US5004722A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making superconductor wires by hot isostatic pressing after bending
Assignee: INTERNATIONAL SUPERCONDUCTOR CORP A CORP OF
•
Filing: 1989-01-19
•
Granted: 1991-04-02
•
Expires: 2009-01-19
Abstract
Abstract Powder or lengths of ceramic or metallic superconductor ceramic compositions are loaded into lengths of metal tubing. Mechanical reduction of filled tubing is facilitated by use of elevated temperatures and intermittent heat treatments as required. Rolling to a flattened cross section aids bending to the final device configurations and subsequent hot-isostatic-pressing. Hot-isostatic-pressing steps (1) close defects, including voids, cracks and joints and improve microstructure, and (2) join tested wire lengths to produce a superconductor length in the final configuration. Encapsulation of the superconductor is completed and assured with metal sleeves and solder or glass.
Inventors
- 👤 Richard L. Tallman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:08
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0801; Y; Y10; Y10S; Y10S505/00; Y10S505/70; Y10S505/704; Y10S505/705; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
146 words
A method of making a superconducting wire, comprising the steps of: (a) introducing a ceramic superconductive material into a metal tube; (b) evacuating ambient air from said tube after introduction of said superconductive material into said tube; (c) backfilling said tube with oxygen; (d) thereafter sealing said tube; (e) subjecting said tube with said material contained therein and after sealing to cross section reduction and elongation, thereby compacting said tube against said material and compacting said material within said tube; (f) thereafter bending said metal tube containing said superconductive material into a useful shape having at least one bend; and (g) thereafter hot isostatically compressing said tube and said superconductive material within said tube at a pressure and temperature and for a duration sufficient such that said tube is collapsed onto said material and voids and cracks in said superconductive material in said tube are healed.
Claim 2
Independent Claim
146 words
A method of making a superconducting wire, comprising the steps of: (a) introducing a ceramic superconductive material into a metal tube; (b) evacuating ambient air from said tube after introduction of said superconductive material into said tube; (c) backfilling said tube with oxygen; (d) thereafter sealing said tube; (e) subjecting said tube with said material contained therein and after sealing to cross section reduction and elongation, thereby compacting said tube against said material and compacting said material within said tube; (f) thereafter bending said metal tube containing said superconductive material into a useful shape having at least one bend; and (g) thereafter hot isostatically compressing said tube and said superconductive material within said tube at a pressure and temperature and for a duration sufficient such that said tube is collapsed onto said material and voids and cracks in said superconductive material in said tube are healed.
Claim 3
Dependent Claim
37 words
The method defined in claim 1, further comprising the step of forming individual bodies of a superconductor by sintering a superconductor powder constituting said superconductive material, said individual bodies being filled into said tube in step (a).
Claim 4
Dependent Claim
24 words
The method defined in claim 1 wherein the cross section reduction in step (e) includes flattening of said tube with said material contained therein.
Claim 5
Dependent Claim
29 words
The method defined in claim 1, further comprising the step of joining individual lengths of said metal tube containing said superconductive material end to end to form said wire.
Claim 6
Dependent Claim
20 words
The method defined in claim 4 wherein said lengths are subjected to hot isostatic compression after said lengths are joined.
Claim 7
Dependent Claim
21 words
The method defined in claim 5 wherein said lengths are also subjected to hot isostatic compression before said lengths are joined.
Claim 8
Dependent Claim
39 words
The method defined in claim 4, further comprising the step of encapsulating joints formed between said lengths upon butting of ends of said lengths together by hot isostatic pressure, and hermetically sealing said joints and ends of said wire.
Claim 9
Dependent Claim
35 words
The method defined in claim 7, further comprising the step of testing said lengths for superconducting properties before joining said lengths and then joining only those of said lengths having superconducting properties following the testing.
Claim 10
Dependent Claim
19 words
The method defined in claim 8 wherein the sealing is effected by flowing a molten metal over said joints.
Claim 11
Dependent Claim
32 words
The method defined in claim 7 wherein the sealing is effected by applying a glassy layer to said joints of a material plastically deforming at the temperature of said hot isostatic compression.
Claim 12
Dependent Claim
37 words
The method defined in claim 7 wherein said cross section reduction is effected at an elevated temperature, thereby inducing shear in said material and superconductor crystals present in said material in a longitudinal dimension of the wire.
Claim 13
Dependent Claim
29 words
The method defined in claim 11, further comprising the step of annealing the tube containing said material prior to said cross section reduction, thereby enhancing ductility of said tube.
Claim 14
Dependent Claim
23 words
The method defined in claim 1 wherein said bending is carried out at an elevated temperature affording increased plastic deformability of said tube.
References Cited (Backward Citations)
US3168399A
Cited
US3221393A
Cited
US3496624A
Cited
US3449818A
Cited
US3748196A
Cited
US4050133A
Cited
US4307280A
Cited
US4944900A
Cited
US4562332A
Cited
US4786374A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-01 | 1994-10-01 | 1995-04-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-01 | 1998-10-01 | 1999-04-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-01 | 2002-10-01 | 2003-04-02 | $7700.00 | Window Closed / Lapsed |