Method of producing porous material having open pores
Assignee: Toto Ltd
•
Filing: 1987-08-21
•
Granted: 1989-05-09
•
Expires: 2007-08-21
Abstract
Abstract A method of producing a porous material having open pores comprises the steps of preparing an emulsion slurry by vigorously agitating a mixture comprising (i) a glycidyl type epoxy resin, (ii) a first hardener selected from the group consisting of modified polyamine hardeners each being prepared by modifying a polyamine hardener with a modifier, amine hardeners and mixtures thereof, (iii) a second hardener selected from the group consisting of polyamide hardeners, (iv) a filler and (v) water, casting said slurry in a water-impermeable mold, and hardening said slurry while it contains water. A large size molded product having a complicated contour and having open pores whose average pore diameter ranges from 0.2 to 10 microns can be produced with high dimensional accuracy.
Inventors
- 👤 Noboru Kishima
- 👤 Akio Matsumoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 14:20
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/16; C08J9/28; C08J9/283; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/50; C08G59/56; C08G59/60; C08J2363/00; Y; Y10; Y10S; Y10S264/00; Y10S264/13
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
125 words
A method of producing a porous material having open pores, comprising the steps of: (a) preparing an emulsion slurry by vigorously aggitating a mixture comprising (i) a glycidyl type epoxy resin, (ii) a first hardener selected from the group consisting of modified polyamine hardeners each being prepared by modifiying a polyamine hardener with a modifier selected from the group consisting of epoxy compounds having one epoxy ring, two epoxy ring or three epoxy rings per molecule, acyrlonitrile and combinations of formaldehyde and a phenolic compound, amine hardeners and mixtures thereof, (iii) a second hardener selected from the group consisting of polyamide hardeners, (iv) a filler and (v) water; (b) casting said slurry in a water-impermeable mold; and (c) hardening said slurry while it contains water.
Claim 2
Independent Claim
125 words
A method of producing a porous material having open pores, comprising the steps of: (a) preparing an emulsion slurry by vigorously aggitating a mixture comprising (i) a glycidyl type epoxy resin, (ii) a first hardener selected from the group consisting of modified polyamine hardeners each being prepared by modifiying a polyamine hardener with a modifier selected from the group consisting of epoxy compounds having one epoxy ring, two epoxy ring or three epoxy rings per molecule, acyrlonitrile and combinations of formaldehyde and a phenolic compound, amine hardeners and mixtures thereof, (iii) a second hardener selected from the group consisting of polyamide hardeners, (iv) a filler and (v) water; (b) casting said slurry in a water-impermeable mold; and (c) hardening said slurry while it contains water.
Claim 3
Dependent Claim
52 words
The method of producing a porous material having open pores according to claim 1, wherein said polyamine hardeners are primary amine hardeners each having at least one primary amine group per molecule, or secondary amine hardeners each having at least one secondary amine group per molecule and having no primary amine group.
Claim 4
Dependent Claim
29 words
The method of producing a porous material having open pores according to claim 1, wherein said modifier is an epoxy compound having at least one epoxy ring per molecule.
Claim 5
Dependent Claim
17 words
The method of producing a porous material pores according to claim 1, wherein said modifier is acrylonitrile.
Claim 6
Dependent Claim
37 words
The method of producing a porous material having open pores according to claim 1, wherein said modifier is a mixture of a phenol and formaldehyde, and each of said modified polyamine hardeners is a Mannich-type reaction product.
Claim 7
Dependent Claim
74 words
The method of producing a porous material having open pores according to claim 1, wherein said amine hardeners are primary amine hardeners each having at least one primary amine group per molecule, or secondary amine hardeners each having at least one secondary amine group per molecule and having no primary amine group, or tertiary amine hardeners each having at least one tertiary amine group per molecule and having no primary and secondary amine group.
Claim 8
Dependent Claim
106 words
The method of producing a porous material having open pores according to claim 1, wherein each of said polyamide hardeners is either: (i) a mixture of (a) an amide compound which is obtained through a reaction between a monomeric fatty acid and an ethyleneamine represented by the formula of H 2 N--(CH 2 --CH 2 --NH) n --H where "n" be 3 to 5, and (b) a polymeric fatty acid polyamide obtained through a reaction of a polymeric fatty acid and said ethyleneamine; or (ii) a reaction mixture obtained by reaction of a mixture of said monomeric fatty acid, said polymeric fatty acid and said ethyleneamine.
Claim 9
Dependent Claim
45 words
The method of producing a porous material having open pores according to claim 1, wherein the mixing ratio of the sum of the modified polyamine hardener and amine hardener to the polyamide hardener is 0.5 to 100 parts by weight to 100 parts by weight.
Claim 10
Dependent Claim
59 words
The method of producing a porous material having open pores according to claim 1, wherein said mixture for forming said emulsion slurry further contains a reactive diluent which lowers the viscosity of said emulsion slurry, a hardening accelerator which acts to accelerate the rate of hardening or to improve the strength of the hardened product and/or a mixture thereof.
Claim 11
Dependent Claim
61 words
The method of producing a porous material having open pores according to claim 1, wherein said modifier of an epoxy compound containing one epoxy ring per molecule is allylglycidyl ether, butylglycidyl ethyer, styrene oxide, ethylene oxide, glycidyl methacrylate, octylene oxide, cyclohexenevinyl monoxide, t-carboxylic acid glycidyl ester, 3-(pentadecyl)phenylglycidyl ether, dipentene monoxide, butylphenylglycidyl ether, pinene oxide, propylene oxide, phenylglycidyl ether or cresylglycidyl ether.
Claim 12
Dependent Claim
52 words
The method of producing a porous material having open pores according to claim 1, wherein said modifier of an epoxy compound having two epoxy rings per molecule is ethyleneglycol diglycidyl ether, neopentylglycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, vinylcyclohexene dioxide, resorcinoldiglycidyl ether, propyleneglycol diglycidyl ether, butadiene oxide, dimethylpentane dioxide or bisphenol-A diglycidyl ether.
Claim 13
Dependent Claim
35 words
The method of producing a porous material having open pores according to claim 1, wherein said modifier of an epoxy compound haivng three epoxy rings per molecule is trimethylolprpoane triglycidyl ether or 2,6-diglycidyl phenylglycidyl ether.
Claim 14
Dependent Claim
68 words
The method of producing a porous material having opening pores according to claim 1, wherein the polyamine of said modified polyamine hardener is an amine selected from the group consisting of diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, iminobispropylamine, bis(hexamethylene)triamine, aminoethylethanolamine, dimethylaminopropylamine, diethylaminopropylamine, methyliminobispropylamine, 1,3-diaminocyclohexane, tetrachloro-p-xylylenediamine, menthenediamine, isophoronediamine, N-aminoethylpiperizine, diaminodiphenyl ether, benzidine, 4,4'-bis(o-toluidine), 4,4'-thiodianiline, m-xylylenediamine, m-phenylenediamine, o-phenylenediamine, dianisidine, methylenebis(o-chloroaniline), 2,4-toluenediamine, bis(3,4-diaminophenyl)sulfone, diaminodiphenylmethane, diaminodiphenylsulfone, diaminoditolysulfone, 2,6-diaminopyridine, 4-chloro-o-phenylenediamine, 4-methoxy-6-methyl-m-phenylenediamine, m-aminobenzylamine, N-methylpiperazine and hydroxyethylpiperazine.
Claim 15
Dependent Claim
81 words
The method of producing a porous material having open pores according to claim 1, wherein the amine hardener ingredient of said first hardener is a member selected from the group consisting of primary amines each having at least one primary amine group per molecule, secondary amines each having at least one secondary amine group per molecule although containing no primary amine group and tertiary amines each having at least one tertiary amine group although having no primary or secondary amine group.
Claim 16
Dependent Claim
33 words
The method of producing a porous material having open pores according to claim 1, wherein said primary amine hardener is diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, diethylaminopropylamine, menthenediamine, N-aminoethylpiperazine, m-xylylenediamine, m-phenylenediamine, o-phenylenediamine, diaminodiphenylmethane, or diaminodiphenylsulfone.
Claim 17
Dependent Claim
26 words
The method of producing a porous material having open pores according to claim 1, wherein said secondary amine hardener is N-methylpiperazine, hydroxyethylpiperazine, piperidine, pyrrolidine or morpholine.
Claim 18
Dependent Claim
33 words
The method of producing a porous material having open pores according to claim 1, wherein said tertiary amine hardner is N,N'dimethylpiperazine, N,N,N',N'-tetramethyl-1,3-butanediamine, pyridine, triethanolamine, dialkylaminoethanol, N-methylmorpholine, hexamethylenetetramine, pyrazine, benzyldimethylamine, 2-(dimethylaminomethyl)phenyl, quinoline or 1-hydroxyethyl-2-heptadecylglyoxalidine.
Claim 19
Dependent Claim
21 words
The method of producing a porous material having open pores according to claim 1, which further comprsiing drying said hardened slurry.
Claim 20
Dependent Claim
38 words
The method of producing a porous material having open pores according to claim 9, wherein said reactive diluent is allyglycidyl ether, butylglycidyl ether, styrene oxide, phenylglycidyl ether, cresylglycidyl ether, ethyleneglycoldiglycidyl ether, neopentylglycoldiglycidyl ether, 1,6-hexanedioldiglycidyl ether or trimethylolpropanetriglycidyl ether.
References Cited (Backward Citations)
US3075932A
Cited
US3057809A
Cited
US3275587A
Cited
US3310529A
Cited
US3705117A
Cited
US3705116A
Cited
US3726819A
Cited
US3634322A
Cited
US3966653A
Cited
US3825506A
Cited
US3914204A
Cited
JPS532464A
Cited
US4480082A
Cited
US4420606A
Cited
US4464485A
Cited
US4594291A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |