Thick-film copper conductor inks
Assignee: General Electric Co
•
Filing: 1988-12-02
•
Granted: 1989-10-17
•
Expires: 2008-12-02
Abstract
Abstract Improved copper conductor inks useful in fabricating multilevel circuits are provided. The inks comprise copper powder, a devitrifying glass frit which does not begin to flow until the furnace temperature is above about 700° C., and a suitable organic vehicle. Devitrifying glass frits with these properties include a zinc-calcium-aluminum-silicate glass frit, a zinc-magnesium-barium-aluminum-silicate glass frit, a zinc-magnesium-barium-aluminum-zirconium-phosphosilicate glass frit and mixtures thereof. The inks are advantageous in that they form copper conductor layers having excellent properties without the inclusion of traditional flux materials such as bismuth oxide.
Inventors
- 👤 Ashok N. Prabhu
- 👤 Kenneth W. Hang
- 👤 Edward J. Conlon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 23:48
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092; C; C03; C03C; C03C10/00; C03C10/0036; C03C10/0045; C03C8/00; C03C8/02; C03C8/08; H01; H01B; H01B1/00; H01B1/14; H01B1/16
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
244 words
A copper conductor ink comprising, on a weight basis: (a) from about 65 to about 85 percent of copper powder; (b) from about 5 to about 15 percent of a devitrifying glass frit selected from the group consisting of a zinc-calcium-aluminum-silicate glass frit, a zinc-magnesium-barium-aluminum-silicate glass frit and mixtures thereof, which does not begin to flow until the furnace temperature is above about 700° C., the zinc-calcium-aluminum-silicate glass frit comprising, on a weight basis: (i) from about 7 to about 12 percent of zinc oxide; (ii) from about 25 to about 45 percent of calcium oxide; (iii) from about 10 to about 20 percent of aluminum oxide; (iv) from about 35 to about 50 percent of silicon dioxide; (v) from 0 to about 2 percent of phosphorus pentoxide; and (vi) from 0 to about 5 percent of zirconium silicate; and the zinc-magnesium-barium-aluminum-silicate glass frit comprising, on a weight basis; (i) from about 15 to about 25 percent of zinc oxide; (ii) from about 10 to about 25 percent of magnesium oxide; (iii) from about 3 to about 12 percent of barium oxide; (iv) from about 5 to about 20 percent of aluminum oxide; (v) from about 35 to about 50 percent of silicon dioxide; (vi) from 0 to about 5 percent of phosphorus pentoxide; and (vii) from 0 to about 5 percent of zirconium silicate; and (c) from about 5 to about 25 percent of a solution of at least one resin as binder.
Claim 2
Dependent Claim
244 words
A copper conductor ink comprising, on a weight basis: (a) from about 65 to about 85 percent of copper powder; (b) from about 5 to about 15 percent of a devitrifying glass frit selected from the group consisting of a zinc-calcium-aluminum-silicate glass frit, a zinc-magnesium-barium-aluminum-silicate glass frit and mixtures thereof, which does not begin to flow until the furnace temperature is above about 700° C., the zinc-calcium-aluminum-silicate glass frit comprising, on a weight basis: (i) from about 7 to about 12 percent of zinc oxide; (ii) from about 25 to about 45 percent of calcium oxide; (iii) from about 10 to about 20 percent of aluminum oxide; (iv) from about 35 to about 50 percent of silicon dioxide; (v) from 0 to about 2 percent of phosphorus pentoxide; and (vi) from 0 to about 5 percent of zirconium silicate; and the zinc-magnesium-barium-aluminum-silicate glass frit comprising, on a weight basis; (i) from about 15 to about 25 percent of zinc oxide; (ii) from about 10 to about 25 percent of magnesium oxide; (iii) from about 3 to about 12 percent of barium oxide; (iv) from about 5 to about 20 percent of aluminum oxide; (v) from about 35 to about 50 percent of silicon dioxide; (vi) from 0 to about 5 percent of phosphorus pentoxide; and (vii) from 0 to about 5 percent of zirconium silicate; and (c) from about 5 to about 25 percent of a solution of at least one resin as binder.
Claim 3
Dependent Claim
53 words
A copper ink in accordance with claim 1, wherein the ink comprises, on a weight basis: from about 75 to about 80 percent of the copper powder; from about 6 to about 9 percent of the glass frit; and from about 12 to about 16 percent of the solution of resin as binder.
Claim 4
Dependent Claim
94 words
A copper ink in accordance with claim 1, wherein said zinc-magnesium-barium-aluminum-silicate glass frit comprises, on a weight basis: (a) from about 15 to about 25 percent of zinc oxide; (b) from about 10 to about 25 percent of magnesium oxide; (c) from about 3 to about 12 percent of barium oxide; (d) from about 5 to about 20 percent of aluminum oxide; (e) from about 35 to about 50 percent of silicon dioxide; (f) from 0 to about 0.5 percent of phosphorus pentoxide; and (g) from 0 to about 1 percent of zirconium silicate.
Claim 5
Dependent Claim
230 words
A copper conductor ink comprising, on a weight basis: (a) from about 65 to about 85 percent of copper powder; (b) from about 5 to about 15 percent of a devitrifying glass frit selected from the group consisting of a zinc-calcium-aluminum-silicate glass frit, a zinc-magnesium-barium-aluminum-zirconium-phosphosilicate glass frit and mixtures thereof, the zinc-calcium-aluminum-silicate glass frit comprising, on a weight basis: (i) from about 7 to about 12 percent of zinc oxide; (ii) from about 25 to about 45 percent of calcium oxide; (iii) from about 10 to about 20 percent of aluminum oxide; (iv) from about 25 to about 50 percent of silicon dioxide; (v) from 0 to about 2 percent of phosphorus pentoxide; and (vi) from 0 to about 5 percent of zirconium silicate; and the zinc-magnesium-barium-aluminum-zirconium-phosphosilicate glass frit comprising, on a weight basis; (i) from about 15 to about 25 percent of zinc oxide; (ii) from about 10 to about 25 percent of magnesium oxide; (iii) from about 3 to about 12 percent of barium oxide; (iv) from about 5 to about 20 percent of aluminum oxide; (v) from about 35 to about 50 percent of silicon dioxide; (vi) from about 0.5 to about 3 percent of phosphorus pentoxide; and (vii) from 1 to about 5 percent of zirconium silicate; and (c) from about 5 to about 25 percent of a solution of at least one resin as binder.
Claim 6
Dependent Claim
230 words
A copper conductor ink comprising, on a weight basis: (a) from about 65 to about 85 percent of copper powder; (b) from about 5 to about 15 percent of a devitrifying glass frit selected from the group consisting of a zinc-calcium-aluminum-silicate glass frit, a zinc-magnesium-barium-aluminum-zirconium-phosphosilicate glass frit and mixtures thereof, the zinc-calcium-aluminum-silicate glass frit comprising, on a weight basis: (i) from about 7 to about 12 percent of zinc oxide; (ii) from about 25 to about 45 percent of calcium oxide; (iii) from about 10 to about 20 percent of aluminum oxide; (iv) from about 25 to about 50 percent of silicon dioxide; (v) from 0 to about 2 percent of phosphorus pentoxide; and (vi) from 0 to about 5 percent of zirconium silicate; and the zinc-magnesium-barium-aluminum-zirconium-phosphosilicate glass frit comprising, on a weight basis; (i) from about 15 to about 25 percent of zinc oxide; (ii) from about 10 to about 25 percent of magnesium oxide; (iii) from about 3 to about 12 percent of barium oxide; (iv) from about 5 to about 20 percent of aluminum oxide; (v) from about 35 to about 50 percent of silicon dioxide; (vi) from about 0.5 to about 3 percent of phosphorus pentoxide; and (vii) from 1 to about 5 percent of zirconium silicate; and (c) from about 5 to about 25 percent of a solution of at least one resin as binder.
Claim 7
Dependent Claim
53 words
A copper ink in accordance with claim 4, wherein the ink comprises, on a weight basis: from about 75 to about 80 percent of the copper powder; from about 6 to about 9 percent of the glass frit; and from about 12 to about 16 percent of the solution of resin as binder.
Claim 8
Dependent Claim
78 words
A copper ink in accordance with claim 4, wherein said zinc-calcium-aluminum-silicate glass frit comprises, on a weight basis; from about 8 to about 10 percent of zinc oxide; from about 29 to about 38 percent of calcium oxide; from about 11 to about 18.5 percent of aluminum oxide; from about 37 to about 44 percent of silicon dioxide; from about 0.5 to about 1 percent of phosphorus pentoxide and from about 2 to 3 percent of zirconium silicate.
Claim 9
Dependent Claim
92 words
A copper ink in accordance with claim 4, wherein said zinc-magnesium-barium-aluminum-zirconium-phosphosilicate glass frit comprises: (a) from about 16 to about 22 percent of zinc oxide; (b) from about 16 to about 22 percent of magnesium oxide; (c) from about 5 to about 10 percent of barium oxide; (d) from about 8 to about 11 percent of aluminum oxide; (e) from about 39 to about 43 percent of silicon dioxide; (f) from about 1 to about 2 percent of phosphorus pentoxide; and (g) from about 2 to about 3 percent of zirconium silicate.
References Cited (Backward Citations)
US4808770A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-16 | 1993-04-17 | 1993-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-16 | 1997-04-17 | 1997-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-16 | 2001-04-17 | 2001-10-17 | $7700.00 | Window Closed / Lapsed |