Method for producing titanium fluoride
Assignee: JFE Engineering Corp
•
Filing: 1988-11-25
•
Granted: 1990-04-17
•
Expires: 2008-11-25
Abstract
Abstract A method for producing titanium fluoride comprises: a dissolution process, wherein iron-containing titanium material is dissolved in solutions containing hydrofluoric acid, fluoride solutions being produced; a first crystallization and separation process, wherein ferric fluoride is crystallized and ferric fluoride crystals thus obtained are separated from the fluoride solutions by cooling the fluoride solutions, crude titanium fluoride solutions being produced; a second crystallization and separation process, wherein a mixed salt of (NH 4 ) 2 TiF 6 and (NH) 3 FeF 6 is crystallized and separated by mixing ammonium fluoride solutions with the crude titanium fluoride solutions to obtain a mixture and concentrating the mixture; a first pyrolysis process, wherein the ammonium fluoride salt is pyrolyzed at a temperature of from 300° to 800° C. in a stream of dry gas after having dried the ammonium fluoride, solid ferric fluoride (FeF 3 ) and gaseous TF 4 , HF and NH 3 being produced; a condensation and separation process, wherein the gaseous TiF 4 , HF and NH 3 are condensed at a temperature of from 20° to 280° C. and followed by the TiF 4 separation of solid.
Inventors
- 👤 Keisuke Nakahara
- 👤 Hideyuki Yoshikoshi
- 👤 Toshio Hinami
- 👤 Takaho Kawawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:49
CPC Classifications
C; C22; C22B; C22B34/00; C22B34/10; C22B34/12; C22B34/1218; C22B34/1222; C01; C01G; C01G23/00; C01G23/02; C01G23/028; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
179 words
A method for producing titanium fluoride, comprising the sequential steps of: (1) dissolving iron-containing titanium material in a hydrofluoric acid solution to produce a fluoride solution; (2) crystallizing ferric fluoride in the fluoride solution followed by separation from the fluoride solution of the ferric fluoride crystals thus obtained by cooling the fluoride solution to produce a crude titanium fluoride solution; (3) crystallizing and separating a mixed salt of (NH 4 ) 2 TiF 6 and (NH 4 ) 3 FeF 6 by mixing an ammonium fluoride solution with the crude titanium fluoride solution followed by concentrating said mixture; (4) drying said mixed salt and pyrolyzing said mixed salt at a temperature of from 300° to 800° C. in a stream of dry gas to produce solid ferric fluoride (FeF 3 ) and gaseous mixture of TF 4 , HF and NH 3 ; and (5) condensing the gaseous TiF 4 , HF and NH 3 at a temperature of from 20° to 280° C. to produce solid TiF 4 which is separated from gaseous HF and NH 3 .
Claim 2
Independent Claim
179 words
A method for producing titanium fluoride, comprising the sequential steps of: (1) dissolving iron-containing titanium material in a hydrofluoric acid solution to produce a fluoride solution; (2) crystallizing ferric fluoride in the fluoride solution followed by separation from the fluoride solution of the ferric fluoride crystals thus obtained by cooling the fluoride solution to produce a crude titanium fluoride solution; (3) crystallizing and separating a mixed salt of (NH 4 ) 2 TiF 6 and (NH 4 ) 3 FeF 6 by mixing an ammonium fluoride solution with the crude titanium fluoride solution followed by concentrating said mixture; (4) drying said mixed salt and pyrolyzing said mixed salt at a temperature of from 300° to 800° C. in a stream of dry gas to produce solid ferric fluoride (FeF 3 ) and gaseous mixture of TF 4 , HF and NH 3 ; and (5) condensing the gaseous TiF 4 , HF and NH 3 at a temperature of from 20° to 280° C. to produce solid TiF 4 which is separated from gaseous HF and NH 3 .
Claim 3
Dependent Claim
35 words
The method of claim 1, further comprising an oxidation step, wherein divalent iron-ion in the fluoride solution is oxidized into trivalent iron-ion by blowing an oxidizing agent into the fluoride solution obtained in step 1.
Claim 4
Dependent Claim
50 words
The method of claim 1, further comprising a second pyrolysis step, wherein the ferric fluoride crystals obtained in step 2 and the ferric fluoride obtained in step 4 are hydrolyzed at a temperature of from 600° to 1000° C. to produce iron oxide (Fe 2 O 3 ) and HF.
Claim 5
Dependent Claim
50 words
The method of claim 1, wherein the ammonium fluoride solution to be mixed in step 3 include solutions which are produced by absorbing the HF and NH 3 gases obtained in step 5 in ammonium fluoride solutions containing a dissolved portion of the ammonium fluoride salt obtained in step 3.
Claim 6
Dependent Claim
25 words
The method of claim 1, wherein the dissolution of titanium material in step 1 is at a reaction temperature of from 60° to 90° C.
Claim 7
Dependent Claim
25 words
The method of claim 1, wherein the cooling of the fluoride solution in step 2 is at a temperature of from 0° to 20° C.
Claim 8
Dependent Claim
50 words
The method of claim 1, wherein step 3 further includes mixing an ammonium fluoride solution with said crude titanium fluoride solution followed by evaporating and concentrating the mixture to crystallize and separate a mixed salt of (NH 4 ) 2 TIF 6 and (NH 4 ) 3 FeF 6 .
Claim 9
Dependent Claim
50 words
The method of claim 1, wherein step 3 further includes mixing an ammonium fluoride solution with said crude titanium fluoride solution followed by evaporating and cooling the mixture to crystallize and separate a mixed salt of (NH 4 ) 2 TiF 6 and (NH 4 ) 3 FeF 6 .
Claim 10
Dependent Claim
38 words
The method of claim 1, wherein step 4 is conducted at a temperature of from 400° to 600° C. in a stream of dry gas selected from the group consisting of dry nitrogen, dry air and dry argon.
Claim 11
Dependent Claim
19 words
The method of claim 1, wherein step 5 is conducted at a temperature of from 50° to 100° C.
Claim 12
Independent Claim
90 words
A method for producing titanium fluoride comprising the sequential steps of: (1) dissolving iron-containing titanium material in a hydrofluoric acid solution to produce a fluoride solution; (2) crystallizing ferric fluoride in the fluoride solution followed by separating from the fluoride solution the ferric fluoride crystals thus obtained to produce a crude titanium fluoride solution; (3) crystallizing a mixed salt of (NH 4 ) 2 TiF 6 and (NH 4 ) 3 FeF 6 by mixing an ammonium fluoride solution with the crude titanium fluoride solution followed by concentrating said mixture.
Claim 13
Independent Claim
90 words
A method for producing titanium fluoride comprising the sequential steps of: (1) dissolving iron-containing titanium material in a hydrofluoric acid solution to produce a fluoride solution; (2) crystallizing ferric fluoride in the fluoride solution followed by separating from the fluoride solution the ferric fluoride crystals thus obtained to produce a crude titanium fluoride solution; (3) crystallizing a mixed salt of (NH 4 ) 2 TiF 6 and (NH 4 ) 3 FeF 6 by mixing an ammonium fluoride solution with the crude titanium fluoride solution followed by concentrating said mixture.
Claim 14
Dependent Claim
35 words
The method of claim 4, further comprising an oxidation step, wherein divalent iron-ion in the fluoride solution is oxidized into trivalent iron-ion by blowing an oxidizing agent into the fluoride solution obtained in step 1.
Claim 15
Dependent Claim
73 words
The method of claim 11, wherein step 3 is followed by pyrolyzing said mixed salt at a temperature of from 300° to 800° C. in a stream of dry gas to produce solid ferric fluoride (FeF 3 ) and gaseous TiF 4 , HF and NH 3 and condensing the gaseous TiF 4 , HF and NH 3 at a temperature of from 20° to 280° C. to produce solid TiF 4 .
Claim 16
Dependent Claim
25 words
The method of claim 11, wherein the dissolving of titanium material in step 1 is at a reaction temperature of from 60° to 90° C.
Claim 17
Dependent Claim
20 words
The method of claim 11, wherein the fluoride solution is cooled at a temperature of from 0° to 20° C.
Claim 18
Dependent Claim
50 words
The method of claim 11, wherein step 3 further includes mixing an ammonium fluoride solution with said crude titanium fluoride solution followed by evaporating and concentrating the mixture to crystallize and separate a mixed salt of (NH 4 ) 2 TiF 6 and (NH 4 ) 3 FeF 6 .
Claim 19
Dependent Claim
37 words
The method of claim 13, wherein pyrolysis is conducted at a temperature of from 400° to 600° C. in a stream of dry gas selected from the group consisting of dry nitrogen, dry air and dry argon.
Claim 20
Dependent Claim
18 words
The method of claim 13, wherein condensation is conducted at a temperature of from 50° to 100° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-16 | 1993-10-16 | 1994-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-16 | 1997-10-16 | 1998-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-16 | 2001-10-16 | 2002-04-17 | $7700.00 | Window Closed / Lapsed |