Compact polymer/metal composite particles, aqueous dispersions thereof, preparation and use in biological applications

Claim 2

A process for preparing compact polymer/metal composite particles comprising the steps of: (1) dispersing, in an organic liquid solvent for a metal-carbonyl, -organocarbonyl or -hydrocarbon complex that can be thermally decomposed at a temperature below the boiling point of said organic liquid, anhydrous particles of polymer bearing nucleophilic sites which can be coordinated with said metal complex, the nature of said polymer being such that said polymer particles swell, in the presence of said organic liquid, to a volume such that said polymer particles become accessible to molecules of said metal complex while remaining insoluble in said organic liquid; (2) introducing a metal-carbonyl, -organocarbonyl or -hydrocarbon complex which is soluble in said organic liquid into the dispersion of swollen polymer particles obtained in said step (1), and thermally decomposing said metal complex, with the proviso that said decomposition takes place under a reducing atmosphere when said metal complex is a metal-hydrocarbon complex; and (3) removing said organic liquid from said swollen polymer particles to obtain said compact polymer/metal composite particles.

Claim 3

The process of claim 1, wherein the size of said polymer particles in said step (1) is from 0.1 micron to 1 mm.

Claim 4

The process of claim 1, wherein said polymer particles swell by 0.1 to 50 times their original volume in the presence of said organic liquid.

Claim 5

The process of claim 1, wherein the ratio by weight of metal in said metal complex : polymer, employed in said step (2), is from 0.5:100 to 200:100.

Claim 6

The process of claim 1, wherein said composite particles obtained are redispersed in a liquid that does not swell said polymer.

Claim 7

The process of claim 1, wherein, after removal of said organic liquid in said step (3), said composite particles obtained are washed using an intermediate non-swelling liquid which is miscible with said organic liquid and with water, and are then separated from said intermediate non-swelling liquid and dispersed in water by washing with water.

Claim 8

The process of claim 1, wherein said composite particles obtained are sized having a uniform size of from 0.1 micron to 1 mm and wherein: said polymer particles employed in said step (1) are sized having a uniform size of from 0.1 micron to 1 mm, the nature of said polymer constituting said polymer particles being such that said polymer particles swell by 0.1 to 50 times their original volume in the presence of said organic liquid; said polymer forms the matrix of said composite particles, and comprises 0.5-30% by weight of nucleophilic sites which can be coordinated with said metal complex; and the ratio by weight of metal in said metal complex : polymer employed in said step (2) is from 0.5:100 to 200:100, whereby said composite particles obtained comprise crystallites of said metal at the zero valence state encapsulated in said matrix, the size of said crystallites being from 10 -6 to 10 -4 mm, and the quantity of encapsulated metal represents about 0.5 to 67% by weight of said composite particles.

Claim 9

The process of claim 7, wherein said composite particles obtained are redispersed in a liquid that does not swell said polymer.

Claim 10

The process of claim 7, wherein said composite particles obtained are washed using an intermediate non-swelling liquid which is miscible with said organic liquid and with water, said non-swelling liquid is removed; and said composite particles are then dispersed in water by washing with water until a concentration of 1 to 50% by weight of said particles in the water is obtained.

Claim 11

The process of claim 1, wherein, in said step (1), the size of said polymer particles is from 0.5 to 100 microns.

Claim 12

The process of claim 1, wherein, in said step (1), said polymer particles swell by 3 to 10 times their original volume in the presence of said organic liquid.

Claim 13

The process of claim 1, wherein, in said step (2), the ratio by weight of metal in said metal complex : polymer employed is from 3:100 to 35:100.

Claim 14

The process of claim 1, wherein said polymer comprises 30 to 99% by weight of at least one monoethylenic monomer which does not coordinate with said metal complex, 0.5 to 50% by weight of at least one crosslinkable polyethylenic monomer which does not coordinate with said metal complex and 0.5 to 30% by weight of at least one nucleophilic monomer which can be coordinated with said metal complex.

Claim 15

The process of claim 13, wherein said polymer comprises: 50 to 95% by weight of at least one monoethylenic monomer which does not coordinate with said metal complex; 2 to 20% by weight of at least one crosslinkable polyethylenic monomer which does not coordinate with said metal complex; and 3 to 30% by weight of at least one nucleophilic monomer which can be coordinated with said metal complex.

Claim 16

The process of claim 13, wherein said monoethylenic monomer is selected from the group consisting of styrene, styrene derivatives, esters and amides of acrylic and methacrylic acid, acrylic acid, methacrylic acid, monoethylenic diacids, vinylpyrrolidone, vinyl esters, vinyl chloride and vinylidene chloride.

Claim 17

The process of claim 13, wherein said polyethylenic monomer is selected from the group consisting of divinylbenzene, divinylbenzene derivatives, conjugated dienes, polyallyl compounds, acrylates and methacrylates of polyols, methylenebis(acrylamide) and bis(acrylamido)acetic acid.

Claim 18

The process of claim 13, wherein said nucleophilic monomer is selected from the group consisting of vinylpyridine, di(ethyl)aminoalkyl acrylates and -methacrylates, di(ethyl)aminoalkylacrylamides and -methacrylamides, allylamine, ethylenimine, acrylonitrile, methacrylonitrile, 1-vinylimidazole and dialkylaminomethylstyrenes.

Claim 19

The process of claim 1, wherein said organic liquid is an aromatic compound, optionally chlorinated, an aliphatic or cycloaliphatic hydrocarbon, a dialkyl ether, an alcohol or an ester, said organic liquid having a boiling point above the decomposition temperature of said metal complex.

Claim 20

The process of claim 1, wherein the concentration of said polymer particles in said organic liquid in said step (1) is from 1 to 35% by weight.

Claim 21

The process of claim 1, wherein said metal complex is a carbonyl complex, an organocarbonyl complex of the aliphatic, cycloaliphatic or aromatic type, or a hydrocarbon complex of the aliphatic or cycloaliphatic type, and wherein the metal of said metal complex is a Group VIa, VIIa or VIII metal of the Periodic Classification of the elements.

Claim 22

The process according to claim 20, wherein said metal complex is selected from the group consisting of Cr(CO) 6 , Mo(CO) 6 , W(CO) 6 , (Mn) 2 (CO) 10 , (Re) 2 (CO) 10 , Fe(CO) 5 , (Fe) 2 (CO) 9 , (Fe) 3 (CO) 12 , (Co) 2 (CO) 8 , (Co) 4 (CO) 12 , Ni(CO) 4 , (Rh) 6 (CO) 12 , (Rh) 4 (CO) 12 , (Ir) 4 (CO) 12 , (Os) 3 (CO) 12 , (Ru) 3 (CO) 12 , (methylcyclopentadienyl)Mn(CO) 3 , (cyclopentadienyl)Mn(CO) 3 , (cyclopentadienyl)Co(CO) 2 , (cyclopentadienyl)Re(CO) 3 , (di-n 5 -cyclopentadienyl)Ni and (di-n 5 -cyclopentadienyl)Fe.

Claim 23

The process of claim 1, wherein said thermal decomposition is carried out at a temperature of from 80° to 200° C.

Claim 24

The process of claim 1, wherein said thermal decomposition is carried out at a temperature in the vicinity of the boiling point of said organic liquid.

Claim 25

An aqueous dispersion of the composite particles produced by the process of claim 1.

Claim 26

The aqueous dispersion of claim 24, wherein said composite particles comprise from 1-50% by weight of said dispersion.

Claim 27

The method of using the composite particles produced by the process of claim 1 wherein said particles are employed as a solid phase in a biological application.

Claim 28

Polymer/metal composite particles, having a size of from 0.1 micron to 1 mm, said composite particles comprising 99.5 to 33% by weight of a matrix based on a copolymer derived from (a) 0.5 to 30% by weight of at least one monomer bearing nucleophilic sites which can be coordinated with a metal complex selected from the group consisting of metal-carbonyl, -organocarbyl and -hydrocarbon complexes, (b) 30 to 99% by weight of at least one monoethylenic monomer which does not coordinate with said metal complex, and (c) 0.5 to 50% by weight of at least one crosslinkable polyethylenic monomer which does not coordinate with said metal complex and, encapsulated in said matrix, 0.5 to 67% by weight of crystallites of a metal of Group VIa, VIIa, or vIII of the Periodic Classification of the elements in the zero valence state derived from said metal complex, the nature of said copolymer being such that particles of said copolymer are capable of swelling by 0.1 to 50 times their volume, in the presence of an organic liquid which is a solvent for said metal complex, said swollen volume of said particles being such that said copolymer particles become accessible to the molecules of said metal complex while remaining insoluble in said organic liquid, said organic liquid having a boiling point above the temperature of decomposition of said metal complex, and wherein said composite particles are compact and sized, and wherein the size of said metal crystallites is from 10 -6 to 10 -4 mm.

Claim 29

Polymer/metal composite particles, having a size of from 0.1 micron to 1 mm, said composite particles comprising 99.5 to 33% by weight of a matrix based on a copolymer derived from (a) 0.5 to 30% by weight of at least one monomer bearing nucleophilic sites which can be coordinated with a metal complex selected from the group consisting of metal-carbonyl, -organocarbyl and -hydrocarbon complexes, (b) 30 to 99% by weight of at least one monoethylenic monomer which does not coordinate with said metal complex, and (c) 0.5 to 50% by weight of at least one crosslinkable polyethylenic monomer which does not coordinate with said metal complex and, encapsulated in said matrix, 0.5 to 67% by weight of crystallites of a metal of Group VIa, VIIa, or vIII of the Periodic Classification of the elements in the zero valence state derived from said metal complex, the nature of said copolymer being such that particles of said copolymer are capable of swelling by 0.1 to 50 times their volume, in the presence of an organic liquid which is a solvent for said metal complex, said swollen volume of said particles being such that said copolymer particles become accessible to the molecules of said metal complex while remaining insoluble in said organic liquid, said organic liquid having a boiling point above the temperature of decomposition of said metal complex, and wherein said composite particles are compact and sized, and wherein the size of said metal crystallites is from 10 -6 to 10 -4 mm.

Claim 30

The composite particles of claim 27, wherein said metal retains its zero valence state and, if magnetizable, its magnetic properties upon exposure of said composite particles to ambient conditions.

Claim 31

The composite particles of claim 27, wherein the quantity of said nucleophilic sites in said matrix represents from 3 to 30% of the weight of said polymer.

Claim 32

The composite particles of claim 27, wherein said composite particles have a uniform size of from 0.5 to 100 microns.

Claim 33

The composite particles of claim 27, wherein said particles comprise 97 to 74% by weight of said matrix and 3 to 26% by weight of said metal.

Claim 34

The composite particles of claim 25, wherein the size of said metal crystallites is from 3×10 -6 to 3×10 -5 mm.

Claim 35

The composite particles of claim 27, wherein said compact and sized composite particles have a uniform size from 0.1 micron to 1 mm.

Claim 36

An aqueous dispersion of the composite particles of claim 27.

Claim 37

The aqueous dispersion of claim 34, wherein said composite particles comprise 1-50% by weight of said dispersion.

Claim 38

The method of using the composite particles of claim 27, wherein said particles are employed as a solid phase in a biological application.

Claim 39

The method of claim 36, wherein said composite particles, as they are or in an aqueous dispersion, are employed as a solid phase in a diagnostic test.

Claim 40

Compact polymer/metal sized composite particles of a uniform size of from 0.1 micron to 1 mm, comprising: 99.5 to 33% by weight of a matrix based on a copolymer derived from 30 to 99% by weight of at least one monoethylenic monomer which does not coordinate with a metal complex, 0.5 to 50% by weight of at least one crosslinkable polyethylenic monomer which does not coordinate with a metal complex and 0.5 to 30% by weight of at least one nucleophilic monomer which can be coordinated with a metal complex; and, encapsulated in said matrix, from 0.5 to 67% by weight of crystallites of a metal of Group VIa, VIIa or VIII of the Periodic Classification of the elements in the zero (valence state, the size of said crystallites being from 10 -6 to 10 -4 mm.

Claim 41

Compact polymer/metal sized composite particles of a uniform size of from 0.1 micron to 1 mm, comprising: 99.5 to 33% by weight of a matrix based on a copolymer derived from 30 to 99% by weight of at least one monoethylenic monomer which does not coordinate with a metal complex, 0.5 to 50% by weight of at least one crosslinkable polyethylenic monomer which does not coordinate with a metal complex and 0.5 to 30% by weight of at least one nucleophilic monomer which can be coordinated with a metal complex; and, encapsulated in said matrix, from 0.5 to 67% by weight of crystallites of a metal of Group VIa, VIIa or VIII of the Periodic Classification of the elements in the zero (valence state, the size of said crystallites being from 10 -6 to 10 -4 mm.