Magnetic recording disc and process for producing the same
Assignee: Emtec Magnetics GmbH
•
Filing: 1986-11-19
•
Granted: 1989-02-28
•
Expires: 2006-11-19
Abstract
Abstract An improved magnetic recording disc comprising: a substrate member of an alumina-based ceramic material having micropores of 5 μm or below and having a relative theoretical density of 90% or higher; a glass coating layer of a thickness of 3 to 200 μm with a surface roughness (R z ) of 180 angstroms or below, and being free from micropores and strain; a magnetic thin film formed on the surface of the glass coating layer; and a protective film formed thereon. A process for production of the magnetic recording disc comprises: forming a glass coating layer to a thickness of 5 to 220 μm on the surface of an alumina-based ceramic substrate having micropores of 5 μm or below and a relative theoretical density of at least 90%; then subjecting the glass coating layer to mechanochemical polishing to a layer thickness of 3 to 200 μm, to make free from micropores and strain, and to have a surface roughness (R z ) of 180 angstroms or below; and further coating the surface of the glass coating layer with a magnetic thin film and a protective film.
Inventors
- 👤 Toshiaki Wada
- 👤 Yoshiaki Katsuyama
- 👤 Junichi Nakaoka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 02:58
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/84; G11B5/62; G11B5/73; G11B5/739; G11B5/73911; G11B5/73921; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/24999
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
128 words
A magnetic recording disc, which comprises: (a) a substrate member of a nalumina-based ceramic material containing therein micropores witha size of 5 μm or below and having a relative theoretical density of 90% or higher; (b) a glass coating layer having a thickness of from 3 μm to 200 μm, having a surface roughness (R z ) of 180 angstroms or below and a softening point of 400°-900° C., containing no more than 50 per 100 cm 2 micropores having a size exceeding 0.2 μm, and being free from strain with a Beilby layer thickness of no more than 50 angstroms; (c) a magnetic thin coating film disposed on the surface of said glass coating layer; and (d) a protective coating film formed on said magnetic thin film.
Claim 2
Dependent Claim
128 words
A magnetic recording disc, which comprises: (a) a substrate member of a nalumina-based ceramic material containing therein micropores witha size of 5 μm or below and having a relative theoretical density of 90% or higher; (b) a glass coating layer having a thickness of from 3 μm to 200 μm, having a surface roughness (R z ) of 180 angstroms or below and a softening point of 400°-900° C., containing no more than 50 per 100 cm 2 micropores having a size exceeding 0.2 μm, and being free from strain with a Beilby layer thickness of no more than 50 angstroms; (c) a magnetic thin coating film disposed on the surface of said glass coating layer; and (d) a protective coating film formed on said magnetic thin film.
Claim 3
Dependent Claim
28 words
A magnetic recording disc as set forth in claim 1, wherein said micropores in the surface of said substrate member has a size of 3 μm or below.
Claim 4
Dependent Claim
30 words
A magnetic recordimg disc as set forth in claim 1, wherein the surface roughness of said glass coating layer is in a range of from 50 angstroms to 150 angstroms.
Claim 5
Dependent Claim
30 words
A a magnetic recording disc as set forth in claim 1, wherein the surface of said glass coating layer has a Beilby layer thickness of no more than 20 angstroms.
Claim 6
Dependent Claim
30 words
A magnetic recording disc as set forth in claim 1 or 4, wherein the surface of said glass coating layer contains micropores having a diameter of 0.1 μm or below.
Claim 7
Dependent Claim
30 words
A magnetic recording disc as set forth in claim 1, wherein the surface of said glass coating layer has a Bailby layer of a thickness of 50 angstroms or below.
Claim 8
Dependent Claim
29 words
A magnetic recording disc as set forth in claim 6, wherein the surface of said glass coating layer has a Bailby layer of thickness of 20 angstroms or below.
Claim 9
Dependent Claim
28 words
A magnetic recording disc as set forth in claim 1, wherein said glass coating layer is formed by at least one method of glazing and physical vapor deposition.
Claim 10
Dependent Claim
34 words
A magnetic recording disc as set forth in claim 1, wherein said glass coating layer has a difference in the thermal expansion coefficient between it and said alumina-based ceramic substrate of 2×10 -6 /deg.C.
Claim 11
Dependent Claim
49 words
A magnetic recording disc as set forth in claim 1, wherein said protective film formed on the outermost surface of said substrate is composed of at least one substance selected from the group consisting of SiO 2 , C, Si 3 N 4 and Al 2 O 3 .
Claim 12
Dependent Claim
30 words
A magnetic recording disc as set forth in claim 8, wherein the glass coating layer has been formed by sputtering and has a softening point of 500° C. or above.
Claim 13
Dependent Claim
27 words
A magnetic recording disc according to claim 10, wherein said glazed glass coating layer has its thickness in a range of from 3 μm to 200 μm.
Claim 14
Dependent Claim
29 words
A magnetic recording disc as set forth in claim 11, wherein said sputtered glass coating layer has its thickness in a range of from 10 μm to 200 μm.
Claim 15
Dependent Claim
57 words
A magnetic recording disc as set forth in claim 1, wherein said alumina-based ceramic substrate material is a sintered body of a material selected from the group consisting of Al 2 O 3 system, Al 2 O 3 -TiC system, Al 2 O 3 -TiO 2 system, and Al 2 O 3 -TiC-Fe 2 O 3 system.
Claim 16
Dependent Claim
44 words
A magnetic recording disc as set forth in claim 1, wherein said magnetic thin film is formed of at least one substance selected from the group consisting of γ-Fe 2 O 3 , Co-Cr system, Co-Ni system, Co-P system, Ba-ferrite, Cr, and Fe-Ni system.
Claim 17
Dependent Claim
35 words
A magnetic recording disc as set forth in claim 1, 15 or 10, wherein said magnetic thin film and said protective film is formed by at least one method of sputtering, spin-coating, and glow-discharge polymerization.
Claim 18
Dependent Claim
172 words
A process for producing a magnetic recording disc, which comprises the steps of: (a) forming a glass coating layer of a glass having a softening point of from about 400°-900° C. to a thickness in a range of from 5 μm to 220 μm on the surface of an alumina-based ceramic substrate containing therein micropores with a size of 5 μm or below having a relative theoretical density of at least 90% or above; (b) then, subjecting said glass coating layer on said substrate to mechanochemically polishing process to render it to have a surface roughness (R z ) of 180 angstroms or less, to contain no more than 50 micropores having a size exceeding 0.2 μm per 100 cm 2 , to be free from strain with a Beilby layer thickness of no more than 50 angstroms, and to have layer thickness in a range of from 3 μm to 200 μm; and (c) further coating the surface of said glass coating layer with a magnetic thin film and protective film.
Claim 19
Dependent Claim
172 words
A process for producing a magnetic recording disc, which comprises the steps of: (a) forming a glass coating layer of a glass having a softening point of from about 400°-900° C. to a thickness in a range of from 5 μm to 220 μm on the surface of an alumina-based ceramic substrate containing therein micropores with a size of 5 μm or below having a relative theoretical density of at least 90% or above; (b) then, subjecting said glass coating layer on said substrate to mechanochemically polishing process to render it to have a surface roughness (R z ) of 180 angstroms or less, to contain no more than 50 micropores having a size exceeding 0.2 μm per 100 cm 2 , to be free from strain with a Beilby layer thickness of no more than 50 angstroms, and to have layer thickness in a range of from 3 μm to 200 μm; and (c) further coating the surface of said glass coating layer with a magnetic thin film and protective film.
Claim 20
Dependent Claim
43 words
A process for producing a magnetic recording layer as set forth in claim 17, wherein said glass coating layer is formed by glazing in a thickness, prior to said mechanochemical polishing process, being in a range of from 10 μm to 220 μm.
Claim 21
Dependent Claim
42 words
A process for producing a magnetic recording disc as set forth in claim 17, wherein said glass coating layer is coated by sputtering in a thickness, prior to said mechanochemical polishing, being in a range of from 5 μm to 220 μm.
Claim 22
Dependent Claim
39 words
A process for producing a magnetic recording disc as set forth in claim 17, wherein the thickness of said sputtered glass coating layer prior to said mechanochemical polishing is in a range of from 15 μm to 25 μm.
Claim 23
Dependent Claim
91 words
A process for producing a magnetic recording disc as set forth in claim 17, wherein said mechanochemical polishing is effected with a suspension liquid containing therein at least one kind of substance selected from the group consisting of Fe 2 O 3 , SiO 2 , MgO, CeO 2 and Al 2 O 3 in finely divided powder having a particle diameter of 0.1 μm or below, which is suspended in pure water, and under a lapping pressure in a range of from 0.05 kgf/cm 2 to 2.0 kgf/cm 2 .
References Cited (Backward Citations)
US3198657A
Cited
US3656229A
Cited
US3959553A
Cited
US4046932A
Cited
US4411963A
Cited
US4254189A
Cited
US4396682A
Cited
US4448842A
Cited
US4528212A
Cited
US4608293A
Cited
US4540638A
Cited
US4636420A
Cited
JPS60138730A
Cited
US4659606A
Cited
US4690846A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |