flame a particulate composition comprising between about 85 w /o to about 99 w /o of metallic aluminum having a particle size of between about 0.09 to about 0.180 mm and between about 1 to about 15 w /o of silicon having a particle size of between about 0.07 to about 0.165 mm.
A protective layer for a carbonaceous material applied by a plasma coating technique comprising the following constituents: between about 65 w/o and about 98 w/o of metallic aluminum, about 1 w/o to about 20 w/o of combined metallic silicon and silica, and up to about 15 w/o of oxygenous aluminum compounds, wherein the relative weight percent of said constituents total 100% and wherein the layer has a resistivity of between 0.07×10 -6 ohm.m and 0.3×10 -6 ohm.m at 20° C. and between 0.12×10 -6 ohm.m and 0.7×10 -6 ohm.m at 400° C.
Claim 2
Dependent Claim
92 words
A protective layer for a carbonaceous material applied by a plasma coating technique comprising the following constituents: between about 65 w/o and about 98 w/o of metallic aluminum, about 1 w/o to about 20 w/o of combined metallic silicon and silica, and up to about 15 w/o of oxygenous aluminum compounds, wherein the relative weight percent of said constituents total 100% and wherein the layer has a resistivity of between 0.07×10 -6 ohm.m and 0.3×10 -6 ohm.m at 20° C. and between 0.12×10 -6 ohm.m and 0.7×10 -6 ohm.m at 400° C.
Claim 3
Dependent Claim
31 words
The protective layer according to claim 1 wherein the layer has a specific weight of between about 1900 to 2300 kg/m 3 and a thickness of about 0.3 to 1.5 mm.