Composite structural material with diffusion barrier layer, especially for slide and friction members, and method of manufacture
Assignee: Glyco Metall Werke Glyco BV and Co KG
•
Filing: 1987-01-12
•
Granted: 1989-05-16
•
Expires: 2007-01-12
Abstract
Abstract A composite structural material particularly intended for frictional and slide elements, consisting of a substrate such as a steel layer with a copper- or tin-containing intermediate layer, a tin- or copper-containing functional layer and, between these last two layers, a diffusion barrier layer protecting against diffusion of tin from the functional layer into the intermediate layer or back to the diffusion barrier layer. The diffusion barrier layer consists of a metallic material having a hexagonal crystal lattice, which material is applied by cathodic sputtering, forming a material structure that is densely packed in vacuo with a space filling by metal ions of above 70%. For the cathodic sputtering, conditions of plasma pressure and substrate temperature can be chosen so that recrystallization occurs simultaneously with the formation of the diffusion barrier layer; this makes it possible to achieve the densest hexagonal packing, with a space filling of up to 74%. Pure titanium is the preferred material for the diffusion barrier layer.
Inventors
- 👤 Erich Hodes
- 👤 Klaus Goerke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:14
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/02; C23C14/024; C23C14/025; B; B32; B32B; B32B15/00; B32B15/01; F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/12; F16C33/122; F16C33/127; F16C2204/00; F16C2204/40; F16C2204/42; Y; Y10; Y10S; Y10S384/00; Y10S384/90; Y10S384/912; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12687; Y10T428/12708; Y10T428/12771; Y10T428/12806; Y10T428/12812
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
119 words
Composite structural material, especially for slide and friction members, comprising in combination a substrate layer; an intermediate layer on said substrate layer; a diffusion barrier layer of 0.5 to 5 um thickness on the intermediate layer; characterized in that a functional tin-based friction or slide layer constituted of material selected from the group consisting of tin-containing alloys is applied to the diffusion barrier layer, and further characterized in that the diffusion barrier layer (3) is a material having a hexagonal crystal lattice and is formed in vacuo by cathode sputtering and has a structure characterized by close packing of the voids of the lattice by metal ions, said attice having a space packing above 70% by said metal ions.
Claim 2
Dependent Claim
119 words
Composite structural material, especially for slide and friction members, comprising in combination a substrate layer; an intermediate layer on said substrate layer; a diffusion barrier layer of 0.5 to 5 um thickness on the intermediate layer; characterized in that a functional tin-based friction or slide layer constituted of material selected from the group consisting of tin-containing alloys is applied to the diffusion barrier layer, and further characterized in that the diffusion barrier layer (3) is a material having a hexagonal crystal lattice and is formed in vacuo by cathode sputtering and has a structure characterized by close packing of the voids of the lattice by metal ions, said attice having a space packing above 70% by said metal ions.
Claim 3
Dependent Claim
26 words
Composite structural material in accordance with claim 1, characterized in that the diffusion barrier layer is constituted as a practically voidless, recrystallized hexagonal crystal lattice structure.
Claim 4
Dependent Claim
41 words
Composite structural material according to claim 1, characterized in that the diffusion barrier layer (3) is selected from a material of the group of titanium, zirconium, hafnium, thorium, beryllium, magnesium or from an alloy containing at least one of these metals.
Claim 5
Dependent Claim
21 words
Composite structural material according to claim 1, characterized in that the diffusion barrier layer (3) is constituted essentially soley of titanium.
Claim 6
Dependent Claim
28 words
Composite structural material according to claim 1, characterized in that the functional layer is applied to the diffusion barrier layer by an immediately following cathode sputtering in vacuo.
Claim 7
Dependent Claim
38 words
Composite structural material in accordance with claim 1, wherein said tin-containing alloys are constituted of materials selected from the rroup consisting of SnSb 12 Cu 6 Pb 2 , PbSn 10 Cu 2 , and PbSn 10 .
Claim 8
Dependent Claim
145 words
A process for the preparation of a composite structural material of the type having a substrate layer; an intermediate layer on said substrate layer; a diffusion barrier layer comprising material having a hexagonal crystal lattice, being formed in vacuo by cathode sputtering and having a structure characterized by close packing of the voids of the lattice by metal ions, said lattice having a space packing above 70% by said metal ions; and a functional friction or slide layer on the diffusion barrier layer, formed by the steps of purifying the coated intermediate layer, by pickling of the free surface of the intermediate layer by means of reverse cathode sputtering in vacuo, followed immediately by cathode sputtering from a target the functional layer while maintaining the temperature of the substrate and the pressure of the plasma to match the desired structure of the diffusion barrier layer.
Claim 9
Dependent Claim
145 words
A process for the preparation of a composite structural material of the type having a substrate layer; an intermediate layer on said substrate layer; a diffusion barrier layer comprising material having a hexagonal crystal lattice, being formed in vacuo by cathode sputtering and having a structure characterized by close packing of the voids of the lattice by metal ions, said lattice having a space packing above 70% by said metal ions; and a functional friction or slide layer on the diffusion barrier layer, formed by the steps of purifying the coated intermediate layer, by pickling of the free surface of the intermediate layer by means of reverse cathode sputtering in vacuo, followed immediately by cathode sputtering from a target the functional layer while maintaining the temperature of the substrate and the pressure of the plasma to match the desired structure of the diffusion barrier layer.
Claim 10
Dependent Claim
74 words
Process according to claim 7, characterized in that during the formation of the diffusion barrier layer the temperature of the substrate at least at the start of the diffusion barrier coat is adjusted to the maximum value permissible for the composition of the intermediate layer and the plasma pressure is adjusted to a value corresponding to the minimum electrical current required for anomalous corona discharge upon applying a selected electrical potential to the target.
Claim 11
Dependent Claim
29 words
Process according to claim 7, characterized in that the temperature of the intermediate layer surface to be coated is increased with a progressive build-up of the diffusion barrier layer.
Claim 12
Dependent Claim
45 words
Process according to claim 7, characterized in that a negative electrical voltage is applied to the substrate during the formation of the diffusion barrier layer, which voltage is lower by one order of magnitude than that of the negative electrical voltage applied to the target.
Claim 13
Dependent Claim
30 words
Process according to claim 7, characterized in that the substrate and the diffusion barrier layer that is being formed are heated by infrared irradiation on the side to be coated.
Claim 14
Dependent Claim
41 words
Process according to claim 11, characterized in that the heating of the substrate to the temperature desired at the formation of the diffusion barrier layer is effected by reversed cathode sputtering, thereby to pickle the free surface of the intermediate layer.
Claim 15
Dependent Claim
24 words
Process according to claim 7, characterized in that the formation of the diffusion layer is carried out by cathode sputtering in a magnetic field.
Claim 16
Dependent Claim
40 words
Process according to claim 7, characterized by subjecting the target to plasma which is to be used for the formation of the diffusion barrier layer by cathode sputtering, and subjecting the material contained in the target to a degassing pretreatment.
Claim 17
Dependent Claim
28 words
Process according to claim 14, characterized by subjecting the material contained in the target for the formation of the diffusion barrier layer to a high vacuum degassing pretreatment.
Claim 18
Dependent Claim
120 words
Composite structural material, especially for slide and friction members, comprising in combination a substrate layer; an intermediate layer on said substrate layer; a diffusion barrier layer of 0.5 to 5 um thickness on the intermediate layer; characterized in that a functional tin-based friction or slide layer constituted of material selected from the group consisting of tin-containing dispersion alloys is applied to the diffusion barrier layer and further characterized in that the diffusion barrier layer (3) is a material having a hexagonal crystal lattice and is formed in vacuo by cathode sputtering and has a structure characterized by close packing of the voids of the lattice by metal ions, said lattice having a space packing above 70% by said metal ions.
Claim 19
Dependent Claim
120 words
Composite structural material, especially for slide and friction members, comprising in combination a substrate layer; an intermediate layer on said substrate layer; a diffusion barrier layer of 0.5 to 5 um thickness on the intermediate layer; characterized in that a functional tin-based friction or slide layer constituted of material selected from the group consisting of tin-containing dispersion alloys is applied to the diffusion barrier layer and further characterized in that the diffusion barrier layer (3) is a material having a hexagonal crystal lattice and is formed in vacuo by cathode sputtering and has a structure characterized by close packing of the voids of the lattice by metal ions, said lattice having a space packing above 70% by said metal ions.
Claim 20
Dependent Claim
35 words
Composite structural material in accordance with claim 16, wherein said dispersion alloys are constituted of materials selected from the group consisting of AlSn 6 , AlSn 10 , AlSn 20 , and AlSn 40 .
Claim 21
Dependent Claim
24 words
Composite structural material in accordance with claim 16, wherein said dispersion alloys are constituted of materials selected from the group consisting of AlSn alloys.
References Cited (Backward Citations)
US3911579A
Cited
US4074016A
Cited
US4245008A
Cited
DE2853724A1
Cited
US4404263A
Cited
DE2914618A1
Cited
US4363854A
Cited
US4448854A
Cited
US4591536A
Cited
US4619865A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-15 | 1992-11-14 | 1993-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-15 | 1996-11-14 | 1997-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-15 | 2000-11-14 | 2001-05-16 | $7700.00 | Window Closed / Lapsed |