Fiber-reinforced silicon nitride composite ceramics
Assignee: Saint Gobain Abrasives Inc
•
Filing: 1986-11-26
•
Granted: 1989-12-05
•
Expires: 2006-11-26
Abstract
Abstract Tough composites of polymer derived silicon carbide fibers in silicon nitride matrices, especially reaction bonded silicon nitride matrices, can be made by precoating the fibers with pyrolytic carbon and controlling the nitridation or other process which forms the silicon nitride matrix so that a thickness of at least 5 nanometers of carbon remains in the composite after it is formed. Failure of such composites is non-catastrophic. Alternatively, with at least some specific types of polymer derived silicon carbide fibers, composites with non-catastrophic failure can be made by controlling the nitriding conditions to produce an essentially void space around the fibers in the final composites. As still another alternative, the space around the fibers may be partially filled with silicon nitride whiskers generated during the nitridation process.
Inventors
- 👤 Normand D. Corbin
- 👤 Craig A. Willkens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 04:50
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/591; C04B35/622; C04B35/626; C04B35/62605; C04B35/62625; C04B35/6263; C04B35/6264; C04B35/628; C04B35/62844; C04B35/62847; C04B35/62852; C04B35/62857; C04B35/6286; C04B35/62863; C04B35/62865; C04B35/62868; C04B35/62871; C04B35/62873; C04B35/62897; C04B35/71; C04B35/78; C04B35/80; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/42; C04B2235/428; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/524; C04B2235/5244; C04B2235/526; C04B2235/5264; C04B2235/5276; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/70; C04B2235/96; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24058; Y10T428/24124; Y10T428/24132; Y10T428/24942; Y10T428/249921; Y10T428/249924; Y10T428/249928; Y10T428/249929; Y10T428/249953; Y10T428/249967; Y10T428/249969; Y10T428/249986; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
161 words
A fiber reinforced composite, comprising: (a) from 20-80% by volume of reinforcing silicon carbide ceramic fibers at least one millimeter in average length, said fibers collectively having sufficient tensile strength to bear the load on said composite at the point of matrix failure without fiber tensile failure, said fibers having a diameter between 8 and 25 microns; (b) crack deflection zones, having mechanical properties substantially different from those of both the matrix and the reinforcing fibers of the composite, occupying a predominant portion of the space in the order of 1 micron thick around said reinforcing fibers; and (c) a matrix comprising predominantly reaction bonded silicon nitride, said composite having non-catastrophic failure under mechanical stress, wherein said reinforcing fibers consist predominantly of silicon carbide derived from decomposition of organosilicon polymers, and wherein said crack deflection zones are comprised predominantly of a material with its most probable direction of slip under mechanical stress substantially parallel to the surfaces of said reinforcing fibers.
Claim 2
Dependent Claim
161 words
A fiber reinforced composite, comprising: (a) from 20-80% by volume of reinforcing silicon carbide ceramic fibers at least one millimeter in average length, said fibers collectively having sufficient tensile strength to bear the load on said composite at the point of matrix failure without fiber tensile failure, said fibers having a diameter between 8 and 25 microns; (b) crack deflection zones, having mechanical properties substantially different from those of both the matrix and the reinforcing fibers of the composite, occupying a predominant portion of the space in the order of 1 micron thick around said reinforcing fibers; and (c) a matrix comprising predominantly reaction bonded silicon nitride, said composite having non-catastrophic failure under mechanical stress, wherein said reinforcing fibers consist predominantly of silicon carbide derived from decomposition of organosilicon polymers, and wherein said crack deflection zones are comprised predominantly of a material with its most probable direction of slip under mechanical stress substantially parallel to the surfaces of said reinforcing fibers.
Claim 3
Dependent Claim
20 words
A composite according to claim 1, wherein said silicon carbide is derived predominantly from the decomposition of methyl poly(disilyl azane).
Claim 4
Dependent Claim
39 words
A composite according to claim 1, wherein said crack deflection zones are comprised predominantly of a material selected from the group consisting of carbon, boron nitride, and polytype 2H(d), 27R, 16H, 21R, 12H, and 32H of the aluminum-nitrogen-silicon-oxygen system.
Claim 5
Dependent Claim
19 words
A composite according to claim 3, wherein said crack deflection zones are composed predominantly of laminar deposited pyrolytic carbon.
Claim 6
Dependent Claim
20 words
A composite according to claim 2, wherein said crack deflection zones have at least half their volume as empty space.
Claim 7
Dependent Claim
15 words
A composite according to claim 1, wherein said crack deflection zones comprise silicon nitride whiskers.
Claim 8
Dependent Claim
25 words
A composite according to claim 6 having a maximum load bearing capacity of at least 350 mega-pascals at a fiber strain of a least 0.3%.
Claim 9
Dependent Claim
25 words
A composite according to claim 5 having a maximum load bearing capacity of at least 350 mega-pascals at a fiber strain of at least 0.3%.
Claim 10
Dependent Claim
25 words
A composite according to claim 4 having a maximum load bearing capacity of at least 350 mega-pascals at a fiber strain of at least 0.3%.
Claim 11
Dependent Claim
25 words
A composite according to claim 3 having a maximum load bearing capacity of at least 350 mega-pascals at a fiber strain of at least 0.3%.
Claim 12
Dependent Claim
25 words
A composite according to claim 1 having a maximum load bearing capacity of at least 350 mega-pascals at a fiber strain of at least 0.3%.
Claim 13
Dependent Claim
25 words
A composite according to claim 2 having a maximum load bearing capacity of at least 350 mega-pascals at a fiber strain of at least 0.3%.
Claim 14
Dependent Claim
25 words
A composite according to claim 3 having a maximum load bearing capacity of at least 350 mega-pascals at a fiber strain of at least 0.3%.
Claim 15
Dependent Claim
25 words
A composite according to claim 4 having a maximum load bearing capacity of at least 350 mega-pascals at a fiber strain of at least 0.3%.
References Cited (Backward Citations)
US3222438A
Cited
US3462340A
Cited
US3833389A
Cited
US4100233A
Cited
US4158687A
Cited
US4335217A
Cited
US4324843A
Cited
US4463058A
Cited
US4738902A
Cited
US4589900A
Cited
US4543345A
Cited
US4642271A
Cited
US4650775A
Cited
US4689188A
Cited
US4781993A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-04 | 1993-06-05 | 1993-12-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-04 | 1997-06-05 | 1997-12-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-04 | 2001-06-05 | 2001-12-05 | $7700.00 | Window Closed / Lapsed |