Method for producing ultra-high purity, optical quality, glass articles
Assignee: Corning Glass Works
•
Filing: 1987-05-20
•
Granted: 1988-12-06
•
Expires: 2007-05-20
Abstract
Abstract A method for producing ultra-high purity, optical quality, glass articles is disclosed which involves: (1) forming a gel from a silicon-containing organic compound, such as, TEOS; (2) drying the gel to produce granules having a mean particle size of less than about 1 millimeter; (3) fully sintering the granules to produce high purity, artificial sand; (4) casting the artificial sand by conventional techniques, such as, slip casting, to form a high density, porous, green body; (5) drying and partially sintering the green body; (6) fully sintering the green body under vacuum; and (7) hot isostatic pressing ("hipping") the green body. The glass articles produced by the process have higher purity, greater homogeneity, and less IR absorption than existing, commercially available, premium quality, fused silica, glass articles. In addition, in accordance with the invention, high purity glass articles of complex shapes can be directly cast, rather than being machined or pressed from sheets of glass, as in the prior art.
Inventors
- 👤 Paul M. Schermerhorn
- 👤 Michael P. Teter
- 👤 Robert V. VanDewoestine
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:59
CPC Classifications
C; C03; C03B; C03B19/00; C03B19/12; C03C; C03C1/00; C03C1/006; C03B19/06; C03B19/066; C03B19/10; C03B19/1005; C03B19/106; C03B19/1065; C03B20/00; C03B37/00; C03B37/01; C03B37/012; C03B37/0128; C03B37/01282
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
198 words
A method for producing a fused silica glass article comprising the steps of: (a) preparing a solution which contains at least one silicon-containing organic compound having the formula Si(OR) 4 or SiR(OR) 3 , where R is an alkyl group; (b) polymerizing the silicon in the solution to form a SiO 2 gel; (c) drying the gel at a rate which causes the gel to fragment into granules having a mean particle size less than about one millimeter; (d) sintering the granules at a temperature less than about 1150° C., the density of the granules after sintering being approximately equal to their maximum theoretical density; (e) forming a green body from the sintered granules; (f) drying and partially sintering the green body in a chamber by (i) raising the temperature of the chamber to above about 1000° C., and (ii) introducing chlorine gas into the chamber and/or subjecting the chamber to a vacuum and/or purging the chamber with an inert gas; and (g) fully sintering the green body in a chamber by raising the temperature of the chamber to a temperature above about 1720° C. while purging the chamber with helium or applying a vacuum to the chamber.
Claim 2
Independent Claim
198 words
A method for producing a fused silica glass article comprising the steps of: (a) preparing a solution which contains at least one silicon-containing organic compound having the formula Si(OR) 4 or SiR(OR) 3 , where R is an alkyl group; (b) polymerizing the silicon in the solution to form a SiO 2 gel; (c) drying the gel at a rate which causes the gel to fragment into granules having a mean particle size less than about one millimeter; (d) sintering the granules at a temperature less than about 1150° C., the density of the granules after sintering being approximately equal to their maximum theoretical density; (e) forming a green body from the sintered granules; (f) drying and partially sintering the green body in a chamber by (i) raising the temperature of the chamber to above about 1000° C., and (ii) introducing chlorine gas into the chamber and/or subjecting the chamber to a vacuum and/or purging the chamber with an inert gas; and (g) fully sintering the green body in a chamber by raising the temperature of the chamber to a temperature above about 1720° C. while purging the chamber with helium or applying a vacuum to the chamber.
Claim 3
Dependent Claim
51 words
The method of claim 1 including the additional step after step (g) of hot isostatic pressing the fully sintered green body in a chamber by raising the temperature of the chamber to above about 1150° C. and introducing an inert gas into the chamber at a pressure above about 100 psig.
Claim 4
Dependent Claim
23 words
The method of claim 2 wherein the fully sintered green body is wrapped in glass wool prior to the hot isostatic pressing step.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein the solution of step (a) contains tetraethylorthosilicate having the formula Si(OC 2 H 5 ) 4 .
Claim 6
Dependent Claim
71 words
The method of claim 1 wherein the glass article is doped through the inclusion in the solution of step (a) of at least one element selected from the group consisting of aluminum, antimony, barium, beryllium, bismuth, boron, bromine, cadmium, calcium, cerium, chlorine, chromium, cobalt, copper, europium, fluorine, germanium, iron, lanthanum, lead, lithium, magnesium, neodymium, nickel, oxygen, phosphorous, potassium, samarium, silver, sodium, strontium, tantalum, tin, titanium, uranium, vanadium, yttrium, zinc, and zirconium.
Claim 7
Dependent Claim
25 words
The method of claim 5 wherein the element is titanium and the glass article has a coefficient of expansion of less than 0.5×10 -7 cm/cm/°C.
Claim 8
Dependent Claim
29 words
The method f claim 6 wherein the titanium is introduced into the solution as a titanium ester having the formula Ti(OR) 4 , where R is an alkyl group.
Claim 9
Dependent Claim
40 words
The method of claim 7 wherein the titanium ester is selected from the group consisting of tetraethyl titanate having the formula Ti(OC 2 H 5 ) 4 and tetraisopropyl titanate having the formula Ti(OCH(CH 3 ) 2 ) 4 .
Claim 10
Dependent Claim
24 words
The method of claim 1 wherein the drying of step (c) is performed in a rotary dryer at a temperature above about 100° C.
Claim 11
Dependent Claim
27 words
The method of claim 1 wherein the gel and/or the granules are treated with oxygen during at least a portion of step (c) to remove organic materials.
Claim 12
Dependent Claim
25 words
The method of claim 10 wherein the rate of oxygen treatment is controlled so as to prevent substantial charring of the gel and/or the granules.
Claim 13
Dependent Claim
30 words
The method of claim 11 wherein the rate of oxygen treatment is controlled so that the temperature of the gel and/or the granules does not rise above about 340° C.
Claim 14
Dependent Claim
50 words
The method of claim 1 wherein the surface area per unit mass of the granules prior to sintering step (d) is greater than about 150 square meters per gram and the surface area per unit mass of the granules after sintering is less than about 0.5 square meters per gram.
Claim 15
Dependent Claim
32 words
The method of claim 1 wherein the sintered granules of step (d) are milled in water to form a slurry and wherein the green body is formed by slip casting the slurry.
Claim 16
Dependent Claim
23 words
The method of claim 14 wherein the mean particle size of the milled granules is between about 5 microns and about 15 microns.
Claim 17
Dependent Claim
21 words
The method of claim 14 wherein the specific gravity of the slurry is greater than about 1.70 grams per cubic centimeter.
Claim 18
Dependent Claim
21 words
The method of claim 1 wherein the granules are held together in the green body by means of an organosilicon binder.
Claim 19
Dependent Claim
32 words
The method of claim 1 wherein oxygen is introduced into the chamber during at least a portion of step (f) to reduce the level of organic material associated with the green body.
Claim 20
Dependent Claim
137 words
The method of claim 1 wherein the glass article is an optical waveguide fiber and wherein: (i) the solution of step (a) contains tetraethylorthosilicate having the formula Si(OC 2 H 5 ) 4 ; (ii) the sintered granules of step (d) are milled in water to form a slurry, said milled granules having a mean particle size between about 5 microns and about 15 microns; (iii) the green body is formed by slip casting the slurry about a rod which contains a center portion and an outer portion, the center portion including at least one region which has an index of refraction which is greater than the outer portion; (iv) chlorine is introduced into the chamber during step (f); and (v) the fully sintered green body produced by step (g) is drawn into an optical waveguide fiber.
Claim 21
Dependent Claim
28 words
The method of claim 19 wherein during at least a portion of drying step (c), the gel and/or the granules are treated with oxygen to remove organic materials.
Claim 22
Dependent Claim
51 words
The method of claim 19 including the additional step after step (g) of hot isostatic pressing the fully sintered green body in a chamber by raising the temperature of the chamber to above about 1150° C. and introducing an inert gas into the chamber at a pressure above about 100 psig.
Claim 23
Independent Claim
104 words
A method for producing fused silica granules comprising the steps of: (a) preparing a solution which contains at least one silicon-containing organic compound having the formula Si(OR) 4 or SiR(OR) 3 , where R is an alkyl group; (b) polymerizing the silicon in the solution to form a SiO 2 gel; (c) drying the gel at a rate which causes the gel to fragment into granules having a mean particle size less than about 1 millimeter; and (d) sintering the granules at a temperature less than about 1150° C., the density of the granules after sintering being approximately equal to their maximum theoretical density.
Claim 24
Independent Claim
104 words
A method for producing fused silica granules comprising the steps of: (a) preparing a solution which contains at least one silicon-containing organic compound having the formula Si(OR) 4 or SiR(OR) 3 , where R is an alkyl group; (b) polymerizing the silicon in the solution to form a SiO 2 gel; (c) drying the gel at a rate which causes the gel to fragment into granules having a mean particle size less than about 1 millimeter; and (d) sintering the granules at a temperature less than about 1150° C., the density of the granules after sintering being approximately equal to their maximum theoretical density.
Claim 25
Dependent Claim
22 words
The method of claim 22 including the additional step after step (d) of milling the granules to reduce their mean particle size.
Claim 26
Dependent Claim
24 words
The method of claim 23 wherein the granules are milled until their mean particle size is between about 5 microns and about 15 microns.
Claim 27
Dependent Claim
23 words
The method of claim 22 wherein the solution of step (a) contains tetraethylorthosilicate having the formula Si(OC 2 H 5 ) 4 .
Claim 28
Dependent Claim
71 words
The method of claim 22 wherein the glass granules are doped through the inclusion in the solution of step (a) of at least one element selected from the group consisting of aluminum, antimony, barium, beryllium, bismuth, boron, bromine, cadmium, calcium, cerium, chlorine, chromium, cobalt, copper, europium, fluorine, germanium, iron, lanthanum, lead, lithium, magnesium, neodymium, nickel, oxygen, phosphorous, potassium, samarium, silver, sodium, strontium, tantalum, tin, titanium, uranium, vanadium, yttrium, zinc, and zirconium.
Claim 29
Dependent Claim
36 words
The method of claim 26 wherein (i) the element is titanium, and (ii) the titanium is introduced into the solution as a titanium ester having the formula Ti(OR) 4 , where R is an alkyl group.
Claim 30
Dependent Claim
40 words
The method of claim 27 wherein the titanium ester is selected from the group consisting of tetraethyl titanate having the formula Ti(OC 2 H 5 ) 4 and tetraisopropyl titanate having the formula Ti(OCH(CH 3 ) 2 ) 4 .
Claim 31
Dependent Claim
24 words
The method of claim 22 wherein the drying of step (c) is performed in a rotary dryer at a temperature above about 100° C.
Claim 32
Dependent Claim
27 words
The method of claim 22 wherein the gel and/or the granules are treated with oxygen during at least a portion of step (c) to remove organic materials.
Claim 33
Dependent Claim
25 words
The method of claim 30 wherein the rate of oxygen treatment is controlled so as to prevent substantial charring of the gel and/or the granules.
Claim 34
Dependent Claim
30 words
The method of claim 31 wherein the rate of oxygen treatment is controlled so that the temperature of the gel and/or the granules does not rise above about 340° C.
Claim 35
Dependent Claim
50 words
The method of claim 22 wherein the surface area per unit mass of the granules prior to sintering step (d) is greater than about 150 square meters per gram and the surface area per unit mass of the granules after sintering is less than about 0.5 square meters per gram.
References Cited (Backward Citations)
US2942991A
Cited
US3310392A
Cited
US3535890A
Cited
US3562371A
Cited
US3678144A
Cited
US4042550A
Cited
US4112032A
Cited
US4042361A
Cited
US4200445A
Cited
GB2041913A
Cited
US4287105A
Cited
US4358306A
Cited
GB2086369A
Cited
US4414014A
Cited
US4419115A
Cited
US4426216A
Cited
EP0084438A2
Cited
US4681615A
Cited
US4574063A
Cited
US4608215A
Cited
GB2170799A
Cited
US4622056A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-06 | 1992-06-06 | 1992-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-06 | 1996-06-06 | 1996-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-06 | 2000-06-06 | 2000-12-06 | $7700.00 | Window Closed / Lapsed |