Selective plating by laser ablation
Assignee: TE Connectivity Corp
•
Filing: 1988-04-12
•
Granted: 1989-10-31
•
Expires: 2008-04-12
Abstract
Abstract A method for the selective plating of a metal substrate on which a thin polymeric plating resist is first applied, followed by the selective removal of said resist to expose portions of said substrate to plating, and plating. More particularly, the method hereof includes the steps of selecting a laser wavelength which couples well to the metal substrate, choosing a polymer based plating resist having a low optical coefficient of absorption at said wavelength, curing said resist, subjecting selective areas of said resist to a single excimer laser shot, having a short wavelength, to cause ablative removal of the resist over the selective areas of said substrate, and subjecting said exposed portions of said substrate to metal plating.
Inventors
- 👤 Jeff C. Wu
- 👤 Richard T. Williams
- 👤 John R. Rowlette
- 👤 Charles P. Brooks
- 👤 Richard H. Zimmerman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 13:38
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/34; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1603; C23C18/1605; C23C18/1607; C23C18/1608; C23C18/1612; C23C18/1633; C23C18/1635; C23C18/1637; C23C18/18; C23C18/1803; C23C18/1813; C23C18/182; C23C18/54; C25D5/02; C25D5/022; C25D5/024; H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/243; H05K2201/00; H05K2201/10; H05K2201/10613; H05K2201/10742; H05K2201/10886; H05K2201/10924; H05K3/0011; H05K3/0017; H05K3/0026; H05K3/0032; Y; Y10; Y10S; Y10S430/00; Y10S430/146
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
219 words
In a method for the selective plating of a metal substrate where a think polymeric plating resist is first applied to said substrate, followed by selective laser ablation of said resist to expose portions of said substrate to plating, the improvement comprising in combination therewith the steps of (a) correlating the operating parameters and character of said laser with said resist and said substrate, (i) selecting abating substrate having a low reflectance, at normal incidence of less than about 70%, (ii) selecting a polymer based plating resist for application to said substrate, including but not limited to said portions, and having an optical coefficient of absorption, no greater than about 1000 cm -1 for a 3 micron film thickness, (iii) curing said resist on said substrate, (iiii) subjecting selective areas of said resist to and excimer laser shot, having a wavelength between about 248 to 360 nm, whereby a potion of the laser energy is transmitted through said resist to be absorbed by said substrate, resulting in said metal substrate being heated at the surface thereof to heat and vaporize the adjacent layer of said resist, said vaporized resist expanding causing the solid resist thereover to lift off exposing a clean metal substrate suitable for metal plating, and (b) subjecting said exposed portions of said substrate to metal plating.
Claim 2
Dependent Claim
219 words
In a method for the selective plating of a metal substrate where a think polymeric plating resist is first applied to said substrate, followed by selective laser ablation of said resist to expose portions of said substrate to plating, the improvement comprising in combination therewith the steps of (a) correlating the operating parameters and character of said laser with said resist and said substrate, (i) selecting abating substrate having a low reflectance, at normal incidence of less than about 70%, (ii) selecting a polymer based plating resist for application to said substrate, including but not limited to said portions, and having an optical coefficient of absorption, no greater than about 1000 cm -1 for a 3 micron film thickness, (iii) curing said resist on said substrate, (iiii) subjecting selective areas of said resist to and excimer laser shot, having a wavelength between about 248 to 360 nm, whereby a potion of the laser energy is transmitted through said resist to be absorbed by said substrate, resulting in said metal substrate being heated at the surface thereof to heat and vaporize the adjacent layer of said resist, said vaporized resist expanding causing the solid resist thereover to lift off exposing a clean metal substrate suitable for metal plating, and (b) subjecting said exposed portions of said substrate to metal plating.
Claim 3
Dependent Claim
33 words
The method according to claim 1 characterized in that the selective removal of said resist was achieved by a single laser shot having an energy density of at least 0.60 J/cm 2 .
Claim 4
Dependent Claim
20 words
The method according to claim 2 characterized in that the energy density level is at least 0.90 J/cm 2 .
Claim 5
Dependent Claim
21 words
The method according to claim 3 characterized in that the energy density range is about 0.90 to 2.5 J/cm 2 .
Claim 6
Dependent Claim
42 words
The method according to claim 1 characterized in that at least a first said laser shot is at an energy density level greater than 2.5 J/cm 2 to effect a change in the surface characteristics of said exposed portions of said substrate.
Claim 7
Dependent Claim
23 words
The method according to claim 5 characterized in that said surface change consists of reducing the surface roughness by closing the pores thereof.
Claim 8
Dependent Claim
18 words
The method according to claim 5 characterized in that said surface change consists of cleaning the surface thereof.
Claim 9
Dependent Claim
19 words
The method according to claim 5 characterized in that said surface change consists in the polishing of said surface.
Claim 10
Dependent Claim
29 words
The method according to claim 1 characterized in that said polymeric coating is applied by a process selected from the group consisting of screening, spraying, dipping, printing and electroplating.
Claim 11
Dependent Claim
16 words
The method according to claim 10 characterized in that said resist is a styrene acrylic copolymer.
Claim 12
Dependent Claim
26 words
The method according to claim 1 characterized in that said plating substrate is selected from a group consisting of nickel, nickel alloys, copper and copper alloys.
Claim 13
Dependent Claim
205 words
In a method for preparing a metal substrate for plating on selective areas thereof, where a thin polymeric plating resist is first applied to said substrate followed by selective laser ablation of said resist to expose said areas of said substrate for plating, the improvement comprising in combination therewith the steps of correlating the operating parameters and character of said laser with said resist and said substrate, (i) selecting a plating substrate having a low reflectance, at normal incidence of less than about 70%, (ii) selecting a polymer based plating resist for application to said substrate, including but not limited to said areas, and having an optical coefficient of absorption, no greater than about 1000 cm -1 for a 3 micron film thickness, (iii) subjecting said selective areas of the resist to an excimer laser shot, having a wavelength between about 248 to 360 nm, whereby a portion of the laser energy is transmitted through said resist to be absorbed by said substrate, resulting in said metal substrate being heated at the surface thereof to heat and vaporize the adjacent layer of said resist, said vaporized resist expanding causing the solid resist thereover to life off exposing a clean metal substrate suitable for metal plating.
Claim 14
Dependent Claim
205 words
In a method for preparing a metal substrate for plating on selective areas thereof, where a thin polymeric plating resist is first applied to said substrate followed by selective laser ablation of said resist to expose said areas of said substrate for plating, the improvement comprising in combination therewith the steps of correlating the operating parameters and character of said laser with said resist and said substrate, (i) selecting a plating substrate having a low reflectance, at normal incidence of less than about 70%, (ii) selecting a polymer based plating resist for application to said substrate, including but not limited to said areas, and having an optical coefficient of absorption, no greater than about 1000 cm -1 for a 3 micron film thickness, (iii) subjecting said selective areas of the resist to an excimer laser shot, having a wavelength between about 248 to 360 nm, whereby a portion of the laser energy is transmitted through said resist to be absorbed by said substrate, resulting in said metal substrate being heated at the surface thereof to heat and vaporize the adjacent layer of said resist, said vaporized resist expanding causing the solid resist thereover to life off exposing a clean metal substrate suitable for metal plating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-30 | 1993-05-01 | 1993-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-30 | 1997-05-01 | 1997-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-30 | 2001-05-01 | 2001-10-31 | $7700.00 | Window Closed / Lapsed |