Abstract
Abstract Process for preparation of toner particles for electrostatic liquid developers utilizing a single vessel wherein (A) a thermoplastic resin and hydrocarbon liquid having a Kauri-butanol value of less than 120 at a total of solids of at least 22% by weight are dispersed in the vessel by moving particulate media (crating shear) at elevated temperature to plasticize and liquify the resin, (B) while the particulate media are maintained in continuous motion the dispersion is cooled whereby the resin precipitates in the form of toner particle having an average by area particle size of 10 μm or less, and (C) the particulate media are removed. Liquid electrostatic developers are prepared by the addition of a charge director compound. The liquid developers are prepared in a shorter time that previously known processes. The liquid developers are useful for preparation of copies and proofs of various colors.
Inventors
- 👤 David E. Blair
- 👤 Bradley J. Gollhardt
- 👤 James R. Larson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 10:27
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/12
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
167 words
A process for the preparation of toner particles for electrostatic liquid developers comprising A. dispersing at an elevated temperature in a vessel a thermoplastic resin, and a hydrocarbon liquid having a Kauri-butanol value of less than 120, such that the dispersion contains a total % solids of at least 22% by weight by means of moving particulate media whereby the moving particulate media creates shear and/or impact, while maintaining the temperature in the vessel at a temperature sufficient to plasticize and liquify the resin and below that at which the hydrocarbon liquid boils and the resin decomposes, B. cooling the dispersion containing a total % solids of at least 22% by weight in said vessel to permit precipitation of the resin out of the dispersant, the particulate media being maintained in continuous movement during and subsequent to cooling whereby toner particles having an average by area particle size of 10 μm or less are formed, and C. separating the dispersion of toner particles from the particulate media.
Claim 2
Dependent Claim
167 words
A process for the preparation of toner particles for electrostatic liquid developers comprising A. dispersing at an elevated temperature in a vessel a thermoplastic resin, and a hydrocarbon liquid having a Kauri-butanol value of less than 120, such that the dispersion contains a total % solids of at least 22% by weight by means of moving particulate media whereby the moving particulate media creates shear and/or impact, while maintaining the temperature in the vessel at a temperature sufficient to plasticize and liquify the resin and below that at which the hydrocarbon liquid boils and the resin decomposes, B. cooling the dispersion containing a total % solids of at least 22% by weight in said vessel to permit precipitation of the resin out of the dispersant, the particulate media being maintained in continuous movement during and subsequent to cooling whereby toner particles having an average by area particle size of 10 μm or less are formed, and C. separating the dispersion of toner particles from the particulate media.
Claim 3
Dependent Claim
27 words
A process according to claim 1 wherein the particulate media are selected from the group consisting of stainless steel, carbon steel, ceramic, alumina, zirconium, silica, and sillimanite.
Claim 4
Dependent Claim
21 words
A process according to claim 2 wherein the particulate media are spherical having an average diameter of 0.04 to 0.5 inch.
Claim 5
Dependent Claim
45 words
A process according to claim 1 wherein the thermoplastic resin is a copolymer of ethylene (80 to 99.9%) and acrylic or methacrylic acid (0 to 20%)/alkyl C 1 to C 5 ester of methacrylic or acrylic acid (0 to 20%), the percentages being by weight.
Claim 6
Dependent Claim
29 words
A process according to claim 4 wherein the thermoplastic resin is a copolymer of ethylene (89%) and methacrylic acid (11%) having a melt index at 190° C. of 100.
Claim 7
Dependent Claim
11 words
A process according to claim 1 wherein a colorant is present.
Claim 8
Dependent Claim
12 words
A process according to claim 1 wherein the colorant is carbon black.
Claim 9
Dependent Claim
13 words
A process according to claim 1 wherein inorganic oxide fine particles are present.
Claim 10
Dependent Claim
11 words
A process according to claim 8 wherein the oxide is silica.
Claim 11
Dependent Claim
13 words
A process according to claim 1 wherein a combination of colorants is present.
Claim 12
Dependent Claim
30 words
A process according to claim 1 wherein after step C. a charge director is added to the dispersion to impart an electrostatic charge of predetermined polarity to the toner particles.
Claim 13
Dependent Claim
29 words
A process according to claim 11 wherein the thermoplastic resin is a copolymer of ethylene (89%) and methacrylic acid (11%) having a melt index at 190° C. of 100.
Claim 14
Dependent Claim
19 words
A process according to claim 1 wherein a plurality of thermoplastic resins are employed in the plasticizing step A.
Claim 15
Dependent Claim
18 words
A process according to claim 1 wherein subsequent to step C. diluting the dispersion with additional hydrocarbon liquid.
Claim 16
Dependent Claim
29 words
A process according to claim 14 wherein the thermoplastic resin is a copolymer of ethylene (89%) and methacrylic acid (11%) having a melt index at 190° C. of 100.
Claim 17
Dependent Claim
32 words
A process according to claim 14 wherein the dilution is conducted to reduce the concentration of toner particles to between 0.1 to 3.0 percent by weight with respect to the hydrocarbon liquid.
Claim 18
Dependent Claim
21 words
A process according to claim 1 wherein the particles have an average by area particle size of 5 μm or less.
Claim 19
Dependent Claim
36 words
A process according to claim 1 wherein a colorant is present in step A and the temperature is maintained in the vessel below that at which the hydrocarbon liquid boils and the resin and colorant decomposes.
Claim 20
Dependent Claim
21 words
A process according to claim 1 wherein toner particles having a plurality of fibers extending therefrom are formed in step B.
Claim 21
Dependent Claim
48 words
A process according to claim 11 wherein an adjuvant selected from the group consisting of polyhydroxy compound, aminoalcohol, polybutylene succinimide, metallic soap, and aromatic hydrocarbon having a Kauri-butanol value of greater than 30, is added with the proviso that the metallic soap is dispersed in the thermoplastic resin.
Claim 22
Dependent Claim
17 words
A process according to claim 20 wherein the adjuvant compound is added after the dispersing step (A).
Claim 23
Dependent Claim
18 words
A process according to claim 1 wherein the hydrocarbon liquid has a Kauri-butanol value of less than 30.
Claim 24
Dependent Claim
18 words
A process according to claim 22 wherein the thermoplastic resin is a copolymer of ethylene and methacrylic acid.
Claim 25
Dependent Claim
13 words
A process according to claim 22 wherein at least one colorant is present.
Claim 26
Dependent Claim
18 words
A process according to claim 24 wherein after step C. a charge director is added to the dispersion.
Claim 27
Dependent Claim
18 words
A process according to claim 25 wherein the thermoplastic resin is a copolymer of ethylene and methacrylic acid.
Claim 28
Dependent Claim
18 words
A process according to claim 26 wherein subsequent to step C. diluting the dispersion with additional hydrocarbon liquid.
Claim 29
Dependent Claim
22 words
A process according to claim 27 wherein the toner particles having a plurality of fibers extending therefrom are formed in step B.
References Cited (Backward Citations)
GB2169416A
Cited
US4794651A
Cited
US4760009A
Cited
US4631244A
Cited
US4670370A
Cited
US4663264A
Cited
US4702985A
Cited
US4702984A
Cited
US4707429A
Cited
US4740444A
Cited
US4681831A
Cited
US4780389A
Cited
US4758494A
Cited
US4783389A
Cited
US4772528A
Cited
US4780388A
Cited
US4783388A
Cited
US4798778A
Cited
US4820605A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |