US4990594A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Producing a copolyester from a lower dialkyl ester of terephthalic acid, a glycol and a dicarboxylic acid
Assignee: Invista North America LLC
•
Filing: 1990-03-07
•
Granted: 1991-02-05
•
Expires: 2010-03-07
Abstract
Abstract A process for producing a copolyester by copolymerizing the monomers from the ester interchange of a lower dialkyl ester of terephthalic acid and glycol and the direct esterification of a dicarboxylic acid and glycol using a novel catalyst system. The novel catalyst composition includes from about 20 ppm to about 150 ppm manganese; from about 50 ppm to about 350 ppm lithium; preferably from about 10 ppm to about 70 ppm cobalt; and from about 200 ppm to about 400 ppm antimony, all amounts being based upon the expected yield of the copolyester. The novel process to make copolyester includes the step of employing an effective catalytic amount of manganese and lithium in an ester interchange reaction where the lower dialkyl ester and glycol produce a first monomer; to the monomer adding a slurry of dicarboxylic acid and glycol and employing an effective catalytic amount of lithium and cobalt in a direct esterification reaction where the dicarboxylic acid and glycol produce a second monomer; and using an effective catalytic amount antimony in a copolycondensation reaction of the monomers. Using the catalyst system allows for the combination of the ester interchange reaction with the direct esterification reaction to produce a copolyester.
Inventors
- 👤 Anthony W. Cooke
- 👤 Monika E. Bader
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:49
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/78; C08G63/82; C08G63/826; C08G63/83; C08G63/85; C08G63/86; C08G63/866
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
167 words
In a process for making a copolyester from a lower dialkyl ester of a terephthalic acid, a dicarboxylic acid having the formula ##STR3## wherein R is selected from the group consisting of ##STR4## and--(CH2) n --where n═2-12 and a glycol comprising the steps of: a. reacting said lower alkyl ester of terephthalic acid and glycol by an ester interchange reaction to produce a first monomer and alcohol; b. removing said alcohol during said ester interchange reaction; c. reacting a mixture of dicarboxylic acid and glycol by a direct esterification reaction to produce a second monomer and water; d. polymerizing a mixture of said first and second monomers by a polycondensation reaction to produce said copolyester and glycol; and e. removing said glycol during said polycondensation reaction; wherein the improvement comprises: adding an effective catalytic amount of manganese and lithium before or during said ester interchange reaction and said direct esterification; and adding an effective catalytic amount of antimony at or before the beginning of the polycondensation reaction.
Claim 2
Dependent Claim
167 words
In a process for making a copolyester from a lower dialkyl ester of a terephthalic acid, a dicarboxylic acid having the formula ##STR3## wherein R is selected from the group consisting of ##STR4## and--(CH2) n --where n═2-12 and a glycol comprising the steps of: a. reacting said lower alkyl ester of terephthalic acid and glycol by an ester interchange reaction to produce a first monomer and alcohol; b. removing said alcohol during said ester interchange reaction; c. reacting a mixture of dicarboxylic acid and glycol by a direct esterification reaction to produce a second monomer and water; d. polymerizing a mixture of said first and second monomers by a polycondensation reaction to produce said copolyester and glycol; and e. removing said glycol during said polycondensation reaction; wherein the improvement comprises: adding an effective catalytic amount of manganese and lithium before or during said ester interchange reaction and said direct esterification; and adding an effective catalytic amount of antimony at or before the beginning of the polycondensation reaction.
Claim 3
Dependent Claim
18 words
In the process of claim 1 wherein said manganese, lithium, and antimony are in the form of salts.
Claim 4
Dependent Claim
22 words
In the process of claim 1, wherein said manganese, lithium, and antimony are in the form of organic compounds or inorganic compounds.
Claim 5
Dependent Claim
22 words
In the process of claim 3, wherein said organic compounds are selected from the class of carboxylated metallic salts or metal amines.
Claim 6
Dependent Claim
24 words
In the process of claim 3, wherein said inorganic compounds are selected from the class of metal halides and metal compounds of Group IV.
Claim 7
Dependent Claim
26 words
In the process of claim 1, wherein said manganese, and lithium are in the form of acetates and said antimony is in the form of oxide.
Claim 8
Dependent Claim
20 words
In the process of claim 1, wherein said lower dialkyl ester is dimethyl terephthalate, and said glycol is ethylene glycol.
Claim 9
Dependent Claim
30 words
In the process of claim 1, wherein said ester interchange reaction occurs at a temperature range of from about 150° C. to about 250° C., and at about atmospheric pressure.
Claim 10
Dependent Claim
38 words
In the process of claim 8, wherein said polycondensation reaction occurs at a temperature range of from about 250° C. to about 310° C. and at a pressure of from about 0.1 to about 3.0 mm mercury vacuum.
Claim 11
Dependent Claim
68 words
In the process of claim 1, wherein said manganese is present in a range of from about 20 ppm to about 150 ppm, said lithium is present in a range of from about 50 ppm to about 350 ppm, and said antimony is present in a range of from about 200 ppm to about 400 ppm, wherein all amounts are based on the expected yield of said copolyester.
Claim 12
Dependent Claim
29 words
In the process of claim 1, wherein said manganese is sequestered after said ester interchange reaction is substantially completed or during said polycondensation reaction by adding a sequestering agent.
Claim 13
Dependent Claim
190 words
In a process for making a copolyester from a lower dialkyl ester of a terephthalic acid, a dicarboxylic acid having the formula ##STR5## wherein R is a selected from the group consisting of ##STR6## and--(CH2) n --where n═2-12 and a glycol comprising the steps of: a. reacting said lower alkyl ester of terephthalic acid and glycol by an ester interchange reaction to produce a first monomer and alcohol; b. removing said alcohol during said ester interchange reaction; c. reacting a mixture of dicarboxylic acid and glycol with said first monomer by a direct esterification reaction to produce a second monomer and water; d. polymerizing a mixture of said first and second monomers by a polycondensation reaction to produce said copolyester and glycol; and e. removing said glycol during said polycondensation reaction; wherein the improvement comprises: adding an effective catalytic amount of manganese and lithium before or during said ester interchange reactions; and adding an effective catalytic amount of cobalt and antimony at or before the beginning of or during the polycondensation reaction, with the proviso that said cobalt not be added prior to substantial completion of said ester interchange reactions.
Claim 14
Dependent Claim
190 words
In a process for making a copolyester from a lower dialkyl ester of a terephthalic acid, a dicarboxylic acid having the formula ##STR5## wherein R is a selected from the group consisting of ##STR6## and--(CH2) n --where n═2-12 and a glycol comprising the steps of: a. reacting said lower alkyl ester of terephthalic acid and glycol by an ester interchange reaction to produce a first monomer and alcohol; b. removing said alcohol during said ester interchange reaction; c. reacting a mixture of dicarboxylic acid and glycol with said first monomer by a direct esterification reaction to produce a second monomer and water; d. polymerizing a mixture of said first and second monomers by a polycondensation reaction to produce said copolyester and glycol; and e. removing said glycol during said polycondensation reaction; wherein the improvement comprises: adding an effective catalytic amount of manganese and lithium before or during said ester interchange reactions; and adding an effective catalytic amount of cobalt and antimony at or before the beginning of or during the polycondensation reaction, with the proviso that said cobalt not be added prior to substantial completion of said ester interchange reactions.
Claim 15
Dependent Claim
83 words
In the process of claim 12, wherein said manganese is present in a range of from about 20ppm to about 150 ppm, said lithium is present in a range of from about 50 ppm to about 350 ppm, said cobalt is present in a range of from about 10 ppm to about 70 ppm, and said antimony is present in a range of from about 200 ppm to about 400 ppm, wherein all amounts are based on the expected yield of said polyester.
Claim 16
Dependent Claim
9 words
A copolyester made from the process of claim 1.
Claim 17
Dependent Claim
9 words
A copolyester made from the process of claim 10.
Claim 18
Dependent Claim
9 words
A copolyester made from the process of claim 11.
Claim 19
Dependent Claim
9 words
A copolyester made from the process of claim 12.
Claim 20
Dependent Claim
35 words
An enhanced copolyester of polyethylene terephthalate/isophthalate comprising from about 20 ppm to about 150 ppm Mn, from about 50 ppm to about 350 ppm Li, and from about 200 ppm to about 400 ppm antimony.
Claim 21
Dependent Claim
35 words
An enhanced copolyester of polyethylene terephthalate/isophthalate comprising from about 20 ppm to about 150 ppm Mn, from about 50 ppm to about 350 ppm Li, and from about 200 ppm to about 400 ppm antimony.
References Cited (Backward Citations)
US3709859A
Cited
US3487049A
Cited
US3657180A
Cited
GB1417738A
Cited
US3951905A
Cited
US3907754A
Cited
US3962189A
Cited
GB1522656A
Cited
US4107149A
Cited
US4010145A
Cited
US4501878A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-04 | 1994-08-06 | 1995-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-04 | 1998-08-06 | 1999-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-04 | 2002-08-06 | 2003-02-05 | $7700.00 | Window Closed / Lapsed |