US4869778A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of forming a patterned aluminum layer and article
Assignee: Gardoc Inc
•
Filing: 1987-07-20
•
Granted: 1989-09-26
•
Expires: 2007-07-20
Abstract
Abstract A process is described for the microdemetalization of an aluminized mylar film, the steps including the printing of a micropattern of a caustic resistant, U.V. curable resin on the aluminum surface, etching of the exposed aluminum with a warm saturated caustic solution, followed immediately by rinsing the patterned surface with an acidic solution to neutralize the caustic and stop the etching. Micropatterns having line widths as small as 0.2 mils may be formed by the process.
Inventors
- 👤 Paul F. Cote
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:20
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/02; H; H05; H05K; H05K3/00; H05K3/02; H05K3/06; H05K3/061; H05K1/00; H05K1/02; H05K1/09; H05K2203/00; H05K2203/07; H05K2203/0779; H05K2203/0786; H05K2203/0789; H05K2203/15; H05K2203/1545
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
202 words
A method for forming a patterned aluminum layer on the top surface of a substrate, the method comprising the steps of: (a) providing a substrate having an aluminum layer on a top surface thereof, (b) forming a patterned masking layer of a caustic resistant material on the aluminum surface, (c) etching the masked aluminum layer by contacting the masked aluminum layer with a caustic etching solution, (d) rinsing the patterned aluminum layer to substantially completely remove the solution and any reaction products of the solution, and (e) drying the patterned aluminum layer, wherein the caustic etching solution contains from about 45 percent to 55 percent by weight of water, remainder sodium hydroxide, and is essentially saturated at a temperature of about 100 to 150 degrees F., and contacts the masked aluminum layer for a time sufficient to substantially completely remove any exposed portions of the masked layer, leaving a patterned aluminum layer on the surface of the substrate underlying the patterned masking layer, and further comprising the step of contacting the resultant patterned surface of the substrate with an acidic solution prior to rinsing and drying to substantially prevent etching of the underlying patterned aluminum layer by undercutting of the masking layer.
Claim 2
Independent Claim
202 words
A method for forming a patterned aluminum layer on the top surface of a substrate, the method comprising the steps of: (a) providing a substrate having an aluminum layer on a top surface thereof, (b) forming a patterned masking layer of a caustic resistant material on the aluminum surface, (c) etching the masked aluminum layer by contacting the masked aluminum layer with a caustic etching solution, (d) rinsing the patterned aluminum layer to substantially completely remove the solution and any reaction products of the solution, and (e) drying the patterned aluminum layer, wherein the caustic etching solution contains from about 45 percent to 55 percent by weight of water, remainder sodium hydroxide, and is essentially saturated at a temperature of about 100 to 150 degrees F., and contacts the masked aluminum layer for a time sufficient to substantially completely remove any exposed portions of the masked layer, leaving a patterned aluminum layer on the surface of the substrate underlying the patterned masking layer, and further comprising the step of contacting the resultant patterned surface of the substrate with an acidic solution prior to rinsing and drying to substantially prevent etching of the underlying patterned aluminum layer by undercutting of the masking layer.
Claim 3
Dependent Claim
14 words
The method of claim 1 in which the masking layer is substantially optically transparent.
Claim 4
Dependent Claim
37 words
The method of claim 1 in which the masking layer is formed by applying a patterned layer of a U.V.-curable resin to the aluminum layer, and irradiating the patterned layer of a U.V.-curable resin with U.V. light.
Claim 5
Dependent Claim
29 words
The method of claim 3 in which the resin composition comprises a diacrylate ester of bisphenol epoxy resin, a difunctional acrylate monomer, a trifunctional acrylate monomer, and a photoinitiator.
Claim 6
Dependent Claim
13 words
The method of claim 2 in which the substrate is substantially optically transparent.
Claim 7
Dependent Claim
19 words
The method of claim 1 in which the acidic solution has a pH of from about 2 to 5.
Claim 8
Dependent Claim
15 words
The method of claim 6 in which the pH is from about 2.5 to 3.5.
Claim 9
Dependent Claim
12 words
The method of claim 7 in which the acid is hydrochloric acid.
Claim 10
Dependent Claim
12 words
The method of claim 6 in which the acid comprises mineral acid.
Claim 11
Dependent Claim
74 words
The method of claim 1 in which the substrate is a continuously moving web, the masking layer is formed by continuously printing a pattern of the caustic resistant material onto the moving aluminum layer, the masked aluminum layer is etched by continuously printing a layer of the caustic solution onto the moving masked aluminum layer, and etching is stopped by continuously printing a layer of the acidic solution onto the moving etched aluminum layer.
Claim 12
Dependent Claim
24 words
The method of claim 10 in which the web is moving at a speed of from about 120 to about 150 feet per minute.
Claim 13
Dependent Claim
19 words
The method of claim 11 in which the thickness of the caustic layer is up to about 2 mils.
Claim 14
Dependent Claim
19 words
The method of claim 11 in which the thickness of the acidic layer is up to about 2 mils.
Claim 15
Dependent Claim
17 words
The method of claim 1 in which the time of etching is up to about 1 second.
Claim 16
Dependent Claim
25 words
The method of claim 14 in which the patterned surface of the substrate is contacted with the acid solution within about 3 seconds after etching.
Claim 17
Dependent Claim
19 words
The method of claim 1 in which the thickness of the masking layer is up to about 0.1 mil.
Claim 18
Dependent Claim
13 words
The method of claim 1 in which the substrate is substantially optically transparent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-25 | 1993-03-27 | 1993-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-25 | 1997-03-27 | 1997-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-25 | 2001-03-27 | 2001-09-26 | $7700.00 | Window Closed / Lapsed |