Process for fabricating a semiconductor device
Assignee: Oki Electric Industry Co Ltd
•
Filing: 1987-09-11
•
Granted: 1989-08-15
•
Expires: 2007-09-11
Abstract
Abstract In a process for fabricating a semiconductor device having a trench at the surface of a semiconductor substrate, a first mask layer is formed to have an opening whose side is set back from an area where the trench will be formed, a second mask layer is formed on the side of the opening of the first mask layer with an opening corresponding to the area where the trench will be formed, and an etching is performed using the first and the second mask layer as a mask to form the trench.
Inventors
- 👤 Jun Kanamori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:33
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/69; H10P50/691; H10P50/693; H10P50/695; H01; H01S; H01S5/00; H01S5/20; H01S5/2054; H01S5/2081
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
181 words
A process for fabricating a semiconductor device which includes a semiconductor substrate having a trench formed at a predetermined area in a surface thereof, said trench having a rounded corner at the surface of said substrate, wherein said process comprises the steps of: (a) forming a first mask layer on said surface of said substrate, said first mask layer having an opening therein with a side spaced from said predetermined area; (b) forming a second mask layer on said side of the opening of said first mask layer, said second mask layer having an opening therein with a side wall substantially aligned with said predetermined area where said trench is to be formed; (c) forming a trench in said substrate at said predetermined area using said first and second mask layers as a mask; (d) removing said second mask layer; and (e) dry etching said substrate at said predetermined area using said first mask layer as a mask, whereby the edge of said trench, which has a higher etching rate than the remainder of said substrate under dry etching, is rounded.
Claim 2
Dependent Claim
181 words
A process for fabricating a semiconductor device which includes a semiconductor substrate having a trench formed at a predetermined area in a surface thereof, said trench having a rounded corner at the surface of said substrate, wherein said process comprises the steps of: (a) forming a first mask layer on said surface of said substrate, said first mask layer having an opening therein with a side spaced from said predetermined area; (b) forming a second mask layer on said side of the opening of said first mask layer, said second mask layer having an opening therein with a side wall substantially aligned with said predetermined area where said trench is to be formed; (c) forming a trench in said substrate at said predetermined area using said first and second mask layers as a mask; (d) removing said second mask layer; and (e) dry etching said substrate at said predetermined area using said first mask layer as a mask, whereby the edge of said trench, which has a higher etching rate than the remainder of said substrate under dry etching, is rounded.
Claim 3
Dependent Claim
18 words
A process according to claim 1, wherein said dry etching step (e) is performed by reactive ion etching.
Claim 4
Dependent Claim
87 words
A process according to claim 1, wherein step (b) of forming said second mask layer comprises the steps of: (b1) unselectively forming a layer of the material of said second mask layer on said first mask layer and on the semiconductor substrate; and (b2) etching said layer of material to remove said unselectively-formed layer except on the side of the opening of said first mask layer, whereby said side wall of said second mask layer remains on the side of the opening in said first mask layer.
Claim 5
Dependent Claim
19 words
A process according to claim 3, wherein said anisotropic etching at step (b2) is performed by reactive ion etching.
Claim 6
Dependent Claim
38 words
A process according to claim 1, wherein said second layer is selectively removable with respect to said first mask layer, said second layer having an etching rate which is substantially higher than that of said first mask layer.
Claim 7
Dependent Claim
15 words
A process according to claim 1, wherein said first mask layer comprises an oxide film.
Claim 8
Dependent Claim
18 words
A process according to claim 1, wherein said trench formed by step (c) is about 4 μm deep.
Claim 9
Dependent Claim
26 words
A process according to claim 1, wherein said dry etching at step (e) is performed until the substrate is etching from about 100 to 1000 Å.
Claim 10
Dependent Claim
40 words
A process according to claim 1, further comprising the steps of: (f) removing said first mask layer; (g) forming an insulator film on the surface of said trench and said substrate; and (h) forming an electrode layer within said trench.
References Cited (Backward Citations)
US4353086A
Cited
US4523369A
Cited
US4577395A
Cited
GB2159326A
Cited
US4534824A
Cited
US4636281A
Cited
US4693781A
Cited
US4707218A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-14 | 1993-02-13 | 1993-08-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-14 | 1997-02-13 | 1997-08-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-14 | 2001-02-13 | 2001-08-15 | $7700.00 | Window Closed / Lapsed |