Thermoplastic elastomer
Assignee: Resonac Holdings Corp
•
Filing: 1989-12-22
•
Granted: 1991-01-15
•
Expires: 2009-12-22
Abstract
Abstract A thermoplastic elastomer with well-balanced physical properties is prepared by treating a rubber/resin composition comprised of (a) 45-90 wt. parts of a rubbery component and (b) 10-55 wt. parts of a polyolefin resin, with a curing agent. The rubbery component (a) is comprised of 5-100 wt. % of an ethylene-propylene copolymer rubber having an ethylene content of 60-78 mole %, a crystallinity of 4 to 20%, a maximum peak temperature of melting of at least 100° C., an MFI of less than 0.01 at 230° C., an HLMFI/MFI of at least 35, an Mw/Mn of at least 4, and a tensile strength at break of at least 100 kg/cm 2 , and 95-0% by weight of an ethylene-propylene-nonconjugated diene copolymer. The rubbery component in the cured product has a gel content more than 80 wt. % and less than 97 wt. % as determined by immersion in cyclohexane at 23° C. for 48 hours.
Inventors
- 👤 Zenichiro Izumi
- 👤 Shigeru Kurosawa
- 👤 Rika Akiyoshi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:28
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/10; C08L23/16; C08L2207/00; C08L2207/04; C08L2312/00
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
214 words
A thermoplastic elastomer which is a cured product prepared by treating a composition comprising (a) 45 to 90 parts by weight of a rubbery component and (b) 10 to 55 parts by weight of a polyolefin resin, based on 100 parts by weight of the sum of the components (a) and (b), with a curing agent; said rubbery component (a) comprising, based on the weight of the rubbery component, 5 to 100% by weight of an ethylene-propylene copolymer rubber having an ethylene content of 60 to 78% by mole, a crystallinity of 4 to 20% as determined by the X-ray diffractometry, a maximum peak temperature of melting of at least 100° C., a melt flow index (MFI) at 230° C. of less than 0.01, a high-load melt flow index (HLMFI)/melt flow index (MFI) ratio of at least 35, a weight average molecular weight (Mw)/number average molecular weight (Mn) ratio of at least 4, and a tensile strength at break of at least 100 kg/cm 2 , and 95 to 0% by weight of an ethylene-propylene-nonconjugated diene copolymer; and said rubbery component (a) in the cured product having a gel content of more than 80% by weight and less than 97% by weight as determined by immersion in cyclohexane at 23° C. for 48 hours.
Claim 2
Dependent Claim
214 words
A thermoplastic elastomer which is a cured product prepared by treating a composition comprising (a) 45 to 90 parts by weight of a rubbery component and (b) 10 to 55 parts by weight of a polyolefin resin, based on 100 parts by weight of the sum of the components (a) and (b), with a curing agent; said rubbery component (a) comprising, based on the weight of the rubbery component, 5 to 100% by weight of an ethylene-propylene copolymer rubber having an ethylene content of 60 to 78% by mole, a crystallinity of 4 to 20% as determined by the X-ray diffractometry, a maximum peak temperature of melting of at least 100° C., a melt flow index (MFI) at 230° C. of less than 0.01, a high-load melt flow index (HLMFI)/melt flow index (MFI) ratio of at least 35, a weight average molecular weight (Mw)/number average molecular weight (Mn) ratio of at least 4, and a tensile strength at break of at least 100 kg/cm 2 , and 95 to 0% by weight of an ethylene-propylene-nonconjugated diene copolymer; and said rubbery component (a) in the cured product having a gel content of more than 80% by weight and less than 97% by weight as determined by immersion in cyclohexane at 23° C. for 48 hours.
Claim 3
Dependent Claim
38 words
The thermoplastic elastomer according to claim 1, wherein the ethylene-propylene copolymer rubber has a crystallinity of 4 to 10%, an Mw/Mn of at least 5, and a tensile strength at break of at least 150 kg/cm 2 .
Claim 4
Dependent Claim
21 words
The thermoplastic elastomer according to claim 1, wherein the ethylene-propylene copolymer rubber has a Shore A hardness of 50 to 95.
Claim 5
Dependent Claim
76 words
The thermoplastic elastomer according to claim 1, wherein the ethylene-propylene-nonconjugated diene copolymer comprises units derived from ethylene and units derived from propylene in a proportion (ethylene units/propylene units) of 60/40 to 78/22, and 1 to 15% by weight, based on the weight of the ethylene-propylene-nonconjugated diene copolymer, of a nonconjugated diene compound having 5 to 20 carbon atoms, and has an intrinsic viscosity [η] of 0.5 to 4 dl/g as measured in decaline at 135° C.
Claim 6
Dependent Claim
33 words
The thermoplastic elastomer according to claim 1, wherein the rubbery component (a) comprises 25 to 75% by weight of the ethylene-propylene copolymer rubber and 75 to 25% by weight the ethylene-propylene-nonconjugated diene copolymer.
Claim 7
Dependent Claim
20 words
The thermoplastic elastomer according to claim 1, wherein the polyolefin resin of the component (b) is a polypropylene type resin.
Claim 8
Dependent Claim
48 words
The thermoplastic elastomer according to claim 6, wherein the polypropylene type resin of the component (b) is a mixture of 10 to 100% by weight of a homopolypropylene and 90 to 0% by weight of a propylene-α-olefin random copolymer containing 5 to 15% by mole of an α-olefin.
Claim 9
Dependent Claim
34 words
The thermoplastic elastomer according to claim 1, wherein said composition further comprises a softening agent in an amount not more than an amount having an equal weight to that of the rubbery component (a).
Claim 10
Dependent Claim
21 words
The thermoplastic elastomer according to claim 1, wherein the curing agent is an organic peroxide, and the treatment is effected dynamically.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-14 | 1994-07-16 | 1995-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-14 | 1998-07-16 | 1999-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-14 | 2002-07-16 | 2003-01-15 | $7700.00 | Window Closed / Lapsed |