Method of making a shaped polyester article

Claim 1

The method of forming a shaped article having at least one major surface comprising a continuous phase of polyester having dispersed therein microbeads of cellulose acetate at least partially bordered by void space oriented generally flatwise with respect to said major surface of said shaped article, said sheet when consisting only of said polyester continuous phase and said microbeads at least partially bordered by void space characterized by having a Kubelka-Munk R value (infinite thickness) of about 0.90 to about 1.0 and the following Kubelka-Munk values when formed into a 3 mil thick film: Opacity -- about 0.78 to about 1.0 SX -- 25 or less KX -- about 0.001 to 0.2 T(i) -- about 0.02 to 1.0 said method comprising (a) forming a mixture of molten polyester and cellulose acetate, wherein the cellulose acetate is a multiplicity of uniformly dispersed microbeads throughout said polyester, said polyester having an I.V. of at least 0.55, said cellulose acetate having an acetyl content of about 28 to 44.8% by weight, a viscosity of about 0.01-90 seconds and a Tg of about 20° C. higher than the Tg of said polyester, (b) forming a shaped article from said mixture, (c) orienting said article by stretching at least in one direction to form microbeads of said cellulose acetate uniformly distributed throughout said article and voids at least partially bordering said microbeads on sides thereof in the direction(s) of orientation.

Claim 2

The method of forming a shaped article having at least one major surface comprising a continuous phase of polyester having dispersed therein microbeads of cellulose acetate at least partially bordered by void space oriented generally flatwise with respect to said major surface of said shaped article, said sheet when consisting only of said polyester continuous phase and said microbeads at least partially bordered by void space characterized by having a Kubelka-Munk R value (infinite thickness) of about 0.90 to about 1.0 and the following Kubelka-Munk values when formed into a 3 mil thick film: Opacity -- about 0.78 to about 1.0 SX -- 25 or less KX -- about 0.001 to 0.2 T(i) -- about 0.02 to 1.0 said method comprising (a) forming a mixture of molten polyester and cellulose acetate, wherein the cellulose acetate is a multiplicity of uniformly dispersed microbeads throughout said polyester, said polyester having an I.V. of at least 0.55, said cellulose acetate having an acetyl content of about 28 to 44.8% by weight, a viscosity of about 0.01-90 seconds and a Tg of about 20° C. higher than the Tg of said polyester, (b) forming a shaped article from said mixture, (c) orienting said article by stretching at least in one direction to form microbeads of said cellulose acetate uniformly distributed throughout said article and voids at least partially bordering said microbeads on sides thereof in the direction(s) of orientation.

Claim 7

The method of forming a paper-like sheet comprising a continuous phase of polyester having dispersed therein microbeads of cellulose acetate encircled by void spaces when viewed in a direction perpendicular to the plane of the sheet, said sheet when consisting only of said polyester continuous phase and said microbeads at least partially bordered by void space characterized by having a Kubelka-Munk R value (infinite thickness) of about 0.90 to about 1.0 and the following Kubelka-Munk values when formed into a 3 mil thick film: Opacity -- about 0.78 to 1.0 SX -- 25 or less KX -- about 0.001 to 0.2 T(i) -- about 0.02 to 1.0 said method comprising (a) forming a molten mixture of poly(ethylene terephthalate) and cellulose acetate, wherein the cellulose acetate is uniformly dispersed through said poly(ethylene terephthalate); said poly(ethylene terephthalate) having a Tg of about 80° C., and an I.V. of at least 0.55, said cellulose acetate having an acetyle content of about 28 to 44.8% by weight, a viscosity of about 0.01-90 seconds and a Tg of about 20° C. higher than the Tg of said poly(ethylene terephthalate), (b) casting a film of said mixture, and (c) orienting said film by stretching to form microbeads of said cellulose acetate uniformly distributed throughout said film and encircled by doughnut-shaped voids lying in planes generally parallel to opposite surfaces of said film.

Claim 8

The method of forming a paper-like sheet comprising a continuous phase of polyester having dispersed therein microbeads of cellulose acetate encircled by void spaces when viewed in a direction perpendicular to the plane of the sheet, said sheet when consisting only of said polyester continuous phase and said microbeads at least partially bordered by void space characterized by having a Kubelka-Munk R value (infinite thickness) of about 0.90 to about 1.0 and the following Kubelka-Munk values when formed into a 3 mil thick film: Opacity -- about 0.78 to 1.0 SX -- 25 or less KX -- about 0.001 to 0.2 T(i) -- about 0.02 to 1.0 said method comprising (a) forming a molten mixture of poly(ethylene terephthalate) and cellulose acetate, wherein the cellulose acetate is uniformly dispersed through said poly(ethylene terephthalate); said poly(ethylene terephthalate) having a Tg of about 80° C., and an I.V. of at least 0.55, said cellulose acetate having an acetyle content of about 28 to 44.8% by weight, a viscosity of about 0.01-90 seconds and a Tg of about 20° C. higher than the Tg of said poly(ethylene terephthalate), (b) casting a film of said mixture, and (c) orienting said film by stretching to form microbeads of said cellulose acetate uniformly distributed throughout said film and encircled by doughnut-shaped voids lying in planes generally parallel to opposite surfaces of said film.