US4997809A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fabrication of patterned lines of high Tc superconductors
Assignee: International Business Machines Corp
•
Filing: 1987-11-18
•
Granted: 1991-03-05
•
Expires: 2007-11-18
Abstract
Abstract A method for producing a patterned layer of high T c oxide superconductor is provided in which patterning is accomplished prior to the attainment of a superconducting state in the layer. A solution containing precursor components of the desired oxide superconductor is sprayed onto a substrate and dried to provide a layer thereon. This layer is then irradiated in selected areas to convert the irradiated layers to an intermediate oxide state, the nonirradiated areas being unchanged. The nonirradiated areas are then dissolved away, leaving a pattern of oxide material. This oxide material is then converted to a high T c superconducting state, as by annealing in an oxygen atmosphere. This provides the patterned layer of high T c oxide superconductor. An example of a such a superconductor is a mixed copper oxide, such as Y 1 Ba 2 Cu 3 O 7-x .
Inventors
- 👤 Arunava Gupta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:50
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0324; H10N60/0661; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/737; Y10S505/742
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
121 words
A method for providing a patterned layer of high T c oxide superconductor material, comprising: preparing a solution containing the components of said oxide superconductor in the proper stoichiometric ratios, coating said solution onto a substrate to provide a coated layer thereon, irradiating selected areas of said coated layer with an energy beam to convert said irradiated areas to an intermediate, nonsuperconducting oxide state, said energy beam being chosen to maintain said proper stoichiometric ratio during conversion to an oxide state, removing the nonirradiated areas of said coated layer to leave a patterned layer of said nonsuperconducting oxide, and converting said patterned layer to a high T c superconducting state, thereby producing a patterned layer of high T c oxide superconductor.
Claim 2
Independent Claim
121 words
A method for providing a patterned layer of high T c oxide superconductor material, comprising: preparing a solution containing the components of said oxide superconductor in the proper stoichiometric ratios, coating said solution onto a substrate to provide a coated layer thereon, irradiating selected areas of said coated layer with an energy beam to convert said irradiated areas to an intermediate, nonsuperconducting oxide state, said energy beam being chosen to maintain said proper stoichiometric ratio during conversion to an oxide state, removing the nonirradiated areas of said coated layer to leave a patterned layer of said nonsuperconducting oxide, and converting said patterned layer to a high T c superconducting state, thereby producing a patterned layer of high T c oxide superconductor.
Claim 3
Dependent Claim
24 words
The method of claim 1, where said nonsuperconductive oxide is converted to a high T c superconducting state by annealing in an oxygen atmosphere.
Claim 4
Dependent Claim
17 words
The method of claim 1, where said solution is coated on said substrate by spraying it thereon.
Claim 5
Dependent Claim
15 words
The method of claim 1, where said patterned high T c oxide layer is epitaxial.
Claim 6
Dependent Claim
13 words
The method of claim 1, where said energy beam is a laser beam.
Claim 7
Dependent Claim
12 words
The method of claim 5, where said laser beam provides ultraviolet wavelengths.
Claim 8
Dependent Claim
12 words
The method of claim 5, where said laser beam provides visible wavelengths.
Claim 9
Dependent Claim
15 words
The method of claim 1, where said energy beam is scanned across said coated layer.
Claim 10
Dependent Claim
17 words
The method of claim 1, where said high T c oxide superconductor is a mixed copper oxide.
Claim 11
Dependent Claim
14 words
The method of claim 1, where said substrate is heated during said irradiation step.
Claim 12
Dependent Claim
16 words
The method of claim 1, where said removing step is accomplished by dissolving said nonirradiated areas.
Claim 13
Independent Claim
103 words
A method for providing a patterned layer of high T c oxide superconductor material, comprising: coating a substrate with a solution containing the components desired in said high T c oxide superconductor, said components being in solution in the proper ratios, and drying to provide a layer on said substrate, locally converting selected areas of said layer to an oxide state while maintaining the cation components of said layer in the proper stoichiometric ratio, removing nonselected areas of said layer to leave a patterned layer of oxide material, and producing a high T c superconducting state in said patterned layer of oxide material.
Claim 14
Independent Claim
103 words
A method for providing a patterned layer of high T c oxide superconductor material, comprising: coating a substrate with a solution containing the components desired in said high T c oxide superconductor, said components being in solution in the proper ratios, and drying to provide a layer on said substrate, locally converting selected areas of said layer to an oxide state while maintaining the cation components of said layer in the proper stoichiometric ratio, removing nonselected areas of said layer to leave a patterned layer of oxide material, and producing a high T c superconducting state in said patterned layer of oxide material.
Claim 15
Dependent Claim
20 words
The method of claim 12, where said high T c superconducting state is YBa 2 Cu 3 O 7-x .
Claim 16
Dependent Claim
19 words
The method of claim 12, where said high T c superconducting oxide state is a mixed oxide of copper.
Claim 17
Independent Claim
162 words
A method for providing a patterned layer of oxide material that is a precursor to a high T c oxide superconductor, comprising the following steps: preparing a solution containing the cation components of said high T c oxide superconductor, said cation components being in said solution in the proper stoichiometric amounts required in said high T c oxide superconductor, coating said solution onto a substrate to produce a coated layer thereon, irradiating selected areas of said coated layer with an energy beam to create regions having chemical properties different than those of the surrounding nonirradiated regions, said irradiated regions being comprised of an oxide precursor to said high T c oxide material, said energy beam having an energy less than that which would change said proper stoichiometric amounts of said cation components, and dissolving said nonirradiated regions to remove them from said layer, thereby leaving a patterned layer of oxide material which is a precursor to said high T c oxide superconductor.
Claim 18
Independent Claim
162 words
A method for providing a patterned layer of oxide material that is a precursor to a high T c oxide superconductor, comprising the following steps: preparing a solution containing the cation components of said high T c oxide superconductor, said cation components being in said solution in the proper stoichiometric amounts required in said high T c oxide superconductor, coating said solution onto a substrate to produce a coated layer thereon, irradiating selected areas of said coated layer with an energy beam to create regions having chemical properties different than those of the surrounding nonirradiated regions, said irradiated regions being comprised of an oxide precursor to said high T c oxide material, said energy beam having an energy less than that which would change said proper stoichiometric amounts of said cation components, and dissolving said nonirradiated regions to remove them from said layer, thereby leaving a patterned layer of oxide material which is a precursor to said high T c oxide superconductor.
Claim 19
Dependent Claim
23 words
The method of claim 15, including the additional step of converting said patterned oxide precursor layer to a high T c superconducting state.
Claim 20
Dependent Claim
17 words
The method of claim 16, where said high T c oxide superconductor is a mixed copper oxide.
Claim 21
Dependent Claim
13 words
The method of claim 17, where said energy beam is a laser beam.
Claim 22
Dependent Claim
12 words
The method of claim 15, where said solution is a nitrate solution.
Claim 23
Independent Claim
148 words
A method for providing a patterned layer of high T c copper oxide superconductor, comprising: preparing a solution containing the components of said high T c oxide superconductor, said components being present in said solution in the amounts required in said high T c copper oxide superconductor, spraying said solution onto a substrate to provide a coated layer thereon, irradiating selected areas of said coated layer with an energy beam to convert said irradiated areas to an intermediate oxide state, the energy and scanning rate of said energy beam being chosen to maintain the relative amounts of the cation components in said layer, dissolving the nonirradiated areas of said coated layer to remove them, leaving a patterned layer of oxide material, and annealing said patterned layer of oxide material in an oxygen atmosphere to produce a high T c superconductivity state, said oxide material being a copper oxide.
Claim 24
Independent Claim
148 words
A method for providing a patterned layer of high T c copper oxide superconductor, comprising: preparing a solution containing the components of said high T c oxide superconductor, said components being present in said solution in the amounts required in said high T c copper oxide superconductor, spraying said solution onto a substrate to provide a coated layer thereon, irradiating selected areas of said coated layer with an energy beam to convert said irradiated areas to an intermediate oxide state, the energy and scanning rate of said energy beam being chosen to maintain the relative amounts of the cation components in said layer, dissolving the nonirradiated areas of said coated layer to remove them, leaving a patterned layer of oxide material, and annealing said patterned layer of oxide material in an oxygen atmosphere to produce a high T c superconductivity state, said oxide material being a copper oxide.
Claim 25
Dependent Claim
18 words
The method of claim 20, where said substrate is heated during said spraying step and said irradiation step.
Claim 26
Dependent Claim
13 words
The method of claim 21, where said energy beam is a laser beam.
Claim 27
Dependent Claim
14 words
The method of claim 22, where said oxide superconductor is a Y-Ba-Cu-O oxide material.
Claim 28
Dependent Claim
18 words
The method of claim 22, where said patterned high T c copper oxide superconductor is an epitaxial layer.
Claim 29
Independent Claim
108 words
A method for providing a patterned layer of high T c copper oxide superconductor material, comprising: coating a substrate with a solution containing the components desired in said high T c copper oxide superconductor, said components being in solution in the proper ratios, to provide a layer on said substrate, locally converting selected areas of said layer to an oxide state exhibiting high T c superconductivity by irradiating said selected areas with an energy beam whose energy fluence is less than that which would alter said proper ratios, and removing nonselected areas of said layer to leave a patterned layer of high T c superconducting copper oxide material.
Claim 30
Independent Claim
108 words
A method for providing a patterned layer of high T c copper oxide superconductor material, comprising: coating a substrate with a solution containing the components desired in said high T c copper oxide superconductor, said components being in solution in the proper ratios, to provide a layer on said substrate, locally converting selected areas of said layer to an oxide state exhibiting high T c superconductivity by irradiating said selected areas with an energy beam whose energy fluence is less than that which would alter said proper ratios, and removing nonselected areas of said layer to leave a patterned layer of high T c superconducting copper oxide material.
Claim 31
Dependent Claim
17 words
The method of claim 25, where said removing step is achieved by dissolving away said nonselected areas.
Claim 32
Dependent Claim
15 words
The method of claim 26, where said superconducting copper oxide layer is an epitaxial layer.
References Cited (Backward Citations)
US3801366A
Cited
US4395436A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-03-04 | 1994-09-03 | 1995-03-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-03-04 | 1998-09-03 | 1999-03-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-03-04 | 2002-09-03 | 2003-03-05 | $7700.00 | Window Closed / Lapsed |