Thick, impact resistant antireflection coatings for IR transparent optical elements
Assignee: Raytheon Co
•
Filing: 1987-11-20
•
Granted: 1990-03-13
•
Expires: 2007-11-20
Abstract
Abstract An impact resistant antireflection coating for an optical element which mitigates damage to the optical element when an air flight system having the optical element is flown through a high velocity droplet impact medium is described. The coating comprises a material having a relatively high modulus of elasticity compared to the modulus of elasticity of the material of the optical element. The coating is deposited to a half wavelength thickness at a wavelength which must be maximally transmitted through the optical element. A quarter wavelength antireflection coating layer at the wavelength which must be maximally transmitted through the optical element is then disposed over the impact protection coating layer. The material of the antireflection coating is preferably of a high modulus of elasticity material having a refractive index which is intermediate the refractive index of the material of the base layer and the medium through which the airborne system is flown.
Inventors
- 👤 Randal W. Tustison
- 👤 Dennis G. Montanari
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 20:16
CPC Classifications
G02B1/105; G; G02; G02B; G02B1/00; G02B1/10; G02B1/11; G02B1/113; G02B1/115; G02B1/14
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
155 words
An optical element comprising: a base comprising a first material having a first predetermined optical transmissivity over a predetermined range of optical wavelengths, and a first predetermined modulus of elasticity; a composite layer disposed on said base layer to protect said base layer from liquid impact erosion comprising: a first layer of a second, different material having a second substantially higher modulus of elasticity than the modulus of elasticity of the first material, said layer having an optical thickness of about (2N+1)λ/2, where λ is a wavelength within the predetermined range of optical wavelengths of the first material of the base and N is an integer; and a second layer of a third, different material having a third modulus of elasticity which is substantially higher than the modulus of elasticity of the first material, a index of refraction at the wavelength selected to antireflection correct the optical element, and an optical thickness of about (λ/4).
Claim 2
Dependent Claim
155 words
An optical element comprising: a base comprising a first material having a first predetermined optical transmissivity over a predetermined range of optical wavelengths, and a first predetermined modulus of elasticity; a composite layer disposed on said base layer to protect said base layer from liquid impact erosion comprising: a first layer of a second, different material having a second substantially higher modulus of elasticity than the modulus of elasticity of the first material, said layer having an optical thickness of about (2N+1)λ/2, where λ is a wavelength within the predetermined range of optical wavelengths of the first material of the base and N is an integer; and a second layer of a third, different material having a third modulus of elasticity which is substantially higher than the modulus of elasticity of the first material, a index of refraction at the wavelength selected to antireflection correct the optical element, and an optical thickness of about (λ/4).
Claim 3
Dependent Claim
79 words
The optical element as recited in claim 1 wherein the first material of the base is selected from the group consisting of zinc sulfide, zinc selenide, gallium arsenide, gallium phosphide, mercury cadmium telluride, and cadmium telluride and a ternary sulfide having the general chemical formula MN 2 S 4 , where M is a cation selected from the Group 1A elements, N is a cation selected from lanthanide where erred seried elements, and S is a sulfide cation S2-.
Claim 4
Dependent Claim
36 words
The optical element as recited in claim 2 wherein the second material of the first layer is selected from the group consisting of hard carbon, diamond, and cerium oxide, titanium oxide, zirconium oxide, and mixtures thereof.
Claim 5
Dependent Claim
39 words
The optical element as recited in claim 3 wherein the third material of the second layer is selected from the group consisting of yttrium oxide, scandium oxide, magnesium oxide, and mixtures of yttrium oxide, scandium oxide, and magnesium oxide.
Claim 6
Dependent Claim
163 words
An optical element having an impact resistant antireflection coating layer disposed over at least a surface thereof which is resistant to high velocity water droplet impact comprises: a base layer of a material selected from the group consisting of zinc sulfide and zinc selenide, said base having a predetermined optical transmissivity over the optical wavelength range of at least 8 microns to 12 microns; and a composite layer disposed over said base layer which provides the impact resistant antireflection coating for the optical element comprising: a first layer comprising a material selected from the group consisting of hard carbon, cerium oxide, titanium oxide, zirconium oxide, and mixtures thereof having an optical thickness of about (2N+1)λ/2, where λ is a wavelength within the predetermined wavelength range of the base, and N is an integer; and a second layer comprising a material selected from the group consisting of yttrium oxide, scandium oxide, and mixtures thereof, including magnesium oxide having an optical thickness of about (λ/4).
Claim 7
Dependent Claim
163 words
An optical element having an impact resistant antireflection coating layer disposed over at least a surface thereof which is resistant to high velocity water droplet impact comprises: a base layer of a material selected from the group consisting of zinc sulfide and zinc selenide, said base having a predetermined optical transmissivity over the optical wavelength range of at least 8 microns to 12 microns; and a composite layer disposed over said base layer which provides the impact resistant antireflection coating for the optical element comprising: a first layer comprising a material selected from the group consisting of hard carbon, cerium oxide, titanium oxide, zirconium oxide, and mixtures thereof having an optical thickness of about (2N+1)λ/2, where λ is a wavelength within the predetermined wavelength range of the base, and N is an integer; and a second layer comprising a material selected from the group consisting of yttrium oxide, scandium oxide, and mixtures thereof, including magnesium oxide having an optical thickness of about (λ/4).
Claim 8
Dependent Claim
30 words
The optical element as recited in claim 5 wherein the first layer of the composite layer is cerium oxide and the second layer of the composite layer is yttrium oxide.
Claim 9
Dependent Claim
38 words
The optical element as recited in claim 5 wherein the second material comprising the first layer of the composite layer is selected from the group consisting of hard carbon, cerium oxide, titanium oxide, zirconium oxide, and mixtures thereof.
Claim 10
Dependent Claim
31 words
The optical element as recited in claim 7 wherein the material of the second layer is selected from the group consisting of yttrium oxide, scandium oxide, magnesium oxide, and mixtures thereof.
Claim 11
Dependent Claim
184 words
An optical element having an impact resistant antireflection coating layer disposed over at least a surface thereof which is resistant to high velocity water droplet impact comprises: a base layer of a material selected from the group consisting of zinc sulfide and zinc selenide, said base having a predetermined optical transmissivity over the optical wavelength range of at least 8 microns to 12 microns; and an adhesion layer disposed on the base layer having an optical thickness of about 10 Å to 1000 Å; a composite layer disposed over said adhesion layer which provides the impact resistant antireflection coating for the optical element comprising: a first layer comprising a material selected from the group consisting of hard carbon, cerium oxide, titanium oxide, zirconium oxide, and mixtures thereof having an optical thickness of about (2N+1)λ/2, where λ is a wavelength within the predetermined wavelength range of the base, and N is an integer; and a second layer comprising a material selected from the group consisting of yttrium oxide, scandium oxide, and mixtures thereof with magnesium oxide said second having an optical thickness of about (λ/4).
Claim 12
Dependent Claim
184 words
An optical element having an impact resistant antireflection coating layer disposed over at least a surface thereof which is resistant to high velocity water droplet impact comprises: a base layer of a material selected from the group consisting of zinc sulfide and zinc selenide, said base having a predetermined optical transmissivity over the optical wavelength range of at least 8 microns to 12 microns; and an adhesion layer disposed on the base layer having an optical thickness of about 10 Å to 1000 Å; a composite layer disposed over said adhesion layer which provides the impact resistant antireflection coating for the optical element comprising: a first layer comprising a material selected from the group consisting of hard carbon, cerium oxide, titanium oxide, zirconium oxide, and mixtures thereof having an optical thickness of about (2N+1)λ/2, where λ is a wavelength within the predetermined wavelength range of the base, and N is an integer; and a second layer comprising a material selected from the group consisting of yttrium oxide, scandium oxide, and mixtures thereof with magnesium oxide said second having an optical thickness of about (λ/4).
Claim 13
Dependent Claim
31 words
The optical element as recited in claim 9 wherein the adhesion layer is yttrium oxide and the first layer is a hard carbon layer, and the second layer is yttrium oxide.
Claim 14
Dependent Claim
34 words
The optical element as recited in claim 9 wherein the material of the composite layer is selected from the group consisting of hard carbon, cerium oxide, zirconium oxide, and titanium oxide and mixtures thereof.
Claim 15
Dependent Claim
28 words
The optical element as recited in claim 11 wherein the third material is selected from the group consisting of yttrium oxide, scandium oxide, magnesium oxide, and mixtures thereof.
Claim 16
Independent Claim
145 words
A method of protecting an optical element from damage caused by water droplet impact comprises the steps of: providing the optical element having a base comprised of a first material having a first predetermined optical transmissivity over a predetermined range of optical wavelengths providing a first layer of a second material having a second substantially higher modulus of elasticity than the modulus of elasticity of the first material, said layer having an optical thickness of about (2N+1)λ/2, where λ is a wavelength within the predetermined range of optical wavelengths of the first material of the base, and N is an integer, and providing a second layer comprising a third material having a third substantially higher modulus of elasticity than the modulus of elasticity of the first material, an index of refraction selected to antireflection correct the optical element, and an optical thickness of about (λ/4).
Claim 17
Independent Claim
145 words
A method of protecting an optical element from damage caused by water droplet impact comprises the steps of: providing the optical element having a base comprised of a first material having a first predetermined optical transmissivity over a predetermined range of optical wavelengths providing a first layer of a second material having a second substantially higher modulus of elasticity than the modulus of elasticity of the first material, said layer having an optical thickness of about (2N+1)λ/2, where λ is a wavelength within the predetermined range of optical wavelengths of the first material of the base, and N is an integer, and providing a second layer comprising a third material having a third substantially higher modulus of elasticity than the modulus of elasticity of the first material, an index of refraction selected to antireflection correct the optical element, and an optical thickness of about (λ/4).
Claim 18
Dependent Claim
36 words
The method as recited in claim 13 wherein the first material of the composite layer is selected from the group of materials consisting of hard carbon, diamond, cerium oxide, titanium oxide, zirconium oxide, and mixtures thereof.
Claim 19
Dependent Claim
31 words
The method as recited in claim 13 wherein the third material of the second layer is selected from the group consisting of yttrium oxide, scandium oxide, magnesium oxide, and mixtures thereof.
Claim 20
Dependent Claim
118 words
The method as recited in claim 13 wherein the second material of the first layer is selected from the group consisting hard carbon and cerium oxide, and the third material of the second layer is selected from the group consisting of yttrium oxide and scandium oxide, and wherein the base material is selected from the group of materials consisting of zinc sulfide, zinc selenide, germanium, gallium arsenide, gallium phosphide, mercury cadmium telluride, and cadmium telluride, and a ternary sulfide having the general chemical formula Mn.sub.2 S.sub.4 where M is a cation selected from the group 1A elements, n is a cation selected from the lanthanide rare earth series elements, and S is a sulfide cation S 2- .
References Cited (Backward Citations)
CH292125A
Cited
US2758510A
Cited
US3432225A
Cited
EP0049032A1
Cited
GB2105371A
Cited
US4498728A
Cited
US4461750A
Cited
GB2165266A
Cited
US4476156A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-12 | 1993-09-11 | 1994-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-12 | 1997-09-11 | 1998-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-12 | 2001-09-11 | 2002-03-13 | $7700.00 | Window Closed / Lapsed |