Water-dispersible polyesters imparting improved water resistance properties to inks

Claim 2

A linear, water-dissipatable polyester having an inherent viscosity of at least about 0.1 as measured in a 60/40 parts by weight solution of phenol/tetrachloroethane at 25° C. and at a concentration of 0.5 gram of polyester in 100 ml of solvent, the polyester containing substantially equimolar proportions of acid moiety repeating units (100 mole %) to hydroxy moiety repeating units (100 mole %), the polyester comprising repeating units of components (a), (b), (c) and (d), as follows wherein all stated mole percentages are based on the total of all acid and hydroxy moiety repeating units being equal to 200 mole %: (a) about 90 to about 97 mole % isophthalic acid, (b) about 3 to about 10 mole % 5-sulfoisophthalic acid, (c) about 70 to about 85 mole % 1,4-cyclohexanedimethanol, and (d) about 15 to about 30 mole % diethylene glycol.

Claim 3

The polyester of claim 1 wherein component (b) is in the form of a sodium salt.

Claim 4

The polyester of claim 1 wherein component (a) is about 91 mole % isophthalic acid, component (b) is about 9 mole % 5-sodiosulfoisophthalic acid, component (c) is about 75 mole % 1,4-cyclohexanedimethanol, and component (d) is about 25 mole % diethylene glycol.

Claim 5

The polyester of claim 1 wherein component (a) is about 93 mole % isophthalic acid, component (b) is about 7 mole % 5-sodiosulfoisophthalic acid, component (c) is about 70 mole % 1,4-cyclohexanedimethanol, and component (d) is about 30 mole % diethylene glycol.

Claim 6

The polyester of claim 1 wherein component (a) is about 93 mole % isophthalic acid, component (b) is about 7 mole % 5-sodiosulfoisophthalic acid, component (c) is about 85 mole % 1,4-cyclohexanedimethanol, and component (d) is about 15 mole % diethylene glycol.

Claim 7

The polyester of claim 1 wherein component (a) is about 95 mole % isophthalic acid, component (b) is about 5 mole % 5-sodiosulfoisophthalic acid, component (c) is about 85 mole % 1,4-cyclohexanedimethanol, and component (d) is about 15 mole % diethylene glycol.

Claim 8

The polyester of claim 1 wherein component (a) is about 95 mole % isophthalic acid, component (b) is about 5 mole % 5-sodiosulfoisophthalic acid, component (c) is about 70 mole % 1,4-cyclohexanedimethanol, and component (d) is about 30 mole % diethylene glycol.

Claim 9

The polyester of claim 1 wherein component (a) is about 97 mole % isophthalic acid, component (b) is about 3 mole % 5-sodiosulfoisophthalic acid, component (c) is about 85 mole % 1,4-cyclohexane. dimethanol, and component (d) is about 15 mole % diethylene glycol.

Claim 10

The polyester of claim 1 having an inherent viscosity of about 0.2 to about 0.6.

Claim 11

An ink or concentrate thereof comprising (A) about 4 to about 80 weight percent of at least one linear, water-dissipatable polyester having an inherent viscosity of at least about 0.1 as measured in a 60/40 parts by weight solution of phenol/tetrachloroethane at 25° C. and at a concentration of 0.5 gram of polyester in 100 ml of solvent, the polyester containing substantially equimolar proportions of acid moiety repeating units (100 mole %) to hydroxy moiety repeating units (100 mole %), the polyester comprising repeating units of components (1), (2), (3) and (4), as follows wherein all stated mole percentages are based on the total of all acid and hydroxy moiety repeating units being equal to 200 mole %: (1) about 90 to about 97 mole % isophthalic acid, (2) about 3 to about 10 mole % 5-sulfoisophthalic acid, (3) about 70 to about 85 mole % 1,4-cyclohexanedimethanol, and (4) about 15 to about 30 mole % diethylene glycol, (B) about 0 to about 45 weight percent of at least one colorant, and (C) about 15 to about 95 weight percent water.

Claim 12

An ink or concentrate thereof comprising (A) about 4 to about 80 weight percent of at least one linear, water-dissipatable polyester having an inherent viscosity of at least about 0.1 as measured in a 60/40 parts by weight solution of phenol/tetrachloroethane at 25° C. and at a concentration of 0.5 gram of polyester in 100 ml of solvent, the polyester containing substantially equimolar proportions of acid moiety repeating units (100 mole %) to hydroxy moiety repeating units (100 mole %), the polyester comprising repeating units of components (1), (2), (3) and (4), as follows wherein all stated mole percentages are based on the total of all acid and hydroxy moiety repeating units being equal to 200 mole %: (1) about 90 to about 97 mole % isophthalic acid, (2) about 3 to about 10 mole % 5-sulfoisophthalic acid, (3) about 70 to about 85 mole % 1,4-cyclohexanedimethanol, and (4) about 15 to about 30 mole % diethylene glycol, (B) about 0 to about 45 weight percent of at least one colorant, and (C) about 15 to about 95 weight percent water.

Claim 13

The ink of claim 10 comprising about 5 to about 40 weight percent of component (A), 0 to about 35 weight percent of component (B), and about 35 to about 90 weight percent of component (C).

Claim 14

The ink of claim 10 additionally comprising up to about 15 weight percent of an additive.

Claim 15

The ink of claim 12 wherein said additive is selected from the group consisting of a wax, a defoamer, a surfactant, an alcohol, a glycol, an alcohol ether, a biocide, a thickener, a pH stabilizer, and a mixture thereof.

Claim 16

The ink of claim 10 containing at least about 0.5 weight percent of component (B).

Claim 17

The ink of claim 14 wherein said colorant is one or a mixture of the following color index materials: C.I. Pigment Yellow 17, C.I. Pigment Blue 27, C.I. Pigment Red 49:2, C.I. Pigment Red 81:1, C.I. Pigment Red 81:3, C.I. Pigment Red 81:x, C.I. Pigment Yellow 83, C.I. Pigment Red 57:1, C. I. Pigment Red 49:1, C.I. Pigment Violet 23, C.I. Pigment Green 7, C.I. Pigment Blue 61, C.I. Pigment Red 48:1, C.I. Pigment Red 52:1, C.I. Pigment Violet 1, C.I. Pigment White 6, C.I. Pigment Blue 15, C.I. Pigment Yellow 12, C.I. Pigment Blue 56, C.I. Pigment Orange 5, C.I. Pigment Black 7, C.I. Pigment Yellow 14, C.I. Pigment Red 48:2, C.I. Pigment Blue 15:3, C.I. Pigment Yellow 1, C.I. Pigment Yellow 3, C.I. Pigment Yellow 13, C.I. Pigment Orange 16, C.I. Pigment Yellow 55, C.I. Pigment Red 41, C.I. Pigment Orange 34, C.I. Pigment Blue 62, C.I. Pigment Red 170, C.I. Pigment Red 88, C.I. Pigment Yellow 151, C.I. Pigment Red 184, C.I. Pigment Blue 1:2, C.I. Pigment Red 3, C.I. Pigment Blue 15:1, C.I. Pigment Red 23, C.I. Pigment Red 112, C.I. Pigment Yellow 126, C.I. Pigment Red 169, C.I. Pigment Orange 13, C.I. Pigment Red 1-10, 12, C.I. Pigment Blue 1:X, C.I. Pigment Yellow 42, C.I. Pigment Red 101, C.I. Pigment Brown 6, C.I. Pigment Brown 7, C.I. Pigment Brown 7:X, C.I. Pigment Black 11, C.I. Pigment Metal 1, or C.I. Pigment Metal 2.

Claim 18

The ink of claim 10 wherein the polyester of component (A) comprises about 91 mole % isophthalic acid, about 9 mole % 5-sodiosulfoisophthalic acid, about 75 mole % 1,4-cyclohexanedimethanol, and about 25 mole % diethylene glycol.

Claim 19

The ink of claim 10 wherein the polyester of component (A) comprises about 93 mole % isophthalic acid, about 7 mole % 5-sodiosulfoisophthalic acid, about 70 mole % 1,4-cyclohexanedimethanol, and about 30 mole % diethylene glycol.

Claim 20

The ink of claim 10 wherein the polyester of component (A) comprises about 93 mole % isophthalic acid, about 7 mole % 5-sodiosulfoisophthalic acid, about 85 mole % 1,4-cyclohexanedimethanol, and about 15 mole % diethylene glycol.

Claim 21

The ink of claim 10 wherein the polyester of component (A) comprises about 95 mole % isophthalic acid, about 5 mole % 5-sodiosulfoisophthalic acid, about 85 mole % 1,4-cyclohexanedimethanol, and about 15 mole % diethylene glycol.

Claim 22

The ink of claim 10 wherein the polyester of component (A) comprises about 95 mole % isophthalic acid, about 5 mole % 5-sodiosulfoisophthalic acid, about 70 mole % 1,4-cyclohexanedimethanol, and about 30 mole % diethylene glycol.

Claim 23

The ink of claim 10 wherein the polyester of component (A) comprises about 97 mole % isophthalic acid, about 3 mole % 5-sodiosulfoisophthalic acid, about 85 mole % 1,4-cyclohexanedimethanol, and about 15 mole % diethylene glycol.

Claim 24

The ink of claim 10 wherein component (A)(2) is in the form of a sodium salt.

Claim 25

The ink of claim 10 wherein the polyester of component (A) has an inherent viscosity of about 0.2 to about 0.6.

Claim 26

The ink of claim 10 coated onto a substrate selected from the group consisting of metal foil, newsprint, bleached Kraft paper, unbleached Kraft paper, clay coated paper, glass, calendered paper, stainless paper, paper board, polyester, polycarbonate, cellulose ester, regenerated cellulose, poly(vinylidene chloride), polyamide, polyolefin, and polystyrene.

Claim 27

The ink of claim 11 coated onto a substrate selected from the group consisting of metal foil, newsprint, bleached Kraft paper, unbleached Kraft paper, clay coated paper, glass, calendered paper, stainless paper, paper board, polyester, polycarbonate, cellulose ester, regenerated cellulose, poly(vinylidene chloride), polyamide, polyolefin, and polystyrene.

Claim 28

The ink of claim 12 coated onto a substrate selected from the group consisting of metal foil, newsprint, bleached Kraft paper, unbleached Kraft paper, clay coated paper, glass, calendered paper stainless paper, paper board, polyester, polycarbonate, cellulose ester, regenerated cellulose, poly(vinylidene chloride), polyamide, polyolefin, or polystyrene.

Claim 29

The ink of claim 14 coated onto a substrate selected from the group consisting of metal foil, newsprint, bleached Kraft paper, unbleached Kraft paper, clay coated paper, glass, calendered paper, stainless paper, paper board, polyester, polycarbonate, cellulose ester, regenerated cellulose, poly(vinylidene chloride), polyamide, polyolefin, and polystyrene.

Claim 30

The ink of claim 15 coated onto a substrate selected from the group consisting of metal foil, newsprint, bleached Kraft paper, unbleached Kraft paper, clay coated paper, glass, calendered paper, stainless paper, paper board, polyester, polycarbonate, cellulose ester, regenerated cellulose, poly(vinylidene chloride), polyamide, polyolefin, and polystyrene.