Yarns and tows comprising high strength metal coated fibers, process for their production, and articles made therefrom
Assignee: MIDDLETON ROBERT W MR
•
Filing: 1988-07-07
•
Granted: 1990-03-20
•
Expires: 2008-07-07
Abstract
Abstract Yarns or tows of high strength composite fibers the majority of which comprise a core of carbon or the like and a thin, uniform firmly adherent electrically conductive layer or an electrodepositable metal, such as nickel or the like, the bond strength of the metal to the core being greater than 10 percent of the intermetallic bond strength of the metal layer. The composites can be produced by electrodeposition from a bath onto the core but the procedure must use external voltages high enough both (i) to dissociate the metal at the core and (ii) to nucleate the metal through the boundary layer into direct contact with the core.
Inventors
- 👤 Louis G. Morin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:52
CPC Classifications
F; F41; F41J; F41J2/00; D; D01; D01F; D01F11/00; D01F11/10; D01F11/12; D01F11/127; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12486; Y10T428/12493; Y10T428/12535; Y10T428/12625; Y10T428/29; Y10T428/2913; Y10T428/2918; Y10T428/2933; Y10T428/2938; Y10T442/00; Y10T442/30; Y10T442/3382; Y10T442/339; Y10T442/40; Y10T442/475
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
150 words
A process for the production of continuous yarns or tows of high strength composite fibers, said process comprising: (a) providing a continuous length of a plurality of electrically conductive graphite core fibers, (b) continuously immersing at least a portion of the length of said fibers in a bath capable of electrolytically depositing at least one metal, (c) applying an external voltage of at least 10 volts to the fiber immediately prior to immersion in the bath; (d) maintaining said voltage and resulting current for a time sufficient to produce a thin, uniform, firmly adherent, electrically conductive layer of electrolytically deposited metal on said core; and (e) maintaining the yarns or tows cool enough outside the bath to prevent degradation of the said fibers by recycling the bath to bathe the yarns or tows from the point of application of the external voltage to the point of immersion in the bath.
Claim 2
Dependent Claim
150 words
A process for the production of continuous yarns or tows of high strength composite fibers, said process comprising: (a) providing a continuous length of a plurality of electrically conductive graphite core fibers, (b) continuously immersing at least a portion of the length of said fibers in a bath capable of electrolytically depositing at least one metal, (c) applying an external voltage of at least 10 volts to the fiber immediately prior to immersion in the bath; (d) maintaining said voltage and resulting current for a time sufficient to produce a thin, uniform, firmly adherent, electrically conductive layer of electrolytically deposited metal on said core; and (e) maintaining the yarns or tows cool enough outside the bath to prevent degradation of the said fibers by recycling the bath to bathe the yarns or tows from the point of application of the external voltage to the point of immersion in the bath.
Claim 3
Dependent Claim
18 words
A process as defined in claim 1 wherein the applied external voltage is between 10 and 50 volts.
Claim 4
Dependent Claim
18 words
A process as defined in claim 2 wherein the applied external voltage is between 12 and 36 volts.
Claim 5
Dependent Claim
18 words
A process as defined in claim 3 wherein the applied external voltage is in excess of 13.0 volts.
Claim 6
Dependent Claim
75 words
A process as defined in claim 1 wherein the bond strength of said layer to said core in the majority of said fibers is at least sufficient to provide that when the composite fiber is bent sharply enough to break the coating on the tension side of the bend because its elastic limit is exceeded, the coating on the compression side of the bend will remain bonded to the core and will not crack circumferentially.
Claim 7
Dependent Claim
14 words
A process as defined in claim 1 wherein said electrolytically deposited metal is crystalline.
Claim 8
Dependent Claim
39 words
A process as defined in claim 1 wherein the product of the process is a tow or yarn of composite fibers which can be knotted without separation of the layer of metal or portions thereof from the core fibers.
Claim 9
Dependent Claim
33 words
A process as defined in claim 1 including the step of weaving or knitting yarns produced by the process alone, or in combination with yarns of a different material in to a fabric.
Claim 10
Dependent Claim
33 words
A process as defined in claim 1 including the step of laying up the yarns produced by the process alone, or in combination with yarns or a different material into a non-woven sheet.
Claim 11
Dependent Claim
25 words
A process as defined in either of claims 8 or 9 including weaving, knitting or laying up the material into a three-dimensional article of manufacture.
Claim 12
Dependent Claim
21 words
A process as defined in claim 1 including the step of chopping the yarns produced by the process into shortened lengths.
Claim 13
Dependent Claim
43 words
A process as defined in any of claims 8, 9 or 11 including the step of forming a reinforced composite by intimately contacting a metal or an organic polymer material with at least a reinforcing amount of said yarn, sheet or chopped fibers.
Claim 14
Dependent Claim
10 words
A reinforced composite prepared by the process of claim 12.
Claim 15
Dependent Claim
30 words
A reinforced composite prepared by the process of claim 12 wherein the amount of yarn, sheet or chopped fibers is at least sufficient to provide an electrostatically shielded reinforced composite.
Claim 16
Dependent Claim
17 words
A single fiber recovered from a continuous yarn or tow produced by the process of claim 1.
References Cited (Backward Citations)
US3107152A
Cited
GB1215002A
Cited
US3550247A
Cited
US3473900A
Cited
US3622283A
Cited
FR1535660A
Cited
US3495940A
Cited
GB1208959A
Cited
US3535093A
Cited
GB1272777A
Cited
GB1309252A
Cited
US3571901A
Cited
US3671285A
Cited
US3896010A
Cited
US3807996A
Cited
US4050997A
Cited
US3953647A
Cited
SU496331A1
Cited
US4132828A
Cited
US4096823A
Cited
US4169911A
Cited
US4201825A
Cited
DE3108380A1
Cited
US4341823A
Cited
US4357985A
Cited
US4367127A
Cited
JPS59106571A
Cited
JPH05243770A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-19 | 1993-09-18 | 1994-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-19 | 1997-09-18 | 1998-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-19 | 2001-09-18 | 2002-03-20 | $7700.00 | Window Closed / Lapsed |